A cylindrical specimen of cold-worked steel has a Brinell hardness of 240. If the specimen remained cylindrical during deformation and its original radius was 10.4 mm, determine its radius after deformation. For steel, the dependence of tensile strength on percent cold work is shown in Animated Figure 7.19b. i mm

A cylindrical specimen of cold-worked steel has a Brinell hardness of 240. If the specimen remained cylindrical during deformation and its original radius was 10.4 mm, determine its radius after deformation. For steel, the dependence of tensile strength on percent cold work is shown in Animated Figure 7.19b. i mm

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 10000N tensile force is used to pull a cylindrical rod with an initial diameter of 2 cm. During the pull, the rod's diameter decreases to 1.8 cm. What is the true stress?I will rate accordingly...
A copper specimen subjected to the Brinell Hardness Test using hardened steel ball indenter of diameter 12 mm and the indentation diameter 3.87 mm is measured using an optical magnifying lens with a ruler. Draw the Brinell Hardness Test setup neatly and determine the force applied on the specimen. Take Brinell Hardness Number for copper as 807. Calculate: 1-Surface Area of Indentation (in mm2) 2-Applied Force (in N)
For the curve shown below, calculate the energy required to destroy the specimen. Use any method but your solution must include one integration step at least.
Part B The stress-strain diagram for a steel alloy having an original diameter of 1.0 in. and a gage length of 7 in. is shown in the figure below. (Eigure 1) Determine the load on the specimen that causes yielding. Express your answer to three significant figures and include appropriate units. HA Py- Value Units Submit Request Answer Part C Figure t oft> Determine the ultimate load the specimen will support. Express your answer to three significant figures and include appropriate units. NO 70 60 50 P. - Value Units 40 30 20 Submit Bequest Answer 10 (in/in) o G04 0m 12 016 020 024 02 a aa omams Provide Feedback
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.
Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 19 mm2 and the applied force as 12 kN.
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 60 % - Percentage of Reduction in Area = 36 % - Final length after fracture = 35.2 mm - Final Diameter after fracture = 3.54 mm & - Ultimate stress = 439 MPa i) Initial Length (in mm) = ii) Final Area (in mm2) = iii) Initial Area (in mm2) =
When a statically determinate structure is heated or cooled, its members do not experience any“thermal” stress. But for a statically indeterminate structure, this is not true. Explain why.
70% + | 8 0 4. An application requires ultimate tensile strength and yield strength of a steel at 110 ksi and 91 ksi, respectively. A data table is attached in the back of the test. Answer the following 4 questions: 4.1. Can SAE 1040 steel be selected for this application? 4.2. If "no" is the answer in Part I, the following Part II, III, and IV can be ignored. If "yes" is the answer in Part I, which condition of SAE 1040 should be selected? 4.3. Why is that steel with the condition in part II selected? 4.4. Is the selected steel brittle or ductile? and Why? Page 4 of 6
Answer the attach file
The diagram below shows a microscopic metal rod with a single crystal structure whose orientation is indicated by the inset. A force of F = 14.9 N is applied to the rod. The cross-sectional area is 1.1 mm². Calculate the shear stress along the close-packed direction. Dogo ooooo a. 4.65 MPa O b. 6.08 MPa c. 5.09 MPa O d. 4.04 MPa O e. 5.53 MPa
Question-8. . A cylindrical metal specimen with a diameter of 16 mm and length of 88 mm is to be subjected to a tensile stress of 80 MPa; at this stress the resulting deformation is elastic. (a) If the elongation is less than 0.058 mm, which of the metals in the table can be considered as candidates? Why ? (b) If the maximum permissible diameter decrease is 0.0012 mm when the tensile stress of 68 MPa is applied, which of the metals satisfy the criterion in question (a) are the suitable candidates? Why ? Metal Shear Modulus / GPa Modulus of Elasticity / GPa 69 Poisson's Ratio Al 25 0.33 Cu 110 46 0.34 Mg 45 17 0.29 Ni 207 76 0.31 Ti 107 6.5 0.34 W 407 23.2 0.28