Answered: For a material with poisons ratio 0.25,…

Engineering

Civil Engineering

For a material with poisons ratio 0.25, the ratio of modulus of rigidity to modulus of elasticity will be

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 13CQ

See similar textbooks

Related questions

Q: An aluminum alloy cylinder with a diameter of 3 in. and a height of 6 in. is subjected to a…

Q: Two bars of different materials and same size are subjected to the same tensile force. If the bars…

A: Given data: Unit elongation =δLδ1Lδ2L=25

Q: A round steel alloy bar with a diameter of 19 mm and a gauge length of 76 mm was subjected to…

A: Calculate the stress at different deformation points, σ = LoadCross sectional area Calculate the…

Q: On the stress-strain diagram of a steel bar, show and explain the following: proportional limit,…

Q: Problem 11. [Concepts: Calculating stress from internal forces, nonlinear stress-strain response,…

A: a) Determine the yield strength assuming a 0.2% offset.b) If a bar of this material has a length of…

Q: A 10.0 mm diameter cylindrical specimen of a bearing bronze material is pulled under uniaxial…

A: given-10.0 mm diameter 1500 N force∆d=0.67 mmn=0.35

Q: A tensile stress is applied along the long axis of a cylindrical steel rod with adiameter of 10 mm.…

A: The given data is as follows: Diameter=10 mmChange in diameter=5×10-3 mmModulus of elasticity=200…

Q: 29. During laboratory testing of an 8-inch aluminum-alloy rod with a cross sectional area of…

A: Given:- The length of the aluminum-alloy rod during testing = 8 inch The cross-sectional area of…

Q: The following figure shows the tensile stress-strain curve for a plain-carbon steel. 600 80 500 MPa…

A: a) Ultimate tensile strength is 580 MPa (Approximately).

Q: Consider a cylindrical specimen of a steel alloy 10.0 mm in diameter and 75 mm long that is pulled…

A: the test is conducted in UTM. the test is standardized by American testing society material . the…

Q: An aluminum alloy cylinder with a diameter of 76 mm and a height of150 mm. is subjected to a…

Q: An aluminum alloy bar with a radius of 7 mm was subjected to tension until fracture and produced…

A: Since we answer Three subpart at a time so we will answer the first three. Please resubmit another…

Q: Question No.2 Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion…

A: It is that point on stress-strain curve, till which stress is linearly varying with strain. As per…

Q: A specimen of steel has a rectangular cross section 20 mm wide and 40 mm thick, an elastic modulus…

A: solution Given tension P =60000N cross section =20mm×40mmelastic modulus E=207Gpa=207000Mpa…

Q: A tensile stress is applied along the long axis of a cylindrical steel rod with a diameter of 10 mm.…

A: It is required to calculate the strain in the x-direction. Here, is the change in diameter, and do…

Q: S Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until…

A: a). Proportional Limit : The proportional limit is the point up to which the stress-strain curve is…

Q: A steel solid is subjected to following set of principal stresses: o1 = 300 MPa and o2 = 250 MPa.…

Q: A steel alloy specimen having a rectangular cross section of dimensions 19.1 mm x 3.1 mm (0.7520 in.…

Q: Find the poisson's ratio for a given material if the modulus of elasticity is 100 GN/m2 and it's…

Q: Determine the value of strain if modulus of elasticity is 70 MPa and stress is 20 MPa

A: Introduction : The given question is related with solid mechanics . In this question we are provided…

Q: 3. The distribution of stress in an aluminum machine component is given (in megapascals) by Ox = y +…

A: The stress tensor is:

Q: A mild steel specimen originally 300 mm long is pulled in tension with a stress of 500 MPa. If the…

A: Given: Original length of specimen, l = 300 mm Tensile stress, s = 500 MPa Modulus of Elasticity, E…

Q: Which of these elastic moduli describes the ratio between volumetric stress and volumetric strain?…

A: a) Young's modulus of elasticity is defined as the ratio of normal stress to normal strain. b) Shear…

Q: If Poisson's ratio is 0.42, the Modulus of rigidity is 70.4225 GPa, and the bulk modulus is 416.66…

Q: Problem 3: Diameter of the metal bar, before and after load application was measured to be 100.00 mm…

Q: A tensile stress is to be applied along the axis of a cylindrical steel rod that has a diameter of…

A: Given data : Poisson's ratio (μ)=0.3Diameter (d)=7.5 mmModulus of elasticity (E)=207 GPaChange in…

Q: Material Yield Tensile Strain at Fracture Elastic Strength StrengthFractureStrengthModulus (MPa)…

A: a) For material to experience the greatest percentage reduction in the area it should have a higher…

Q: A 12-mm thick steel tire has a width of 110 mm and an internal diameter of 800 mm. It is heated and…

Q: The stress-strain diagram for a steel alloy having an original diameter of 0.5 in. and a gage length…

A: We have to determine the value of approximate amount of elastic recovery and the increase in the…

Q: Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until…

A: (a) The proportion limit is the point on the the graph upto which the stress strain curve is…

Q: Determine the Poisson's ratio v.

Q: An aluminum alloy bar with a rectangular cross section that has a width of 12.5 mm, thickness of…

A: (a) Load (kn) Elongation (mm) area (mm2) stress (mpa) strain 0 0 78.125 0.00 0 3.3 0.025…

Q: Determine the modulus of Elasticity E for a material that has proportional stress of 100 MPa and…

A: Given data : Proportional stress (σ)=100 MPaProportional strain (ε)=0.001Strain has no unit .

Q: ne force that will produce an elastic reduction of lus (E) and Poisson's ratio (v) are,…

Q: A 100 mm x 100 mm x 100 mm cube made with glass polymers in the y- direction is subjected to a…

A: Given data: Py=100 kNEx=20 GPa Vxy=0.25Ey=50 GPa Vxz=0.5Ez=20 GPa Vyz=0.25…

Q: Your answer is incorrect. An extruded polymer beam is subjected to a bending moment M. The length of…

Q: A steel bar has a length of 2.5 m and cross-section of 200-mm x 100-mm. The modulus of elasticity of…

Q: A machine component is subjected to a load of P = 3,800 N. Which stress element represents the state…

A: Stress element: The elements which are generally used to represent the stresses acting at a point on…

Concept explainers

Bars

In civil engineering, bars refer to steel reinforcement bars or rebars. These are structural members primarily used for reinforcement purposes in masonry works. A bar is characterized by its cross-sectional area, which is negligible compared to its length. Bars are usually manufactured by steel which is uniform throughout the length, or by meshing multiple steel wires. Other materials of the bar include carbon steel, glass fiber, carbon fiber, and basalt fiber. The reinforcing bars are coated with epoxy resins and other materials to enhance some of their properties including corrosion resistance.

Question

For a material with poisons ratio 0.25, the ratio of
modulus of rigidity to modulus of elasticity will be

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
A specimen of steel has a rectangular cross section 20 mm wide and 40 mm thick, an elastic modulus of 207 GPa, and a Poisson's ratio of 0.30. If this specimen is pulled in tension with a force of 60,000 N, what is the change in width if deformation is totally elastic? O Increase in width of 3.62 x 10-6 m O Decrease in width of 7.24 x 10-6 m Increase in width of 7.24 x 106 m O Decrease in width of 2.18 x 10-6 m
A bronze rod is rigidly attached between an aluminum rod and a steel rod as shown in the figure below. Axial loads are applied at the positions indicated. a) Find the maximum value of P that will not exceed a stress in steel of 140 MPa, in bronze of 100 MPa, or in aluminum of 90 MPa. b) Determine the deformation of the bronze rod if the value of P is 22.50 KN. The moduli of elasticity are 200 GPa for steel, 80 GPa for bronze and 70 GPa for aluminum.
For a material, stress at proportionality limit is 200 MPa and modulus of elasticity is 200 GPa. The modulus of resilience for the material will be
S Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 900 Metal A 600 Metal B 300 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, m/m FIGURE P1.16 Stress, MPa
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 740 mm. The cross-sectional dimensions of the beam are b1= 35 mm, d1= 101 mm, b2 = 21 mm, d2 21 mm, and a = 7 mm. For this material, the allowable tensile bending stress is 13 MPa, and the allowable compressive bending stress is 13 MPa. Determine the largest moment M that can be applied as shown to the beam. %3D b2 M. d2 di 14 L. b1 Answer: N-m M = %3D
A cylindrical polymer with a diameter of 10nm when stress is applied to it and a change in diameter of 0.0025nm is equal. If you know that the polymer is completely elastic and the modulus of elasticity is 97Gps, what is the amount of elongation in the direction of the x-axis
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 620 mm. The cross-sectional dimensions of the beam are b1 = 39 mm, d, = 82 mm, b = 23 mm, dɔ = 23 mm, and a = 8 mm. For this material, the allowable tensile bending stress is 20 MPa, and the allowable compressive bending stress is 12 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 lak M di B L b1 Answer: M = i N.m
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 560 mm. The cross-sectional dimensions of the beam are b1 = 32 mm, d1 = 118 mm, b2 = 19 mm, d2 = 19 mm, and a = 6.5 mm. For this material, the allowable tensile bending stress is 14 MPa, and the allowable compressive bending stress is 13 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 a M d2 | A В b1 Answer: M = i N-m
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 900 mm. The cross-sectional dimensions of the beam are b1 = 37 mm, d1 = 88 mm, b2 = 22 mm, d2 = 22 mm, and a = 7.5 mm. For this material, the allowable tensile bending stress is 18 MPa, and the allowable compressive bending stress is 14 MPa. Determine the largest moment M that can be applied as shown to the beam.
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 760 mm. The cross-sectional dimensions of the beam are b1 = 33 mm, d1 = 110 mm, b2 = 20 mm, d2 = 20 mm, and a = 6.5 mm. For this material, the allowable tensile bending stress is 11 MPa, and the allowable compressive bending stress is 12 MPa. Determine the largest moment M that can be applied as shown to the beam.
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 700 mm. The cross-sectional dimensions of the beam are b1 = 30 mm, d1 = 103 mm, b2 = 18 mm, d2 = 18 mm, and a = 6 mm. For this material, the allowable tensile bending stress is 11 MPa, and the allowable compressive bending stress is 12 MPa. Determine the largest moment M that can be applied as shown to the beam.