b) A 1-cm-thick copper plate is cold-reduced to 0.50 cm and later further reduced to 0.16 cm. Determine I. The total percent cold work and Il- Predict the properties of the metal at the calculated cold work? 0.16 cm I cm 0.5 cm Figure-2

b) A 1-cm-thick copper plate is cold-reduced to 0.50 cm and later further reduced to 0.16 cm. Determine I. The total percent cold work and Il- Predict the properties of the metal at the calculated cold work? 0.16 cm I cm 0.5 cm Figure-2

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: In an engineering application, the material is a strip of iron with a fixed crystallographic…

A: Given: The yield strength of material for grain size of 30 microns, σ₁ = 110 MPa The yield strength…

Q: The effect of temperature on the crystallization of a material is given below. Calculate the…

A: Given is Effect of temperature on the crystallization of the material To determine…

Q: Identify the material as shown in the figure.,

Q: Certain type of steel whose Proportional limit the above theðry sing n The principal stresses were…

Q: Q.3 a - What are the most preffered properties in metals to be used in high temp. to resist creep…

A: Properties of material which are used to resist the creep. *** AS per our company policy we are…

Q: t as a separate question that has no relationship to previous parts of the question. 1 and 2 are…

Q: Explain the Stress Strain Relationship with the help of graph

A: We have to explain stress strain relationship

Q: B43 (a) For moderate loads, most metals are elastic. What is meant by the term clastic? (b) The…

Q: The figure below is a stress strain curve for an alloy of aluminum at various temperatures. a) What…

A: (a) Draw the line at the Centre between the temperatures 250k and 350k. This line gives line of 298k…

Q: Temperature (°C) 1600 (1) 1400 1200 1000 800 600 400 1538°C (Fe) 912°C 8+7 1394°C(F) -1493°C (G) y,…

A: Given:

Q: The yield region for steel that has a normal grain diameter of 2.4x10-2 mm is 260 MPa. At a grain…

Q: Strain hardening is associated with hot working process. Select one: True False

Q: A cold worked brass specimen of average grain size 0.02 mm has a yield strengh of 160 MPa. Estimate…

A: From Hall-Petch equation - σy =σi + kyd-12Let us calculate the value of constant σi (Putting the…

Q: Which of the following startements is incomeef? A Under and fatigne 1oa0ding materials may fail at…

A: The incorrect statement out of the above given statements is option (D) (D) Choosing the material…

Q: Q2/ hardness test type (Brinell hardness Test) was applied to an alloy, the device shows that BHN…

A: Dear student, According to guidelines I am allowed to answer only one problem…

Q: Determine values for the constants n and k for the recrystallization of copper (Figure 10.11) at…

Q: Q1: Which one is stronger; pure copper with 10-μm grains or pure copper with 100-um grains? Q2:…

Q: 1) The shape and magnitude of the stress-strain curve of a metal will depend on i. Composition…

A: Stress strain curve: It is a graphical representation of the material's deformation with a…

Q: The three figures show the stress-strain diagram for three different metals, c, b, and a, if you…

A: (a) The metals according to the increasing ductility are arranged as shown below. c>b>a…

Q: The uniaxial stress-strain diagram of a typical material can be following? Can you expect Kinematic…

Q: Don’t use ai pls

A: Step 1:The steel with carbon content 0.78% is called as eutectoid steel. In this project, the steel…

Q: 2- A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length…

A: Given: Dia-0.495 in. Gauge length = 2 in

Q: Borosilicate glass bottles are processed into bottles using press and blow method shown in Figure…

A: Blow moulding is the process of inflating or blowing a thermoplastic molten tube termed a…

Q: Figure 2 shows the results of tensile tests performed on Alloys A and B. Interpret from the curves…

A: The figure given is : It represents two materials with different material properties

Q: hy.

A: The hardness is usually based on the hardness of the material.

Q: Strain hardening aluminium increases the strength by reducing the number of dislocations True False

Q: the reasons: a): Show the effect of factor in List (I) on the property in List (II), and give (1):…

A: Given some factors and properties in the table. The objective is to find out the effect of these…

Q: Choose a common metal that is solid at 0°C and liquid at 1500°C. a) Look up the following values:…

Q: An 0.29 inch diameter copper bar is to be cold worked 57%. Find the final diameter in inches.

A: Givend=0.29 inchCW=57%

Q: An aluminum specimen subjected to the Brinell hardness test, the indenter and indentation diameters…

Q: A copper-zine alloy has the properties shown in the table below. Grain Diameter (mm) Strength (MPa)…

A: (a).Hall-Petch equation-σy=σo+kd158=σo+k0.025158=σo+6.324k ........(1)145=σo+k0.050145=σo+4.47k…

Q: sample 1 20.93 M cal M water 3 , -19.2 27.3°C 34.4°C 202.19 84.49 12.1" Tcool Trinal M total Msample…

A: Solution For steady flow condition mwCw∆Tw=msCs∆Ts

Q: c. Find the homologous temperature (or the percent homologous) of Material A with a melting point of…

A: Given

Q: 200 stress (MPa) 150 100 50 0.1 0-2 strain From the tensile stress-strain behavior for the brass…

Q: 300 250 200 150 100 50 0.005 Select one: 420% 0.5% O 20% O 5% 35% Stress (Mpa)

A: highlighted points shows the ductile part of the material As per given dataThe %ductility is given…

Q: 3. A steel tape is calibrated at 20°C. On a cold day when the temperature is -15°C,what will be the…

Q: Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20). If we use a 4340:…

A: Solution:

Q: (u,)Japprox = 1000 Submit Previous Answers Request Answer X Incorrect; Try Again; 9 attempts…

Q: Q.3. A cylindrical specimen of cold-worked Brass has a tensile strength of 500 MPa. If the specimen…

A: Given:- Tensile strength =500 MPa Original radius, ro=10.6mm To find:- Radius after deformation, rd

Concept explainers

Engineering Drawing

Technical drawing has been around since ancient times. As in the ancient Renaissance, complicated drawings were created, including Leonardo da Vinci's drawing. Modern engineering drawing, including its specific orthographic projection with scale conventions, began in Europe (France) during the early stages of Industrialization. L.T. C. Rolt also made some of Marc's drawings for its block-making machinery (in 1799) that also may have contributed significantly to British engineering technology. Since he learned the art of presenting three-dimensional(3D) items in a two-dimensional(2D) plane, as we now term mechanical drawing. 

Question

b) A 1-cm-thick copper plate is cold-reduced to 0.50 cm and later further
reduced to
0.16 cm. Determine
I. The total percent cold work and
Il- Predict the properties of the metal at the calculated cold work?
0.16 cm
I cm
0.5 cm,
Figure-2

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Trending now

This is a popular solution!

Step by step

Solved in 4 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

We wish to produce an 0.3 inch plate of oxygen-free, high-conductivity (OFHC) copper that has a yield strength of at least 45 ksi and elongation of at least 10%. The original thickness of the plate is 3 inches. The width of the plate remains the same during processing. Which of the following procedures would give the correct final properties. More than one answer is possible. Group of answer choices Hot work from 3 to 0.5 inches; cold work from 0.5 to 0.3 inches Cold work from 3 to 1 inch; cold work from 1 to 0.5 inches; hot work from 0.5 to 0.3 inches Cold work from 3 to 1 inch; cold work from 1 to 0.4 inches; cold work from 0.4 to 0.3 inches Cold work from 3 to 1 inch; do full anneal; cold work from 1 to 0.5 inches; do full anneal; cold work from 0.5 to 0.3 inches Hot work from 3 to 0.4 inches; cold work from 0.4 to 0.3 inches None of the above will work Cold work from 3 to 0.3 inches Cold work from 3 to 1 inch; hot work from 1 to 0.4 inches; cold work from 0.4…
Stress (MPa) 500 400 Consider the brass alloy for which the stress-strain behavior is shown in the Animated Figure 7.12. A cylindrical specimen of this material 9.9mm (0.3898 in.) in diameter and 98.8mm (3.890 in.) long is pulled in tension with a force of 9780N(2199/b). If it is known that this alloy has a value for Poisson's ratio of 0.35, compute (a) the specimen elongation, (b) the reduction in specimen diameter. Note: because the diameter decreases, enter a minus sign in your answer. Tensile strength 450 MPa (65,000 psi), Strain =0 Stress = 0 MPA Stress =0 psi 70 Strain = 0 Stress 0 MPA 60 Stress = 0 psi 103 psi 50 40 MPa Yield strength 300 250 MPa (36,000 psi) 40 30 200 200 20 100 10 100 0 0 T 10 P 0.10 0.20 Strain 10.065 0 0.30 0.40 30 20 10 Stress (10 psi)
Excellent combinations of hardness, strength, and toughness are obtained from bainite. One heat treater austenitized a eutectoid steel at 750°C, quenched and held the steel at 250°C for 15 min, and finally permitted the steel to cool to room temperature. Did he produce the required bainitic structure? Use the diagram below in your answer 900 600 700 14 00 Y. 400 12 52 M. 00 57 M. 100 0.3 10 10 10 Answer: Time Temperature ("C) Rockwell Chardnens
Consider the tensile stress-strain diagram in the figure below labeled 1 and 2.
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Tensile stress-strain diagram 150 100 0.05 02 05 035 Strain 300 250 200 150 100 50 W Stress (Mpa)
Determine the young's modulus of metal alloy having the following tensile stress - strain diagram
What is heat flux in thermal stress?
None
Please solve and answer the question correctly please. Thank you!!
In cold working of metals, the elongated grain structure will give good properties in length direction. Select one: True False
Given a example of copper specimen that has had a tensile test conducted on it. Diameter of 6.4mm Max force of 11112.5N Max extension of 7.79mm Calculate: 1) modulus of elasticity 2) tensile strength 3) the ductility, in percent elongation 4) yield strength at a strain of 0.002
i need the answer quickly