The following torsion test data were obtained for AA6061-T6 aluminum alloy has a round cross section with 30mm outer diameter, 0 inner diameter and 100 length. No. 00 T Y degree (rad) (N.m) (N/m2) (rad) (GN/m²) 1 1 32 3 3.5 130 4 286 5.5 347 6. 6.5 487 7.5 591 8 9 786 9. 10.5 910 10 13.5 1105 11 16.5 1163 12 21.5 1235 13 25.5 1222

The following torsion test data were obtained for AA6061-T6 aluminum alloy has a round cross section with 30mm outer diameter, 0 inner diameter and 100 length. No. 00 T Y degree (rad) (N.m) (N/m2) (rad) (GN/m²) 1 1 32 3 3.5 130 4 286 5.5 347 6. 6.5 487 7.5 591 8 9 786 9. 10.5 910 10 13.5 1105 11 16.5 1163 12 21.5 1235 13 25.5 1222

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: In a tensile test of stainless steel, the following data were obtained: 20,200 13,200 Load (N)…

A: AS THIS QUES HAS MULTIPLE PARTS SO WE WILL SOLVE ONLY FIRST THREE PARTS FOR YOU Given Data…

Q: Q1- The engineering tensile stress-strain data were obtained for AA6061-T6 aluminum alloy shown: *…

Q: Consider steel B is a cylindrical sample with original length 40mm and subjected to 15700N.…

A: Option b is correct.

Q: The stress-strain diagram for a steel alloy having an original diameter of 0.80 in. and a gage…

Q: A tension test was performed on a steel specimen having an original diameter of 0.503 in. and gauge…

A: Given: The original diameter of steel specimen d=0.503 in The original gauge length l=2 in

Q: 12) If we want a component made from this material to withstand at least 5 x 10° Cycles, what is the…

A: Given: The number of cycles, N = 5x105

Q: A tension test was performed on a steel specimen having an original diameter of 0.503 in. and gauge…

Q: Analyse the differences between the 2 attached stress-strain curves for 0.9% carbon steel and 0.15%…

A: Graph 1: 0.9 % carbon steel The ultimate tensile strength is 648 MPa The percent elongation or…

Q: The following data were obtained during a tensile test of an alluminium alloy specimen. Initial…

A: Given data:

Q: tress-strain diagram for a steel alloy having an original diameter of 0.80 in. and a ength of 2 in.…

Question

Calculations
The following torsion test data were obtained for AA6061-T6 alunminum alloy has a
round cross section with 30mm outer diameter, 0 inner diameter and 100 length.
No.
degree (rad)
(N.m) (N/m2)
(rad) (GN/m?)
1
2
1
32
3
3.5
130
4
5
286
5
5.5
347
6.
6.5
487
7
7.5
591
8
9
786
9
10.5
910
10
13.5
1105
11
16.5
1163
12
21.5
1235
13
25.5
1222

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step by step

Solved in 4 steps with 7 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

I need only MATLAB coding please.....
Use the S-N Curve below to answer the following questions 550 mT 500 450 400 350 300 250 200 150 100 50 10 Fatigue life (cycles) 10? 103 105 106 107 Stress amplitude (MPa)
A tension test was performed on a specimen having an original diameter of 11.5 mm and a gauge length of 50 mm. The data are listed in the table. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Redraw the linear-elastic region, using the same stress scale but a strain scale of 20 mm = 0.001 mm/mm. From the diagram, determine approximately the modulus of elasticity. Express your answer to three significant figures and include the appropriate units. E 215 Submit Previous Answers Request Answer Part B μÀ X Incorrect; Try Again; 2 attempts remaining Tu = 530 Determine the ultimate stress. Express your answer to three significant figures and include the appropriate units. GPa μÅ Part C Submit Previous Answers Request Answer MPa | μA ? X Incorrect; Try Again; 2 attempts remaining of=479.15 Determine the…
A tension test was performed on a specimen having an original diameter of 13.0 mm and a gauge length of 50 mm. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Using the data listed in the table, plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Part A From the diagram, determine approximately the modulus of toughness. Express your answer to three significant figures and include the appropriate units. U = Submit O μA Value Request Answer Units < Return to Assignment Provide Feedback ?
Data taken from a stress-strain test for a ceramic are given in the table. The curve is linear between the origin and the first point. Plot the diagram, and determine the modulus of elasticity and the modulus of resilience.
A specimen of magnesium having a rectan- gular cross section of dimensions 3.2 mm × 19.1 mm (in. × in.) is deformed in ten- sion. Using the load-elongation data tabulated as follows, complete parts (a) through (f). lbf 0 310 625 1265 1670 1830 2220 2890 3170 3225 3110 2810 Load N 0 1380 2780 5630 7430 8140 9870 12,850 14,100 14,340 13,830 12,500 in. 2.500 2.501 2.502 2.505 2.508 2.510 2.525 2.575 2.625 2.675 2.725 2.775 Fracture Length mm 63.50 63.53 63.56 63.62 63.70 63.75 64.14 65.41 66.68 67.95 69.22 70.49 (a) Plot the data as engineering stress versus engineering strain. (b) Compute the modulus of elasticity. (c) Determine the yield strength at a strain offset of 0.002. (d) Determine the tensile strength of this alloy. (e) Compute the modulus of resilience. (f) What is the ductility, in percent elongation?
A structural member 10 cm long must be able to support a load of 50,000 N without experiencing any plastic deformation. Given the following data for brass, steel, aluminum, and titanium, rank them from least to greatest weight in accordance with these criteria. Yield strength Ultimate tensile Alloy Density (g/cm3) (MPa) strength (MPa) Brass 415 600 8.5 Steel 860 800 7.9 Aluminum 310 435 2.7 * 700 Titanium 550 4.5
In a tensile test for an aluminum alloy, the sample used is 2 inches long and 0.5 inches in diameter. The proportional portion of the tension stress-strain diagram for an aluminum alloy is shown below. _x106 lb/in² Pay attention to units and calculate your answer to 1 decimal place for the unit specified above. σ (ksi) 70 t 0.00614 Determine the modulus of elasticity for this material: € (in./in.)
A tension test was performed on a specimen having an original diameter of 13.7 mm and a gauge length of 50 mm. The data are listed in the table. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Redraw the linear-elastic region, using the same stress scale but a strain scale of 20 mm = 0.001 mm/mm. From the diagram, determine approximately the modulus of elasticity. Express your answer to three significant figures and include the appropriate units. E = Submit Part B συ = Submit Part C ☐☐ μÅ of = Value Determine the ultimate stress. Express your answer to three significant figures and include the appropriate units. Request Answer μĂ Value Request Answer Units μĂ - Value Units Determine the fracture stress. Express your answer to three significant figures and include the appropriate units. ? Units ? ?