A tension test was performed on a steel specimen havingan original diameter of 0.503 in. and gauge length of2.00 in. The data is listed in the table below. (Figure 1)FigureLoad (kip) Elongation (in.)001.500.00054.600.00158.0011.0011.8011.8012.0016.6020.0021.5019.5018.500.00250.00350.00500.00800.02000.04000.10000.28000.40000.46001 of 1Part ADetermine approximately the modulus of elasticity.Express your answer to two significant figures and include the appropriate units.E =Submit▾ Part Bσy =μASubmitValueRequest AnswerDetermine approximately the yield stress.Express your answer to two significant figures and include the appropriate units.μÃValue[IMG] ?Request AnswerUnitsUnitswww.?

Given: The original diameter of steel specimen d=0.503 in The original gauge length l=2 in

Answered: A tension test was performed on a steel…

A tension test was performed on a steel specimen having an original diameter of 0.503 in. and gauge length of 2.00 in. The data is listed in the table below. (Figure 1)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final)…

A: Given:Li=40 mmAf=264.327 mm2P=122.5 KNLf=47.516 mm

Q: we are to find the sheer strain, sheer stress and modulus of rigidity. table,specimen length,gauge…

Q: that when a sion measur

Q: In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final)…

A: GivenL=40mmAfinal=264.327 mm2P=122.5kNLf=47.516mm

Q: Extensometer in the Universal Testing Machine is used to measure the diameter of the tensile…

A: Extensometer is used to measure the change in length and area reduction in the tensile specimen. It…

Q: Specimen (Rebar) Original Length Length when it was clamped Diameter (mm) Internal Diameter (mm)…

A: The data for the specimen is given below,SpecimenA0P maxTensile strengthModulus of elasaticity…

Q: The truss shown is supported by a pin at A and a roller at G. Using the method of sections,…

A: Consider horizontally forward & vertically upward force as (+)ve and horizontally backward &…

Q: In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final)…

A: Given data: Gauge length of specimen = 40 mm Final length of specimen = 47.516 mm Final area of…

Q: . Water in a hydraulic press is under a pressure of 92.580 MPa abs. at 16 degrees C. if the initial…

Q: mm. If nr

Q: The following results were obtained in a tensile test on a mild steel specimen of original diameter…

A: According to Hooke's law, Young's Modulus of Elasticity is defined as the ratio of longitudinal…

Q: Given the following data: Original diameter = 3.50 mm Original gauge length = 12.00 mm Deformation…

A: GivenOriginal diameter d= 3.50 mm Original gauge length L= 12.00 mm Deformation ∆L= 0.46 mm Load =…

Q: Based on the information above; draw stress-strain diagram of the material and answer the following…

Q: Measurement Observation Vernier Main scale Average DTI scale reading SI. of the NO: specimen in…

A: LENGTH = 73.2854 mm

Q: If the Vicker’s hardness number (HVN) is 385 N/mm2, how much load was applied on the test specimen…

Q: ease help, (Will provide helpful ratings if got cor

Q: 38) A tensile test specimen has a gauge length =2in. and a diameter= 0.875in. Yielding occurs at a…

Q: 1. A tensile test was conducted on a metal "505" specimen and the following stress-strain curves…

A: Elastic Modulus (Young's Modulus): The elastic modulus represents the stiffness of a material and is…

Q: A tensile test uses a test specimen that has a gauge length of 100.00mm and a cross sectional area…

Q: A tension test specimen had a gauge length of 2.5 in. After the test, the gauge length had increased…

A: In this problem, we will compute the uncertainty in the percentage elongation of the specimen by…

Q: A strain gauges system mounted at a point on a structural member that is subjected to multiaxial…

A: Given data, Normal strain in x-direction, εx=6.686×10-4 Normal strain in y-direction, εy=3×10-4…

Q: 1 The cross-sectional area and gauge length of a tensile test specimen are both equal to 60 mm². The…

Q: 38)A tensile test specimen has a gage length=3.0 inches and a diameter= .75 inches. Yielding occurs…

A: Given data:Gauge length = 3 inchesDiameter d = 0.75 inchesLoad at yield point = 38000…

Q: Q.7. A cylindrical specimen of aluminium having a diameter of 12 mm and gauge length of 48.000 mm is…

A: Specimen material = Aluminium Specimen diameter, d=12mm Specimen gauge length, L=48.00mm

Q: In a Torsion test done, the following data were collected: the radius of the specimen was 3mm and…

A: Given , d= 6 mm l = 76.2 mm

Q: The following curve is a result of a tensile test. The gauge length was 2 in, and the specimen…

A: According to the given data Force and extension diagram is given We need to find Yield strength at…

Q: A sample material with circular cross-section tapers uniformly. Over a gauge length of 200mm, it…

Q: In tensile test the percentage of elongation was 29.8%. If the final length reached to 84.37mm, so…

Q: Table Q4 below indicates results on a tensile test of a mild steel specimen. 95 kN Proportional…

A: According to the company's guidelines when multiple sub parts are asked, only first 3 subparts has…

Q: The following data were obtained during a tensile test of an alluminium alloy specimen. Initial…

A: Given data:

Q: A pine wood specimen was prepared with actual dimensions of 50 mm *50 mm * 250 mm and grain parallel…

A: Load (kN) Deformation (mm) stress(MPa) strain 0 0 0 0 0 1 8.9 0.457 3.56 0.002285 2 17.8…

Q: In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final)…

A: The initial area of the specimen: Option (b) : 313.994 mm2

Q: 2/ Aluminum tensile specimen with 12.5mm diameter, a gauge length of 50.8mm and the final ameter was…

Q: Using strain gauges with an instrumentation amplitier which is initially ideal: 1. Two strain gauges…

A: Given: Horizontal beam being bent downwards at one end To find: Sketch the layout

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

A tension test was performed on a steel specimen having
an original diameter of 0.503 in. and gauge length of
2.00 in. The data is listed in the table below. (Figure 1)
Figure
Load (kip) Elongation (in.)
0
0
1.50
0.0005
4.60
0.0015
8.00
11.00
11.80
11.80
12.00
16.60
20.00
21.50
19.50
18.50
0.0025
0.0035
0.0050
0.0080
0.0200
0.0400
0.1000
0.2800
0.4000
0.4600
1 of 1
Part A
Determine approximately the modulus of elasticity.
Express your answer to two significant figures and include the appropriate units.
E =
Submit
▾ Part B
σy =
μA
Submit
Value
Request Answer
Determine approximately the yield stress.
Express your answer to two significant figures and include the appropriate units.
μÃ
Value
[IMG] ?
Request Answer
Units
Units
www.
?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step 5

Trending now

This is a popular solution!

Step by step

Solved in 5 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

in a Torsion test done. the following data were collected: the radius of the specimen was 3mm and the gauge length was 76.2mm. During the elastic zone: T1=0. 01N.m. 81=14.760, 12-17.13N.m, and 02 36.910, The modulus of rigidity G will be equal to: Select one O a 44.283 GPa. O b. 26.522 GPa. O C 462.91 MPa. O d. 12.94 GPa.
A tensile test was performed on a metal specimen with a diameter of 1/2 inch and a gage length (the length over which the elongation is meas- ured) of 4 inches. The data were plotted on a load-displacement graph, P vs. AL. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/AL = 1392 kips/in. What is the modulus of elasticity? BI
A specimen with an initial diameter of 12 + b* was tested under tensile conditions and a maximum load of 60 kN was recorded together with a %65 of strain. What should be the load to be applied in order to obtain a strain of %30
I want answers to all four questions if possible. Thanks for help :) Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the fracture strength (in MPa) of the material. - Calculate the percent elongation of the specimen at fracture point. - Determine the modulus of resilience (in N.mm/mm3) of the material. (Use at least five decimal units) - Determine the toughness index number (in N.mm/mm3) of the material.
Hi, I need help with this question.
Determine the final cross-sectional area for a tensile specimen that has 31 mm2 as the initial area and 57 % as the percentage of reduction in area. Final cross-sectional Area (mm2) = %3D
In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final) of specimen after tensile test was 264.327. The load which caused fracture was (122.5 KN). After fracture, the final length was 47.516mm The % reduction in area is * O 15.819% 18.819 O 17.819 O 20.819
Question Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the yield strength (in MPa) of the material. - Calculate the percent elongation of the specimen at yield point. (Use at least five decimal units) - Calculate the stiffness (in MPa) of the specimen material. - Calculate the ultimate strength (in MPa) of the material. - Calculate the percent elongation of the specimen at point of ultimate strength.
In a Torsion test done, the following data were collected: the radius of the specimen was 3mm and the gauge length 76.2mm. During the elastic zone: T1-0. 01N.m. 01-14.760, T2-17. 13N.m, and 02-36.910. The modulus of rigidity be equal to:
Question 2 In designing prosthetic sockets, the latter will need to be experimentally tested for their structural integrity. Figure 2 shows one such design of a prosthetic socket which is made of carbon fibre composite. Strain gauges are installed to record the strains at various locations of the legs during walking and the readings are recorded using a telemetry system to detemine the critical stressed area. At a particular strain gauge location indicated in Figure 2, the readings recorded by one of the 45° strain gauge rosettes are: Ea = 2500 x 10*, es = 1500 x 10°, & = -950 x 10* Using Mohr's Cicle or otherwise, detemine: (a) the principal strains and the direction of the maximum principal strain relative to the gauge "a". (b) the corresponding principal stresses and sketch the results on a properly oriented element. You may assume that the prosthetic socket is made of polypropylene whose Young's modulus of 1.0 GPa and Poisson ratio of 0.3. Figure 2
I need the answer as soon as possible
39) A tensile test specimen has a gauge length=2in. and a diameter of 0.875in. Yielding occurs at a load of 35,500lbs. The corresponding gauge length = 2.0113in. (neglect the .2% yield point). The maximum load of 45,000lbs is reached at a gauge length of 2.543in. If fracture occurs at a gauge length of 2.673in, determine the percent elongation at fracture (Round to the nearest whole %)