Consider a metal single crystal oriented such that the normal to the slip plane and the slip direction are at angles of 35.5° and 25.4° , respectively, with the tensile axis. If the critical resolved shear stress is 25 MPa, will an applied stress of 30 MPa cause the single crystal to yield? If not, what stress will be necessary?

Q: What is the defect size in soda-lime-silicate glass if KIC = 750 KN m²3/2 and the typical measured…

A: Given: The fracture strength, KIC = 750 kN.m^3/2 The ultimate strength = 70 MPa

Q: Determine the critical resolved shear stress on a BCC single crystal if a normal stress of 10 MPa…

A: Given data: Normal stress σ=10 MPa acts along l=[100] direction. Applied stress causes slip in the…

Q: In hot working of metals, the distorted grains are completely removed and fresh new grains are…

A: In hot working of metals, the distorted grains are completely removed and fresh new grains are…

Q: A. A tensile stress (♂) is applied to a single crystal. The angle between the direction of the…

A:

Q: A cylindrical specimen of a cold-worked brass has a ductility (%EL) of 21%. If its cold-worked…

A:

Q: t as a separate question that has no relationship to previous parts of the question. 1 and 2 are…

A:

Q: Some aircraft component is fabricated from an aluminium alloy that has a plane strain fracture…

A:

Q: The yield region for steel that has a normal grain diameter of 2.4x10-2 mm is 260 MPa. At a grain…

A:

Q: A single crystal metal test sample oriented such that a tensile stress is applied in the [012]…

A:

Q: When λ=1.5Å and θ=30°, how much strain (Δd/d) is needed to cause a peak broadening same as that of…

A: This problem is related to Braggs law.  if λ is the wavelength of X-ray,d is the distance between…

Q: In hot working of metals, the distorted grains are completely removed and fresh new grains are…

A: Basics of Hot working.

Q: The yield stress for a metal changes from 410 Nmm^-2 to 670 Nmm^-2 when the average grain diameter…

A: Given:σy1=410 N/mm2    σy2=670 N/mm2d1=0.053 mmd2=0.037 mmdavg=0.045 mmσy=560 N/mm2

Q: The critical resolved shear stress for a metal is 33 MPa. Determine the minimum stress necessary to…

A: Given Data

Q: There are three slip systems on a FCC octahedral plane, i.e. one of the {111} planes. Assume a 2 MPa…

A: "Since you have asked multiple questions, we will answer the first question for you. If you want any…

Q: A monocrystal of a CCC metal is oriented so that the direction [001] is parallel to an applied…

A: Given data A mono crystal of a bcc metal is oriented so that  the direction is parallel to the…

Q: From the grain distribution curve, D60 = 1.45 mm, D30 = 0.75 mm and D10 = 0.45 mm. Determine the…

A: Write the formula for uniformity coefficient. Cu=D60D10 Here, Cu is the uniformity coefficient, D60…

Q: 3. How can you understand if a fracture is brittle or ductile? Briefly explain which experimental…

A: If a specimen under tension test results in a noticeable value of strain before it fractures, then…

Q: You are given 1) the normal to the slip plane and the normal to the slip direction angle with the…

A:

Q: Determine the critical resolved shear stress on a BCC single crystal if a normal stress of 10 MPa…

A: Write the formula for the angle between two planes with Miller indices [u1 v1 w1 ] and [u2 v2 w2].…

Q: Some aircraft component is fabricated from an aluminium alloy that has a plane strain fracture…

A:

Q: onsider the tensile stress-strain diagram in the figure below labeled 1 and 2. These diagrams are…

A:

Q: (i)Explain why the titanic was failed catastrophically (ii)Determine the suitable laboratory testing…

A: 1. It should be a type of  catastrophic failure in the structural materials because of the below…

Q: Which one of the following materials would plastic deformation through twinning be the most likely…

A: Since you have asked multiple question, we will solve the first question for you. If you want any…

Q: Slip in Single Crystals 2. Consider a metal single crystal oriented such that the normal to the slip…

A: Given:The normal to the slip plane makes an angle, The slip direction makes an angle, The critically…

Q: A single crystal of aluminum is loaded under a stress state such that ơi1 = 250 kPa, 022 = 50 kPa ,…

A: Write the x-coordinate of the normal unit vector to the (1 1 1) plane. Inx=1112+12+12     =13 Here,…

Q: determine the critical resolved shear stress for aluminum.

A:

Q: 4. What is ductile brittle transition temperature? Draw a plot between impact energy of fcc, bcc and…

A:

Q: 2.2. When the Hall-Petch coefficient is 20 GPa nm/2, estimate the grain size of this alloy after…

A: Hall-Petch coefficient (k) = 20 GPa nm^1/2From the hand-written notes,yield strength of the alloy,…

Q: 5. Consider a single crystal of some hypothetical metal that has the FCC crystal structure and is…

A: The solution is provided below.

Q: A tensile stress of 25.0 MPa is applied on a single crystal of nickel oriented such that the tensile…

A:

Q: :) Consider a homogeneous structure made out of metal subjected to homogeneous oundary conditions t…

A: The yield stress for a material subjected to different stress states can be determined using…

Q: Problem 3. The following two questions relate to residual stress. (1) Explain why thermally grown…

A: Note: Since you have posted multiple independent questions in the same request, we will solve the…

Q: Q2 The main factors that make a material more likely to undergo a ductile failure could be:

A: Ductile failure: Metals are commonly described as ductile or brittle. When they fail as a result of…

Q: Problem 1 out of 2: A single crystal of a metal that has the BCC crystal structure is oriented such…

A:

Q: Explain the basis of Paris' Law and discuss with a sketch the relationship between crack growth rate…

A: "Since you have asked multiple questions, we will solve the first question for you. If you want any…

Q: In order to find out the effects of the grain sizes on the mechanical strength of a metal, three…

A: Given data: