(a) Explain what is meant by term multi-directional composite laminate and using relevant sketches and/or equations explain why in-practice for many applications a multidirectional composite laminate is used, instead of a uni- directional (UD) composite laminate, despite the fact that UD laminate will have higher axial tensile strength and stiffness. (b) You have been provided, UD carbon fibre cloth and epoxy resin for making a part. Explain simple methods of mathematically estimating the axial stiffness (modulus) as well as transverse stiffness (modulus) of the resultant part made from these constituents. In both cases, clearly indicate the limitations of your method and what alternates can be adopted to get better approximations. (c) A power transmission shaft (torsional shaft) is to be produced using carbon fibre epoxy composites. There is a suggestion to use continuous carbon fibre (T300) and Epoxy (LY5052). What additional pieces of information must be specified at the minimum to complete his material description? Also briefly explain why each of that additional piece of information is required.

(a) Explain what is meant by term multi-directional composite laminate and using relevant sketches and/or equations explain why in-practice for many applications a multidirectional composite laminate is used, instead of a uni- directional (UD) composite laminate, despite the fact that UD laminate will have higher axial tensile strength and stiffness. (b) You have been provided, UD carbon fibre cloth and epoxy resin for making a part. Explain simple methods of mathematically estimating the axial stiffness (modulus) as well as transverse stiffness (modulus) of the resultant part made from these constituents. In both cases, clearly indicate the limitations of your method and what alternates can be adopted to get better approximations. (c) A power transmission shaft (torsional shaft) is to be produced using carbon fibre epoxy composites. There is a suggestion to use continuous carbon fibre (T300) and Epoxy (LY5052). What additional pieces of information must be specified at the minimum to complete his material description? Also briefly explain why each of that additional piece of information is required.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A continuous aligned fibre-reinforced composite is produced containing 28% aramid fibres of tensile strength 2.82GPA and the remainder of polycarbonate with tensile strength 60 MPa. What is the longitudinal strength of the composite in MPa? [Enter your answer as a real integer number - do not include the unit]
AT- shape section composed of two 12 mm by 36mm rectangles. What is the section modulus of the composite area in mm?? a. 11222 c. 9792 b. 9182 d. 5875
PLEASE ANSWER 2
Which one of the following reinforcing geometries offers the greatest potential for improving strength and stiffness in the resulting composite material? a) flakes. Ob) particles. O c) discontinuous fibers. O d) continuous fibers
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 45% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
What is the volume fraction of the reinforcement in a polymer matrix composite using epoxy and glass fiber if the volume fraction of glass fiber is 0.30?Ms. A wanted to make a polymer matrix composite using epoxy and glass fiber. The elastic moduli of epoxy and glass fiber are 3 and 70 GPa, respectively. If she wants to incorporate 0.30 volume fraction of glass fiber, determine the elastic modulus (GPa) of the composite in an iso-strain condition. What is the reinforcement in a cement?
The tensile curves on the right correspond to an A356 alloy1 (unreinforced) and to the same alloy reinforced with Al3Ti particles. Please, provide the following information for the reinforced composite: Young’s modulus in GPa. UTS (MPa) The approximate proof stress 0.2 (MPa) Ductility  (%) Toughness (MJ/m3) True stress (MPa) at the fracture point.
Please explain about modulus of elasticity of the composite versus fiber volume fraction.
Compare the desired properties of the matrix and the fiber phases of the fiberreinforced composite.