Q1. Experiments were conducted in a tension testing machine to evaluate the material properties of two metallic rods both having diameter equal to 10 mm. First rod having modulus of rigidity of the material equal to 400 tonnes/cm² when subjected to an axial tensile force of 6 kN, the change in its diameter was observed to be 0.0018 cm. The value for the bulk modulus of the second metallic rod is same as that of the first one but modulus of elasticity 18% more. Based on the material properties calculate and compare the values of different moduli as well as Poisson's ratio for both metallic rods. Justify your answer with reasons.

Q1. Experiments were conducted in a tension testing machine to evaluate the material properties of two metallic rods both having diameter equal to 10 mm. First rod having modulus of rigidity of the material equal to 400 tonnes/cm² when subjected to an axial tensile force of 6 kN, the change in its diameter was observed to be 0.0018 cm. The value for the bulk modulus of the second metallic rod is same as that of the first one but modulus of elasticity 18% more. Based on the material properties calculate and compare the values of different moduli as well as Poisson's ratio for both metallic rods. Justify your answer with reasons.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A rod specimen of ductile cast iron was tested in a torsion-testing machine. The rod diameter was 22 mm, and the rod length was 240 mm. When the applied torque reached 300.0 N-m, a shear strain of 2370 microradians was measured in the specimen. What was the angle of twist in the specimen?
A rod specimen of ductile cast iron was tested in a torsion-testing machine. The rod diameter was 24 mm, and the rod length was 280 mm. When the applied torque reached 302.9 N-m, a shear strain of 2155 microradians was measured in the specimen. What was the angle of twist in the specimen? Answer: i
Figure Q1(a) shows the stress-strain graphs of four different materials labelled as A, B, C and D. Qualitatively, classified the materials in orderof largest to smallest strain hardening.
Q 55 1. What is the boundary tension called where the material ceases to comply with Hooke's Law? 2. How can a material with final deformation of 10% be characterized? 3. The stress-strain curve with the actual stress is calculated in the current area and has different final stress from the engineering stress, being called... 4. What is the stress that causes permanent deformation in the material? 5. What is the % range of the yield limit of some steels referring to the limit stress that the material begins to suffer deformation? 6. For what type of material can the Octahedral Stress Criterion be applied? 7. What is the tension at which the material begins to soften?
Calculate the true strain when the initial length 10.5 mm and the final length *12mm 0.143 O 0.134 O 0.413 O 0.314
The representative curves of the applied stress versus the number of cycles for different metals are shown in Figure Q2. Analyze both metals in terms of fatigue properties. 500 Stress amplitude (MN/m²) 400 300 200 100 0 1045 steel 10³ 104 2014-T6 aluminium 10⁹ 106 107 Number of cycles, N₂ Figure Q2: Representative curves of stress amplitude vs number of cycles 108 10⁹
A wire with circular base of radius 3 mm was subjected to tensile stress of 13.5 Pa. If half the amount of stress is to be applied to a wire with square base of 2.60 mm width, what must have been the force (in Newton) applied to this new wire?
The principal strains in a plane, measured experimentally at a point on the aluminum fuselage of a jet aircraft, are ε1 = 60 x 10-6, and ε2 = 210 x 10-6. If this is a case of plane stress, determine the associated principal stresses at the point in the same plane. E(al)= 10(10^3)ksi V(al)= 0.33
A brass alloy rod having a cross sectional area of 0.24 in.2and a modulus of 16 * 106 psi is subjected to a tensile load. Plastic deformation was observed to begin at a load of 8,944 lb.a. Determine the maximum stress that can be applied without plastic deformation.b. If the maximum length to which a specimen may be stretched without causing plastic deformation is 3.28 in., what is the original specimen length?