he extrusion die for a polyethylene parison used in blow molding has a mean diameter of 20 mm. The size of the ring opening in the die is 1.5 mm. The mean diameter of the parison is observed to swell to a size of 22 mm after exiting the die orifice. If the diameter of the blow molded container is to be 160 mm, determine (a) the corresponding wall thickness of the container and (b) the wall thickness of the parison.

Q: For a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene…

A: In this problem, we will calculate the percent crystallinity of the manufactured parts at the given…

Q: A diesel component steel plate has a surface area of 200 in2 with a thickness of 0.002 in. Determine…

A: Given data as per the question Surface area of plate=200 in2=1290.32 cm2thickness =0.002 in=0.00508…

Q: 1. A 150 W immersion heater is used to keep the water in a large beaker boiling under standard…

A:

Q: n a single-barrel extrusion system, the operator observes that the extrudate (made of polyethylene,…

A: v = 0.5 m/sdf = 0.5  d cmW= screw pitch = 1 cmBarrel diameter = 1.5 cmBarrel length, L= 10 cmScrew…

Q: Calculate the surface-to-volume ratio of a sphere of radius r. Then calculate the total drop surface…

A: Given   Surface area, A =  2.80337 cm3 Radius, r1 = 0.50 nm              r2 = 1 mm Find…

Q: 7) You are working on design improvements for a set of 4" diameter gears for a children's toy, and…

A: Concerns High tooling costs and long set-up lead times. Up-front costs are high due to the plan,…

Q: For a powder binding process that mixes a 3:1 volume ratio mixture of semi-crystalline polyethylene…

A: Given: Here are the given data, Density in amorphous state, ρas=0.870 gcm3 Density in crystalline…

Q: An extruder barrel has a diameter of 4.0 in and an L/D ratio of 28. The screw channel depth = 0.25…

A: As per our guidelines, we can answer only one question. Kindly post the remaining question in…

Q: Consider an extruder in which the barrel diameter = 4.5 in and length = 11 ft. The extruder screw…

A:

Q: A hydraulic press for compacting powdered samples has a large cylinder which is 10.0 cm in diameter,…

A:

Q: What are the benefits of using a chain in place of a rope? What are the concerns about dropping an…

A: The advantages of having chain drive over rope are given below. a) In Power transmission through…

Q: A steel plate used for polymer forming is to be bent into a circular shape having an inside radius…

A:

Q: A glass fiber/polymer compound is injection molded in a steel tool. To simplify the analysis, assume…

A: Given Data: D=10 mmL=150 mmt=2 sρ=980 kg/m3μ=1000 N-s/m3   To Find: Injection pressure.

Q: Explain the diameter of the propeller, pitch of the propellerand the drawing given.

A: DefinitionPropeller:The blade rotates and produces thrust by pushing air behind it, This device is…

Q: The recommended sintering time for a pressed part is 20 min. The sintering chamber of the…

A: Given: time = 20 min length = 4m total pieces = 15 pc on 1 m To find: (a) speed of the conveyor (b)…

Q: two cylinders are printed on a 3d printer, with a setting of 40% fill rate. This means that the…

A: Fill rate is the percentage of total volume which is filled by plastic. For given problem, fill rate…

Q: 12) Assuming injection molding pressures of 10kpsi, estimate the die clamping force required for…

A: Disk diameter=1.5 inch Pressure P=10kpsi Runner area= 5.0 in2 there 10 identical which means Area of…

Q: An extruder barrel has a diameter of 4.0 in and an L/D ratio of 28. The screw channel depth = 0.25…

A: As per our guidelines, we can answer only one question. Kindly post the remaining question in…

Q: In powder processing, a cylinder with a diameter of 2 inches and a height of 10 inches is to be made…

A: To findEstimate the compaction pressure at the punch surface.Givendiameter of cylinder, Height, The…

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.