QUESTION (B) please Figure 1 shows the Binary Eutectic Phase Diagram of Pb-Sn.a) What is the name of Alloy 1 and Alloy 2?b) Find weight percent composition of Alloy 2 at a,c,d,e points using Lever Rules and Tie-Linemethod.Temperature (°C)in a327300250200150100500100%Pba183SolidusSolvus10a + liquid19.2Liquidusil2030Alloy 2e40.0Alloy 1Liquida + ß61.9li4050 60Weight percent tinLiquidus3+ liquidEutectic point70 80 90Figure 1: Binary Eutectic Phase Diagram of Pb-Sn.97.5100%SnSolidus-BSolvus

To calculate the weight percentage of Alloy 2 at a,c, d, e

b) Find weight percent composition of Alloy 2 at a,c,d,e points using Lever Rules and Tie-Line method. 327 300 250 200 a Solidus Liquidus a + liquid Alloy 2 7 Alloy 1 I Liquid Liquidus 3+ liquid Solidus

b) Find weight percent composition of Alloy 2 at a,c,d,e points using Lever Rules and Tie-Line method. 327 300 250 200 a Solidus Liquidus a + liquid Alloy 2 7 Alloy 1 I Liquid Liquidus 3+ liquid Solidus

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: 2.1 Please help. Written on paper not typed on computer or keyboard please. Need help both…

A: The weight of the box can be found by multiplying its mass by the acceleration due to gravity. Since…

Q: . Sitting in front of her all-wooden desk in her all-wooden chair, a writer reached for her wooden…

A: a) Principle of motion economy violated in this work sequence are as follows 1. Two or more tools…

Q: Instructions: In this exercise, incomplete relationships are set up among fluid conductors and…

A: Here we have to complete the relationship among fluid conductors and connectors by choosing…

Q: Experiment 1: The atmosphere a) Calculate the mass of air in a typical classroom (50 feet long, 30…

Q: rate you with “LIKE/UPVOTE," if it is COMPLETE STEP-BY-STEP SOLUTION. If it is INCOMPLETE…

A: Given Data : For triangular section : Load intensity(h)= 6 KN/m Distance upon which load is…

Q: A printer costs $900. Its salvage value after 5 years is $300. Annual maintenance is $50. If the…

A: Given: Printer cost; P = 900 $ No. of years; n =5 Salvage value; F =300 $ Annual maintenance; M =…

Q: Coal has the following ultimate analysis: C=73.71%, H=1.78%, O=1.43%, N=1.69%, S-4.74%, and the…

Q: An ideal gas undergoing an isobaric process initially occupies a volume of 1500 L, pressure of 450…

Q: If it is INCOMPLETE SOLUTION and there are SHORTCUTS OF SOLUTION, I will rate you with…

A: Given Data⇒ Load intensity for rectangular section : F=4 KNm Distance upon which load is…

Q: The diameters of the two cylinders A and B in the figure shown are 80 mm and 750 mm, respectively.…

Q: Each bar chart should show the distribution of energy across the categories as well as the total…

Q: A gas is contained in a cylinder with a moveable piston on which a heavy block is placed. Suppose…

A: As per given question we have determine What is the distance s through which the piston rises?

Q: You are in an inventory management field these days. You are working for a place which works on 365…

A: The objective of this question is to determine the number of orders per year that should be placed…

Q: I will rate you with “UPVOTE/LIKE” if you answer every question. I will rate you with…

A: Given Data : Force systems

Q: Using the Method of Compone nts (no other method will be accepted) in tabular format learned in…

Question

QUESTION (B) please

Figure 1 shows the Binary Eutectic Phase Diagram of Pb-Sn.
a) What is the name of Alloy 1 and Alloy 2?
b) Find weight percent composition of Alloy 2 at a,c,d,e points using Lever Rules and Tie-Line
method.
Temperature (°C)
in a
327
300
250
200
150
100
50
0
100%
Pb
a
183
Solidus
Solvus
10
a + liquid
19.2
Liquidus
il
20
30
Alloy 2
e
40.0
Alloy 1
Liquid
a + ß
61.9
li
40
50 60
Weight percent tin
Liquidus
3+ liquid
Eutectic point
70 80 90
Figure 1: Binary Eutectic Phase Diagram of Pb-Sn.
97.5
100%
Sn
Solidus
-B
Solvus

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: Introduction

VIEW

Step 2: calculate weight percentage of alloy 2

VIEW

Solution

VIEW

Step by step

Solved in 3 steps with 3 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Phase Diagrams and Its Applications in Metallurgy

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

i need the answer quickly
(a) Indicate hypooeutenic, hypereutenic ranges and eutenic composition in wt%Sn. Use the phase diagram below.
Need asap
3
Use the phase diagrams for Cu-Ni and Cu-Ag systems below to answer the question: Based on the mechanism, would you expect a solution containing 80 wt% Cu to be stronger if the remaining 20% of the alloy was Ni or Ag? Briefly explain
help pls A two-phase phase diagram is shown. Answer the following questions t -1300 1500+ Temperature 1100 0 34 54! 166 482 80 Composition of Ni % 20 What is the composition (in % Cu) of the solid phase corresponding to the red dot in between the solidus and liquidus lines in the phase diagram? Just write the number. Do not write the % symbol. Question 17 2.33 100 An alloy is being made with 66% Ni and 34% Cu. When it is cooled from 1500°C to the temperature corresponding to the red dot in the phase diagram, how many kg of liquid is present in the mixture?
Temperature (°C) Based on the Ti-Al phase diagram (important for standard commercial alloy Ti-6Al- 4V) shown below, identify a) the type of reaction (e.g., peritectic) of the marked points (1) and b) list the phases before and after the reactions. 10 20 Weight percent aluminum 30 40 50 60 70 80 90 100 1800 1700 1670°C (1) 1600 L 1500 1400 a (ẞTi) 1300 1285 y-TiAl 1200 1100 1125 لسسسلسسسل 1000 Ti, Al (L10) 900 ር? 882°C 800 (aTi) (D019) 700 600 500 0 10 20 Ti Superlattice structures -TiAl, 665°C 660.452°C TiAl₂ aTiAl3 (Al). 20 30 40 50 60 70 80 90 100 Atomic percent aluminum PM Al
Can you pleae solve this and show all your work
part a) A carbon-Fe alloy containing 1.5 wt% C is cooled down to 800°C. Determine what phases are present, the fraction of each phase present, and the composition of each phase. part b) A carbon-Fe alloy containing 1.5 wt% C is cooled down to 400 Celsius. Same as above, determine what phases are present, the fraction of each phase present, and the composition of each phase. use the picture below Irn-Iron Carbide Phase Diagram 1600 8 (Ferrite)N538°C 1100 2000 1495°C Liquid 1000- 1400 1394°C 1200 Y (austenite) 2500 y +liquid 1148°C 2.11% 900 Y+ Fe,C 4.30% 2000 1500 800 1000 Y+ cementite Detail view 727°C a+y 700 912°C 727°C a+y 80에 0.77% 0.022% 1500 Ferrite 600 600 a + cementite -Fe,C 1000 α (errte) 1000 Cementite (FeC) - 500 400 a + Fe,C 1 Carbon (% by weight) 6 6.67 0.5 1.0 Carbon (% by weight) 1.5 2.0 2.5 (a) (b) FIGURE 5.4 (a) The iron-iron carbide phase diagram. (b) Detailed view of the microstructures above and below the eutectoid temperature of 727°C (1341°F). Because of the…
Given the Cu-Zn phase diagram below, determine the amount of the phase/s present of a 75 wt% Zn -25 wt% Cu alloy for the following temperatures. Indicate the required composition for each temperature in the diagram. Round off your final answers up to two decimal places. Show your solutions completely and neatly and follow the table format below, Temperature Phase/s present Phase composition Relative amount 600 °C 570 °C y+ L 700 1200 8+L L 600 P 598°C 560°C 570 |1000 e + L y +e 500 60 68.6 70 74.3 75 78.2 80 90 Composition (wt % Zn) Temperature (°C) ta Temperature (°F)
For the alloy Mg-45 wt% Pb alloy at 500 C, what is the percentage of the liquid phase?
Figure 1 show Eutectoid Plain Carbon Steel Phase Diagram. Please indicate the phases present and their corresponding weight fraction at points a, b, c and d. Show your tie-line and calculations based on Lever Rules. Temperature (°C) 1100 900 700 500 300 100 0 100% Fe 7 0.02 1.0 Fe,C 1.2 2.0 7 7 7 7 Fe, C Figure 1 Fe,C Pearlite 4.0 3.0 Weight percent carbon 7+ Fe, C 727°C a + Fe₂C 5.0 Fe, C 6.0 6.7