A metal bar of 10 mm diameter when subjected to a pull of 23.5 kN gave an elongation of 0.3 mm on a gauge length of 200 mm. The Young's modulus of elasticity of the metal will nearly be

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 15ETSQ

See similar textbooks

Similar questions

Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
I5 In a tensile test experiment of carbon steel. a standard specimen (D= 0.505 in. Gauge length=2.0 in & total length 8 in) had a 0.2% offset yield strength of 80.000 psi and engineering strain of 0.010 at the yield strength point Calculate: The load (force) at this point. The instantaneous area of the specimen at this point. c. The true stress at this point. d. The true strain at this point. e. The total length of the specimen. if the load is released at this point.
The tension of a specimen of steel having an initial diameter of 0.507 in. was tested using a gauge length of 2 in. The following data were obtained for the elastic and plastic states. For the elastic state PAlb) 10 1000 2000 3000 4000 7000 8400 8800 9200 For the plastic state PAlb) 8800 9200 9100 13200 15200 17000 16400 14800 A/(in) 10 The reduction in the area Ris 0.0004 0.0006 0.0010 0.0013 0.0023 0.0028 0.0036 0.0089 NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part. % A, (in2) 0.1984 0.1978 0.1963 0.1924 0.1875 0.1563 0.1307 0.1077 What are the values of the yield strength, Sy and the reduction in the area? The value of the yield strength Sy is [ kpsl. 4
An aluminum rod is rigidly attached between a steel rod and a bronze rod as shown in Fig. P-108. Axial loads are applied at the positions indicated. Find the maximum value of P that will not exceed a stress in steel of 140 MPa, in aluminum of 90 MPa, or in bronze of 100 MPa. Figure P-108 PARTNER Aluminum A=400 mm² Steel A = 500 mm² 2.5 m 2.0 m Bronze A = 200 mm² 1.5 m 2P
The specimen shown is made from a 25 mm diameter cylindrical steel rod with two 38 mm outer-diameter sleeves bonded to the rod as shown. Knowing that E = 200 GPa, determine (a) the load P so that the total deformation is 0.05 mm, (b) the corresponding deformation of the central portion BC. 38 mm diameter P' 25 mm diameter B 38 mm diameter C 50 mm 75 mm 50 mm
Q.3. (30%) A circular aluminum tube subjected to T pure torsion by torques T has an outer radius r2 equal to 2 times the inner radius r1. (a) If the maximum shear strain in the tube is measured as 500x10-6 rad, what is the shear strain y1 at the inner surface? (b) If the maximum allowable rate of twist (0) is 0.15°/m and the maximum shear strain is to be kept at 500x10-6 rad by adjusting the torque T, what is the minimum required outer radius (r2 )min?
A circular tube of aluminum is subjected totorsion by torques T applied at the ends (see figure).The bar is 24 in. long, and the inside and outsidediameters are 1.25 in. and 1.75 in., respectively. It isdetermined by measurement that the angle of twistis 48 when the torque is 6200 lb-in.(a) Calculate the maximum shear stress t max in thetube, the shear modulus of elasticity G, and themaximum shear strain Υmax (in radians).(b) If the maximum shear strain in the tube islimited to 2.5 x10 -3 and the inside diameteris increased to 1.375 in., what is the maximumpermissible torque?
In a tensile test, a test piece of 25 mm diameter is tested over a gauge length of 125 mm The elongation over this length is 0.0875 mm under a pull of 68725 N. In a torsion test, a test piece was made of the same material and of same diameter, and it twisted 0.025 radians over a length of 250 mm at a torque of 0.3068 kN-m. Find Poisson's ratio and the three elastic modulis of the test piece material
3. An aluminum rod is rigidly attached between a steel rod and a bronze rod as shown in the figure. Axial loads are applied at the positions indicated. Find the maximum value of P that will not exceed a stress in steel of 140 MPa, in aluminum of 13.05 ksi, or in bronze of 100 MPа. Aluminum A = 400 mm? Bronze A = 200 mm Steel A = 500 mm? 2P 4D 2.5 m 2.0 m 1.5 m
Q.1 The yield stresses (oy) have been measured using steel and aluminum specimens of various grain sizes, as follows: Material D (µm) σΥ (MPa) Steel 60.5 160 136 128 Aluminum 11.1 235 100 223 (a) Determine the coefficients o and kỵ in the Hall- Petch for these two materials. (b) Determine the yield stress in each material for a grain size of d=26 um.
Strain = 600 Stress = Strain = 500 Stress = 400 500 300 400 300 200 200 100 100 0.000 0.002 0.004 0.006 Strain 0.00 0.04 0.08 0.12 0.16 0.20 Strain Stress (MPa)
On a steel bar specimen of 15 mm diameter and 150 mm gauge length, when tested as a tensile test specimen, a force of 15 kN produces an extension of 0.063 mm. When the specimen of same diameter and same length is tested under torsion, a twisting moment of 6.94 Nm produces an angular twist of 0.15⁰. Determine the Poisson's ratio of the material of the bar.