Cylindrical samples of steel, glass and rubber are each subjected to a gradually increasing tensile force F. The extensions are measured and graphs are plotted as shown below. Which row in the following table correctly relates the graphs to the materials?

Cylindrical samples of steel, glass and rubber are each subjected to a gradually increasing tensile force F. The extensions are measured and graphs are plotted as shown below. Which row in the following table correctly relates the graphs to the materials?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1.3 mm at 18 kN and Final diameter if the percentage of reduction in area is 25 %. Fine this ans 1-Initial Cross-sectional Area (in mm2) 2-The Diameter of the Specimen (in mm) 3-Final Length of the Specimen (in mm) 4-Stress at the elastic load (in N/mm2) 5-Young's Modulus of the Specimen (in N/mm2) 6-Final Area of the Specimen at Fracture (in mm) 7-Final Diameter of the Specimen after Fracture (in mm)
640 480 160 0.002 0,004 0.006 0.008 0.010 Strain (mm/mm) A tensile test specimen of Aluminum alloy having a gauge length of 280 mm was tested to fracture. Stress and strain data obtained during the test are shown in the attached Figure. **Answers are approximate - do your best to read the graph. Determine: (a) the modulus of elasticity in GPa (4sigs). Enter this value into D2L answer box. (b) the proportional limit in MPa (3sigs). (c) the ultimate strength in MPa (3sigs). (d) Ductility of material based on percent elongation. (3sigs) Your Answer: Stress (MPa)
15. Given the following data, plot the stress-strain curve for this tensile steel specimen. The gage length of the specimen is 2.0". The cross sectional area is 0.195 in². Use the diagram that you plot to determine: a.) The Modulus of Elasticity b.) The Yield Stress c.) The Ultimate Stress LOAD P (pounds) Deformation (inches) 0.0000 3000 0.0007 0.0017 0.0025 6000 9000 12000 14000 0.0036 0.0044 15000 0.0060 0.0100 16000 17000 0.0250 0.2000 0.4000 18000 12000* rupture occurred. 2.
As Fast As you can Please mak sure the answer is correct 100% Please match the following to the appropriate areas or sublocations illustrated on the steel stress-strain curve shown below: (ultimate tensile stress- yield stress - repture stress) (4) The maximum stress point on the stress strain curve. (2) The point where the proportional limit ends and the moment the elastic limit of the specimen is reached, the specimen will return to its original state after the loading is removed. Typically occurs before the steel specimen starts to plastically yield. (5) The point at which the steel specimens has underwent necking and breaks. This typically occurs after the maximum stress is reached during the experiment.
A structural member 10 cm long must be able to support a load of 50,000 N without experiencing any plastic deformation. Given the following data for brass, steel, aluminum, and titanium, rank them from least to greatest weight in accordance with these criteria. Yield strength Ultimate tensile Alloy Density (g/cm3) (MPa) strength (MPa) Brass 415 600 8.5 Steel 860 800 7.9 Aluminum 310 435 2.7 * 700 Titanium 550 4.5
2-15 Brinell hardness tests were made on a random sample of 10 steel parts during process- ing. The results were Ha values of 230, 232(2), 234, 235(3), 236(2), and 239. Estimate the mean and standard deviation of the ultimate strength in kpsi. Ans: 50.111 kpsi Som- / -1 bpci
Question 4 Save Answer You do a series of tensile tests on plates of a magnesium alloy that have been subjected to prior cold rolling to true plastic strains of 0.1, 0.2 and 0.3. The resulting true stress-true strain curves are shown below (including a zoomed in version expanding on the small strain region). It is reasonable to approximate the the 0.2% offset yield strength of the magnesium as ✓ MPa for 0.2 and ✓ MPa for 0.3. Assuming the yield strength is ✓ MPa for 0.1 plastic strain, proportional to the square root of the prior true plastic strain results in a hardening coefficient of approximately k= MPa. Hence, we can predict that we need a prior plastic strain of approximately True Stress (MPa) True Stress (MPa) True Stress (MPa) 250 200 150 100 50 0 0.00 250 200 150 100 50 0 0.00 250 200 150 100 50 0 0.00 Ep = 0.1 0.01 Ep=0.2 0.01 Ep=0.3 0.01 0.02 True Strain 0.02 0.03 0.02 0.03 True Strain 0.03 0.04 0.04 0.04 True Stress (MPa) 0.05 0.000 0.001 True Stress (MPa) Ep=0.1 True…
Draw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking region
Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…
A piece of steel rebar is tested in tension to determine its mechanical properties. The length of the sample is 87.3 mm and the cross-sectional area is 52.1 mm². When stretched by 37.2 mm, the force measured is 14,884 N. At this point, the graph is non-linear, but no clear neck is visible. If the Poisson's ratio of the material is 0.281, calculate the cross-sectional area (mm²) at this point.
Load (N) Elongation (mm) In a tensile test of stainless steel, the following data were obtained: 7,200 11,250 13,500 16,200 18,900 20,200 20,700 13,200 24.90 0.0 0.505 2.03 5.08 10.16 15.24 21.80 The dimensions of the cylindrical specimen were initial length L₁= 50.8 mm and initial area A₁ = 35.8 mm² and the area at fracture was Ar = 10.0 mm². Plot the stress-strain diagram and determine the following: a) Modulus of elasticity b) The yield strength at a strain offset of 0.002 c) Ultimate strength d) Fracture strength
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture