Question

-3
=
The hole density in an n-type Si slab (doped at Na 1018 cm-3) decreases linearly from 10¹4 cm7
to 10¹3 cm-³ between x = 0 and x = 1 µm. Calculate the hole diffusion current density. Find the diffusion length.

Expert Solution

Trending now

This is a popular solution!

Step by step

Solved in 3 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Blurred answer

Similar questions

The radii of the two concentric conductive spheres are r1 and r2>r1. The resistivity of the material between the spheres is p. If the total current I from the inner sphere to the outer sphere, Find the electric potential difference between the spheres.Give your answer in terms of (r1, r2, p, I).
You are given 1.0 [g] of aluminum (mass density = 2700 kg/m3) and asked to make a wire, using all the aluminum, that will dissipate 7.5 [W] when connected to a 1.5 [V] battery. What length and diameter will you choose for your wire?
A wire sample (0.75 mm in diameter and 20 cm in length) is placed in anelectrical circuit. A voltage drop of 464 mV is measured across the length ofthe wire as it carries a 2 A current. Calculate the electrical conductivity of thisalloy. From Table 4 below, which gives the conductivities of differentmaterials at 20C, identify the material. MaterialElectrical Conductivity(Sm-1)Manganin 2x106Nickel 14x106Aluminium 30x106Copper 50x106Silver 63x106Table 4. Conductivities of different materials at 20 C.
A copper wire 100m long with cross-sectional area of 2x10-4 cm2 is heated from room temperature of 25 C to 200 C. Find The drift speed of the “electron group” in the wire, if the current is 3A and density of electrons is 8.5x1028 electrons /m3 The voltage drop across the wire resistor for this current of 3A The power dissipated by resistor.
(c) If the gate oxide were destroyed by a static electricity discharge, speculate on how the current readings might be different from those that were observed.Be detailed in your response. (d)Using an electron mobility value of μn= 800 cm2/V-s and a gate oxide thickness of xox= 80 nm, compute the value of Kn= μnCox.From this value and some of the simulateddata points (where the drain current is saturated) make a rough estimate of the W/L ratio for the 2N7000 MOSFET. Does this W/L ratio seem reasonable?