Steady-state creep data taken for an iron at a stress level of 140 MPa are given here: &, (h:¹) T(K) 6.4×104 1080 8.8 x 102 1180 If it is known that the value of the stress exponent n for this alloy is 8.5, compute the steady-state creep rate at 1290 K and a stress level of 82 MPa. h1

Steady-state creep data taken for an iron at a stress level of 140 MPa are given here: &, (h:¹) T(K) 6.4×104 1080 8.8 x 102 1180 If it is known that the value of the stress exponent n for this alloy is 8.5, compute the steady-state creep rate at 1290 K and a stress level of 82 MPa. h1

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: ts) In a laboratory creep experiment at 1000°C, a steady-state creep rate of 5 x 10-1% per hour is…

A: Given:Given that, experiment duplicate the service stress, henceFind:Creep rate at service…

Q: Iculate the activation energy (in J/mol) for creep for an alloy having the steady state creep havior…

Q: Brass is an alloy that can consist of copper and zinc, where zinc has a coefficient of linear…

A: Given:Brass alloy contains copper and zincCoefficient of linear expansion for zinc: 23.0 to 32.5 x…

Q: Q.3 a - What are the most preffered properties in metals to be used in high temp. to resist creep…

A: Properties of material which are used to resist the creep. *** AS per our company policy we are…

Q: aluminum alloy 2014

A: Problem asked to specify a practical heat treatment for a 2014 aluminum alloy that will produce a…

Q: Temperature (°C) 1600 (1) 1400 1200 1000 800 600 400 1538°C (Fe) 912°C 8+7 1394°C(F) -1493°C (G) y,…

A: Given:

Q: Steady-state creep rate data are given here for some alloy taken at 200°C (473 K): i Es (h-¹) 2.2 x…

Q: Composition (at% Pb) 10 30 40 70 100 700 1200 600 a +L Mg2Pb 1000 500 a 800 400 L. Mg2Pb 600 300 400…

A: To obtain the percentage of the liquid phase in an alloy composition at a certain temperature can be…

Q: 1900 Fo = Forsterite 1800 Liquid En = Enstatite Qz = Quartz 1700 Fo+liq 1600 -En+lig Qz+liq 1500…

A: From the olivine mineral group, forsterite is a magnesium silicate crystal with the chemical formula…

Q: (6) For an aluminum alloy under constant load, the creep rate increased by a factor of 2 when the…

Q: Do provide explanations too. Thank you.

A: The grain boundary and bulk diffusion creep both are the mechanism that leads to the elongation of…

Q: the thermal expansion coefficient is 1.5*10^-0.5 the material is cast alloy steel. . Estimate…

A: L = 200mm α= 1.5x10-5 / °C T= 30°C T1 = 40°C T2 = 5 ° We need to find thermal expansion X1 and X2…

Q: 8- For the S-N plot below, determine the following: a. What is the fatigue limit for this alloy? b.…

A: Given: The stress amplitude is σa1=400 MPa and σa2=255 MPa. Concept used: Fatigue limit: The number…

Q: Q1. A tower crane is used to lift I beams to construct skyscraper. As shown in Figure Q1 (a), the…

A: When elastic cables are subjected to tensile force it tends to extend and this elongation per unit…

Q: Calculate the activation energy in j/mol for the creep of an alloy having the steady state creep…

Q: Which of the following statements is incorrect? Under creep and fatigue loading materials may fail…

A: Given: Which of the following statements is incorrect?Under creep and fatigue loading materials may…

Q: Q5/ A. Classify the ceramics materials and give typical example with justification for each class.…

A: (A) Write the classification of ceramic materials.

Q: Name three comonly used methods for deriving the element stiffness matrix and element…

A: Three commonly used method for deriving the element stiffness matrix and element equation are; a)…

Q: Borosilicate glass bottles are processed into bottles using press and blow method shown in Figure…

A: Blow moulding is the process of inflating or blowing a thermoplastic molten tube termed a…

Q: Problem 1: . Consider a steel alloy having the stress-strain diagram shown in the figure below: 1.…

A: here, there is more than 1 question,As you not mentioned which question's answer you want as per…

Q: Steady-state creep rate data are given here for some alloy taken at 200°C (473 K): i, (h) a (MPa)…

A: Find the steady state creep rate .

Q: A ceramic with KIc = 4 MPa m1/2 contains pores with radius a = 5 µm due to incomplete sintering.…

Q: Not yet answered Stress-Strain Diagram Marked out of 15.00 question 200 a ns a s aos 02 Sain m…

A: given:

Q: 2. A brass ring of diameter 10.00 cm at 20.0°C is heated and slipped over an aluminum rod of…

A: Solution:

Q: 11. Steady-state creep rate data are given below iron at 900 C. &($) 104 10-6 σ (MPa) 17 6.5 If it…

Q: Excellent combinations of hardness, strength, and toughness are obtained from bainite. One heat…

A: The eutectoid composition of austenite is approximately 0.8% carbon; steel with less carbon content…

Q: Using the isothermal transformation diagram for an iron-carbon alloy of eutectoid composition,…

Q: An of at least 100 days at 500°C, computer level. (refer Fig below). Larsen - Miller C=Constant…

A: Rupture Lifetime, tr = 100 days = 100 × 24hrs = 2400 hr Temperature, T = 500°C = 500 + 273 = 773 K…

Q: Sintered silicon nitride parts are expected to experience tensile stresses 50% of the ultimate…

A: Given data:- tensile stresses (σ) =50% of the ultimate tensile strength Specific surface energy (γ)=…

Q: determine the grain size using the following equation n100=nM M = M 100 2 Real length Scale bar…

A: Given: Equation of the grain size: →n100=nMM1002 Where M is : →M=Real length Scale bar Because real…

Q: 25 30 35 40 45 50 |12. 10° (R-h) х103 х103 х103 х103 х103 х103 Larson-Miller 100,000 |2.2- 10° (K-Һ)

A: stress=80MPa(11600psi)Temperaure=700°C(973k) To-Find:- Time to rupture =.................hours

Q: S/N Grain Diameter (mm) Strength (MPa) 1. 0.015 170 2. 0.025 158 3. 0.035 151 4 0.050…

A: (1)Hall-Petch equationstrength = sigma0 + K*d^(-1/2)to obtain two constants K and sigma0, two…

Q: S11 S22 S33 S44 S55 S66 S12 S13 0.007692 (Gpa)^-1 0.00625 (Gpa)^-1 0.005263 (Gpa)^-1 0.011111…

A: Given Data: Find: what is the various E’s, G’s and Poisson’s ratios of this anisotropic single…

Q: A cylindrical specimen of a cold-worked brass has a ductility (%EL) of 33%. If its cold-worked…

Q: You are given three metal test samples, with the same chemical composition and differing grain…

Q: For the stress-strain curve shown below, please estimate the properties indicated. Please do your…

A: Given:Stress-Strain curve.To find:Various mechanical properties enlisted.

Q: The properties of a titanium allow used in commercial airplanes are shown in the table: Grain Size…

A: (a) The general equation of the Hall-Petch equation is, σy=σi+K·d-12 where σi and K are the…

Q: Q-5 Consider an S-590 alloy component as shown in following figure that is subjected to a stress of…

A: Givenσ=200Mparapture lifetr=500h

Q: 5. Derive expressions for a simple Voigt element in the following experiments: (a) Creep experiment:…

A: Solution: Given Data: A Voigt Element. To Find: (a) J(t) (b) E(t) (c) σ(t)

Q: Consider an alloy containing 30 wt% Sb. If the alloy is held at 400 oC, how much of the alloy is in…

Q: 4) In the temperature range from 600°C to 750°C, a steel wire with 100 mm length shows the steady…

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

Steady-state creep data taken for an iron at a stress level of 140 MPa are given here:
&, (h:¹)
T(K)
6.4×104 1080
8.8 x 102 1180
If it is known that the value of the stress exponent n for this alloy is 8.5, compute the steady-state creep rate at 1290 K and a stress
level of 82 MPa.
i
h1

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Parvinbhai
the behaviour of graphite materials under stress
Given the following: Cp of Br: 0.226 J/g-K BP of Br: 59 deg C density of Br: 3.12 g/mL Hvap of Br: 30,900 J/mol V of liquid Br solution: 50 mL Cp of Br2: 0.473 J/g-K What is the total heat required in heating Br from 25 to 75 deg C?
5. Figure shows the cooling curve for aNiO-MgO ceramic. (e) the super heat; 2800 2700 2600 2525 2500 28 2400 10 20 30 40 50 Time (min) Temperature (°C)
The state of stress at a point in an engine piston is given in the x-y-z coordinates by: 90 180 [0]=0, MPa = 180 240 yx yy 120 zy Using the matrix transformation law, determine the state of stress at the same point for an element rotated about the x-axis (in the y-z plane) 60° clockwise from its original position. Calculate the stress invariants and write the characteristic equation for the original state of stress, Calculate the deviatoric invariants for the original state of stress, Calculate the principal stresses and the absolute maximum shear stress at the point. What are the stress invariants and the characteristic equation for the transformed state of stress, а. b. С. d. e
A steel ruler of 40 cm, calibrated at 27°C, was used to measure a component in a relatively hot environment of 65°C. What would be the error % in the measurements if a .steel=17.7x10-6 °C^-1
Consider the following data for a range of materials. In which of the following situations is creep likely to occur? Melting temperature of various materials: Melting Temperature (°C Material Ti alloy 1668 Carbon steel 1375 Alumina 2070 Nylon 66 polymer 262 A carbon steel component under continuous load in a power station operating at 200°C. A nylon pipe carrying fluid at 125K. All of the scenarios. A Ti alloy in a turbine operating at 350°C. An alumina ceramic component in a furnace operating at 600°C.
In a laboratory creep experiment at 1273K, a steady-state creep rate of 5 ××10-1 %, per hour is obtained in a metal alloy. The creep mechanism for this alloy is known to be dislocation climb with an activation energy of 200 kJ>mol. Predict the service temperature in (°C) for a creep rate of 8.68 ×10-5 %, per hour. (Assume that the laboratory experiment duplicated the service stress.)
Q3) Compute the change in Gibbs free energy of a certain material when 2 mol is heated from 298 K to 1100 K at 1 atm. (the properties of the material are: c, = 5x10*xT J/molK, S°298 = 7.0 J/molK)
Calculate the activation energy in J/mol for creep for an alloy having the steady state creep behavior shown in the figure. Use the data taken at stress level of 300MPa and temperature of 650C and 730C. Assume that the stress component n is independent of the temperature.
Only the highlighted I need want to make sure I did it right
i need the answer quickly