If the original specimen length is 76 (b) mm, what is the maximum length to which it may be stretched without ?causing plastic deformation إجابتك A cylindrical specimen of a nickel alloy having an elastic modulus of 207 GPa and an original diameter of 10.2 mm will experience only elastic deformation when a tensile load of 8900 N is applied. Compute the maximum length of the specimen before deformation if the maximum .allowable elongation is 0.25 mm

If the original specimen length is 76 (b) mm, what is the maximum length to which it may be stretched without ?causing plastic deformation إجابتك A cylindrical specimen of a nickel alloy having an elastic modulus of 207 GPa and an original diameter of 10.2 mm will experience only elastic deformation when a tensile load of 8900 N is applied. Compute the maximum length of the specimen before deformation if the maximum .allowable elongation is 0.25 mm

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: A torsion test shows that the shear modulus of an aluminum specimen is 27.6 GPa. When the same…

A: Shear modulus, G= 27.6 GPa Modulus of elasticity, E= 73.2 GPa To find: Poisson's ratio, μ

Q: A three-point bending test was performed on an aluminum oxide specimen having a circular cross…

A: Given data:- Material aluminum oxide For circular cross-section Radius (r)=5.6 mm fracture load…

Q: A tensile test specimen has a starting gage length 50 mm and a cross-sectional area 200 mm2. During…

Q: The stress-strain diagram for a steel alloy having an original diameter of 0.40 in. and a gage…

Q: An 820 MPa (145,000 psi) stress is applied to a specimen of 4341 steel alloy, which has a plane…

A: Given Data

Q: What is the modulus of elasticity

A: force F = 613 kNdiameter d = 43 mm = 0.043 mlength L = 304 mm = 0.304 melongate length l = 0.00224 m

Q: A cylindrical specimen of some metal alloy 7.7 mm in diameter is stressed in tension. A force of…

A: Given: d=7.7 mmF=6280 Nδd=0.0033 mmν=0.35

Q: modulus of elasticity

A: in the question original length is not given. With original length of the specimen not possible to…

Concept explainers

Axial Load

When a bar of the uniform cross-section is acted by a load, such that the load acts along the longitudinal axis of the bar, such kinds of loadings are known as axial loadings. In general terms, a load is an external force acting on a component. An axial load acts perpendicular to the geometric cross-section of the component. Based on the direction of the application of the load, an axial load can be tensile or compressive. The analysis of bodies under the action of axial loads is generally studied under the branch of mechanics, known as statics.

Question

9:00
blai 3 If the original specimen length is 76 (b)
mm, what is the maximum length to
which it may be stretched without
?causing plastic deformation
إجابتك
bläi 4 A cylindrical specimen of a nickel alloy
having an elastic modulus of 207 GPa
and an original diameter of 10.2 mm
will experience only elastic
deformation when a tensile load of
8900 N is applied. Compute the
maximum length of the specimen
before deformation if the maximum
.allowable elongation is O.25 mm
إجابتك
Select the valid answer(s)
نقطة واحدة
:Metals .ying-ability is due to

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step 5

Step by step

Solved in 5 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

4. A titanium alloy (Ti-5Al-2.5Sn) specimen with the dimensions shown below is subjected to a uniaxial tensile load of 1500 N. (a) Determine if the deformation is entirely elastic. (b) What is the extension and gauge length (in mm) under this load? You may assume a Modulus of Elasticity of 110 GPa and a yield strength of 760 MPa. 13 mm 45 mm 9 mm R8 mm/ 40 mm
Engineering and true strain
Part B The stress-strain diagram for a steel alloy having an original diameter of 1.0 in. and a gage length of 7 in. is shown in the figure below. (Eigure 1) Determine the load on the specimen that causes yielding. Express your answer to three significant figures and include appropriate units. HA Py- Value Units Submit Request Answer Part C Figure t oft> Determine the ultimate load the specimen will support. Express your answer to three significant figures and include appropriate units. NO 70 60 50 P. - Value Units 40 30 20 Submit Bequest Answer 10 (in/in) o G04 0m 12 016 020 024 02 a aa omams Provide Feedback
i need the answer quickly
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 60 % - Percentage of Reduction in Area = 36 % - Final length after fracture = 35.2 mm - Final Diameter after fracture = 3.54 mm & - Ultimate stress = 439 MPa i) Initial Length (in mm) = ii) Final Area (in mm2) = iii) Initial Area (in mm2) =
tensile test uses a circular test specimen that has a gage length of 50 mm and diameter = 20 mm. During the test the specimen yields under a load of 100,000 N. The corresponding gage length = 50.5 mm. This is the 0.2% yield point. The maximum load of 180,000 N is reached at a gage length = 65 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage length of 73 mm, determine the ductility. i need clear ans by hand and solve very very fast in 20 min and thank you | DYBALA
Whats the correct answer for this please ?
A cylindrical specimen of a steel alloy 10 mm in diameter and 100mm long is pulled in tension at a load of 23500N and the strain found to be 0.0015, the elongation will be: Select one: 0.15mm Ob. 0.023mm 0.100mm Od. 0.0015mm
A ductile specimen that has an initial length of 10 cm is tested under uniaxial loading. If the test is under tension and the nominal strain is 21.9%, please calculate the true strain in %.
4. For a brass alloy, the stress at which plastic deformation begins is 345 MPa and the modulus of elasticity is 103 GPa. What is the maximum load that may be applied to a specimen with a cross-sectional area of 130 mm² without plastic deformation? b. If the original specimen length is 76 mm, what is the maximum length to which it may be stretched without causing plastic deformation?
A cylindrical specimen of some metal alloy having an elastic modulus of 101 GPa and an original cross-sectional diameter of 3.9 mm will experience only elastic deformation when a tensile load of 4633 N is applied. Calculate the maximum length of the specimen ( in mm) before deformation if the maximum allowable elongation is 0.31 mm.