Glass has density of 3.1 Mg/ m³, specific heat of 0.88 j/g.k, fracture strength of 300 Mpa,elastic modulus of 400Gpa, coefficient of expantion 4.5 x 10-6 /k ,thermal conductivity of 100w/m.k ,thermal diffusivity of 37 x 10-6 m² /s, poission ratio of 0.2 Calculate the themal shock resistace at measuring unit of : 1. K 2.w/m 3. m² k/s

Glass has density of 3.1 Mg/ m³, specific heat of 0.88 j/g.k, fracture strength of 300 Mpa,elastic modulus of 400Gpa, coefficient of expantion 4.5 x 10-6 /k ,thermal conductivity of 100w/m.k ,thermal diffusivity of 37 x 10-6 m² /s, poission ratio of 0.2 Calculate the themal shock resistace at measuring unit of : 1. K 2.w/m 3. m² k/s

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

ε = ce { 3. Assume the activation energy for the creep of Al2O3 is 425kJ/mol. (a) Predict the creep rate, &, for Al2O3 at 1000°C and 1800 psi applied stress. (See Table 6.12 for data at 1300°C and 1800psi.) (b) Calculate the lifetime of an furnace tube at 1000°C and 1800 psi if 1% total strain is permissible. (ε = 2.7x10-6/hr for Al2O3 at 1300°C and 1800psi.)
A new sintering regime is proposed for producing Alumina acetabular liners for total hip replacement. If the alumina has a plane strain fracture toughness of 2.7 MPa.mº.5, an ultimate tensile strength of 307 MPa and Y is assumed to be 1.2, which of the following would be the maximum acceptable size of surface flaw? Select one: Ⓒa. 4.8 μm O b. 9.6 μm O c. 19.2 μm O d. 2.4 μm
QI/ If the thermal shock resistance of RBSN is 2214 w/m, poission ratio= 0.2 , cofficient of expansion= 2.6 x 10 /k, thermal conductivity=9 w/ m.k, specific heat= 0.86 j/ g.k ,thermal diffusivity= 4.4 x10 m /s, modulus of elasticity = 200 Gpa Calculate : 1.fracture streangth in Mpa 2. the density in Mpa 3. the thermal shock resistance in m' k/ s
The major difference between solid and fluid is the molecules are well-packed in solid but free to move in fluid. As a consequence of such difference, which of the following statements are correct? (i) Stress is proportional to strain in solid but stress is proportional to rate of strain in fluid. (ii) Fluid can be used as a lubricating film to separate 2 solid surfaces from direct contact to reduce friction. (iii) The energy required to move a ship slowly is low but increases rapidly with speed. (A) (B) (i) and (ii) (i) and (iii) (ii) and (iii) All of the above
Given the following: Cp of Br: 0.226 J/g-K BP of Br: 59 deg C density of Br: 3.12 g/mL Hvap of Br: 30,900 J/mol V of liquid Br solution: 50 mL Cp of Br2: 0.473 J/g-K What is the total heat required in heating Br from 25 to 75 deg C?
5. Figure shows the cooling curve for aNiO-MgO ceramic. (e) the super heat; 2800 2700 2600 2525 2500 28 2400 10 20 30 40 50 Time (min) Temperature (°C)
If the viscosity of SCl2 gaseous molecule at 20.0 °C and 1 atm. is 132 pP. what is the viscosity of 7cz gaseous molecule in pP at the same temperature and pressure assuming both molecules having the same cross section? (MM of 35c - 35.0g mol MM of 37a - 37.0 g mol1)
Compute the fracture stresses in MPa for internal cracks that are 6.00 cm long in a composite of Kevlar 49 in F-155 epoxy with a fracture toughness of 23.0 MPa-m1/2.
In a thin-walled cylindrical pressure vessel, the axial and circumferential joint efficiencies specified to account for fabrication process and inspection procedure considerations are 1.0 and 0.5 respectively. The ratio between the circumferential stress and axial stress used in the design is, O a. 4:1 O b. 1:1 Oc. 2:1 O d. 1:2
In a laboratory creep experiment at 1273K, a steady-state creep rate of 5 ××10-1 %, per hour is obtained in a metal alloy. The creep mechanism for this alloy is known to be dislocation climb with an activation energy of 200 kJ>mol. Predict the service temperature in (°C) for a creep rate of 8.68 ×10-5 %, per hour. (Assume that the laboratory experiment duplicated the service stress.)
Determine the notch sensitivity for the specimen whose max strese in notched specimen is 250MPa and stress in notch free specimen is 100 the theoritical stress concentration factor is given by .6
Show the steps