A direct extrusion process is used to reduce a cylindrical part that has a diameter of 5 inch and is 10 inch long to a cylinder with 2 inch diameter. The die angle is 90°. The cylinder material has a strength coefficient of 10 ksi and strain hardening exponent Of 0.15. Determine a. Extrusion strain b. Ram force

A direct extrusion process is used to reduce a cylindrical part that has a diameter of 5 inch and is 10 inch long to a cylinder with 2 inch diameter. The die angle is 90°. The cylinder material has a strength coefficient of 10 ksi and strain hardening exponent Of 0.15. Determine a. Extrusion strain b. Ram force

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: What are the elastic modulus (E) and the Poisson's ratio () used to indicate? 2. Illustrate the…

A: The elastic modulus (E) and Poisson's ratio are two important parameters used to describe the…

Q: As James orbits, he slams into a space elevator, peals himself off, and gets in. On the way down, he…

A: Write down the given values using suitable variables. Here L signifies leg length, m signifies leg…

Q: elasticity

A: Original Diameter D1= 0.505 in Hence Original Area A0= π4D12= π4×0.5052= 0.2003 m2 Final Diameter…

Q: Give an example of the Absolute Maximum Shear Strain?

Q: What is the force required to punch a 20-mm diameter hole in a plate that is 25 mm thick? Shear…

Q: a) Material A is the strongest material (T) / (F) b) Material B is the most rigid material (T) / (F)…

A: As per the guidelines, we are bound to solve only 3 sub parts questions. Please repost the other…

Q: An unknown specimen with an initial diameter of 5.25 mm experiences a reduction in diameter to 4.50…

A: Initial diameter of the specimen, di=5.25 mmFinal diameter of the specimen, df=4.50 mmTensile load,…

Q: Rank the curves based on the change in strain that occurs during the necking phase. Rank the curves…

A: Various stages shown on the stress-strain diagram are: Proportionality limit Plastic limit Necking…

Q: 1) Drawing: Consider a cylindrical rod fabricated from a linear strain hardening material with a…

A: Given:The constitutive relationship is .The original diameter of the rod is .For completely elastic…

Q: No wrong answer please , i could downvote The piece of suture is tested for its stress relaxation…

Q: A 20 foot long x 4 feet wide x ½ inch thick sheet of an aluminum alloy is cold rolled to a thickness…

A: Given data as per question The initial thickness of the sheet =0.5 in Final thickness =0.25 in The…

Q: Demonstrate that Equation 6.16, the expression defining true strain, may also be represented by ET =…

Q: A 20 foot long x 4 feet wide x ½ inch thick sheet of an aluminum alloy is cold rolled to a thickness…

A: Write the given data with suitable variables. Lo=20 ftbo=4 ftto=0.5 in=0.04 ft12 in 1 ftt=0.25…

Q: A compression test is performed on a 2” diameter by 5” long bar of an unknown metal. At the end of…

A: Given:d1=2 inl1=5 inl2=3.5 inK=250 MPan=0.4a)Volume before compression=volume after compression…

Q: 3) A tensile test is performed to determine the parameters strength constant C and strain- rate…

Q: What is the linear variation in the shear strain?

A: The change in shape obtained due to shear stress is defined by shear strain.

Q: A long, copper strip, 500 mm wide, 3 mm thick, was found to have 450 MPa yield stress. The strip is…

A: The width of the strip, b = 500 mmThe thickness of strip, t = 3 mmThe yield strength, σ = 450 MPaThe…

Q: What are the principal strains?

A: Principal Strain: Maximum and minimum normal strain possible for a specific point on a structural…

Concept explainers

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.

Question

3) A direct extrusion process is used to reduce a cylindrical part that has a diameter of 5 inch and is 10
inch long to a cylinder with 2 inch diameter. The die angle is 90°. The cylinder material has a
strength coefficient of 10 ksi and strain hardening exponent Of 0.15. Determine
a. Extrusion strain
b. Ram force

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step 3

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 3 steps with 3 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Question 4 Save Answer You do a series of tensile tests on plates of a magnesium alloy that have been subjected to prior cold rolling to true plastic strains of 0.1, 0.2 and 0.3. The resulting true stress-true strain curves are shown below (including a zoomed in version expanding on the small strain region). It is reasonable to approximate the the 0.2% offset yield strength of the magnesium as ✓ MPa for 0.2 and ✓ MPa for 0.3. Assuming the yield strength is ✓ MPa for 0.1 plastic strain, proportional to the square root of the prior true plastic strain results in a hardening coefficient of approximately k= MPa. Hence, we can predict that we need a prior plastic strain of approximately True Stress (MPa) True Stress (MPa) True Stress (MPa) 250 200 150 100 50 0 0.00 250 200 150 100 50 0 0.00 250 200 150 100 50 0 0.00 Ep = 0.1 0.01 Ep=0.2 0.01 Ep=0.3 0.01 0.02 True Strain 0.02 0.03 0.02 0.03 True Strain 0.03 0.04 0.04 0.04 True Stress (MPa) 0.05 0.000 0.001 True Stress (MPa) Ep=0.1 True…
In a slab rolling operation, the maximum thickness reduction (del hmax) is given by del hmax = μ²R, where R is the radius of the roll and u is the coefficient of friction between the roll and the sheet. If µ = 0.1, find the maximum angle subtended by the deformation zone at the centre of the roll.
10. A compound tube is formed by shrinking together two tubes with common radius 150 mm and thickness 25 mm. The shrinkage allowance is to be such that when an internal pressure of 30 MN/m² (300 bar) is applied the final maximum stress in each tube is to be the same. Determine the value of this stress. What must have been the difference in diameters of the tubes before shrinkage? E=210 GN/m².
...). A 450 mm-long sheet with a cross sectional area of 320 mm² is stretched with a force, F, until α = 22°. The material has a true-stress-true-strain curve o = 750 x 106 0.35 (a) Find the total work done, ignoring end effects and bending. (b) What is a max before necking begins? F 300 mm - 150 mm
what are t three components of shear strain?
What are the fundamental problems in Shear stress?
A cylindrical specimen of brass that has a diameter of 15 mm, a tensile modulus of 120 GPa, and a Poisson’s ratio of 0.30 is pulled in tension with force of 50,000 N. If the deformation is totally elastic, what is the approximate strain experienced by the specimen?