A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compressive load of 150 kips. The modulus of elasticity for this specimen is 8,000 ksi and Poisson's ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region.

A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compressive load of 150 kips. The modulus of elasticity for this specimen is 8,000 ksi and Poisson's ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: A cylinder with a 150 mm diameter and 300 mm length is put under a com-pressive load of 665 kN. The…

A: σ=P/Awhere, P=applied load,A= areaand, E=σ/εσ=stressand ε= linear strain.

Q: 3.33 The following data are obtained from a tensile test of a 12.7-mm-diameter aluminum specimen…

A: As per the Guidelines of Bartleby We are supposed to answer only first three subparts. Ultimate…

Q: 5. A tensile test was done on a magnesium sample of original diameter and original length of 12mm…

A: To plot the stress v/s strain curve and to find the required parameters Note: as per the answering…

Q: A cylindrical metal specimen having an original diameter of 11.26 mm and gauge length of 53.3 mm is…

Q: A specimen is originally 300mm long and has a diemter of 11mm and it subjected to a force of 4kN.…

Q: Q1: A tensile test uses a circular test specimen that has a gage length of 50 mm and diameter = 20…

A: Given that, gage length = 50 mm diameter = 20 mm loat at 0.2% yield point = 100,000 N gage length…

Q: A stainless-steel rod 16mm in diameter and 300mm long is put under a tensile load of 250 kN.…

A: Given data Initial diameter of the rod(Di) = 16 mm Then Area (Ai) = (π/4)*Di2 = 201.062 mm2…

Q: Problem NO. 2. A student performed a tensile test in one of his samples, an aluminum specimen which…

Q: 1.5-7 The data shown in the table were obtained from a tensile test of a metal specimen with a…

Q: amplitude was 210 MPa. Compute the maximum and minimum stress. (Enter your answers to three…

Q: Determine the following: a. Young's modulus within the linear portion b. Tangent modulus at a stress…

A: a).Young's Modulus : At the proportional limit, stress is directly proportional to strain stress α…

Q: Copy the sketch of the tensile stress-strain test (Figure A1) results for a waisted metallic…

A: Objective: To indicate the given points on the stress-strain diagram and calculate the Young's…

Q: The following observations were made during a tensile test on a mild steel specimen 40 mm in…

A: Given data, Yield load =161 KN Maximum load = 242 KN Length of specimen at fracture = 249 mm…

Q: operation. First, circulate the kick out of the hole using original mud, then Circulate the kill…

A: Driller’s method is a two-step well kill operation. First, circulate the kick out of the hole using…

Q: 3. A new material is being developed and tested in the lab. The column was made using the new…

A: To find the elastic modulus and vicose coefficient

Q: Q.3 The following data were obtained from the tensile test of Aluminum alloy. The initial diameter…

A: Given data; Gauge length = 2 in Initial diameter = 0.505 in

Q: For a given elextic material, the Eastic Modulus E is 210 GPa and its Poission's Ratio is 0.27. What…

Question

A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compressive load of 150 kips. The modulus of elasticity for this
specimen is 8,000 ksi and Poisson's ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load
assuming that the material remains within the linear elastic region.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1: Given

VIEW

Step 2: Calculate final length of the specimen

VIEW

Step 3: Calculate final diameter of specimen

VIEW

Solution

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 4 steps with 8 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

The modulus of elasticity is measured as the secant for a stress at: a) 30% b) 45% c) 25% d) 40%
#3 solution?
A cylindrical metal specimen having an original diameter of 10.63 mm and gauge length of 50.1 mm is pulled in tension until fracture occurs. The diameter at the point of fracture is 7.60 mm, and the fractured gauge length is 74.5 mm. Calculate the ductility in terms of (a) percent reduction in area (percent RA), and (b) percent elongation (percent EL). (a) i percent RA (b) i percent EL
A compact tension specimen is tested according to ASTM standard E399. The load displacement curve is shown in the Figure below with PQ= 120 kN (Type 1 curve). The specimen dimensions are B=0.5 cm, W=10 cm, and “a” =5 cm. If the materials yield stress is 600 MPa are the conditions correct for a valid K1C measurement? Please look up McEviley’s textbook on the thickness criterion for a valid fracture toughness value.
Please answer d,e,f
A cylinder with a 150 mm diameter and 300 mm length is put under a compressive load of 665 kN. The modulus of elasticity for this specimen is 55 GPa and Poisson’s ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region.
2. A steel bar, whose cross section is 0.55 inch by 4.05 inches, was tested in tension. An axial load of P = 30,500 lb. produced a deformation of 0.105 inch over a gauge length of 2.05 inches and a decrease of 0.0075 inch in the 0.55-inch thickness of the bar. Determine the lateral strain. * Your answer Determine the axial strain. Your answer Determine the Poisson's ratio v. * Your answer Determine the decrease in the 4.05-in. cross-sectional dimension (in inches). * Your answer
A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compressive load of 150 kips. The modulus of elasticity for this specimen is 8,000 ksi and Poisson’s ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region.
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 74.0 ksi, e = 104.0 ksi , g = 85.0 ksi , and h = 0.15 in/in. Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.7 in . Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 11.0 kips, find the nominal stress experienced by the rod. Determine the force P needed to reach the ultimate stress in the steel-rod specimen.
650 600 550 500 450 400 350 300 250 200 150 100 50 0.002 0.004 0.006 0.008 0.01 0.012 0.014 0.016 0.018 0.02 Strain mm/mm The graph above shows the stress-strain relationship of a steel bar under tension test. The steel bar diameter = 8 mm and the bar gauge length = 100 mm. Determine the following: Toughness of the specimen Stress (MPa)
The solid circular drill rod AB is made of a steel that is assumed to be elastoplastic with τY = 22 ksi and G = 11.2 × 106 psi. Knowing that a torque T = 72 kip·in. is applied to the rod and then removed, determine the maximum residual shearing stress in the rod. The maximum residual shearing stress in the rod is ksi.
An aluminium specimen with an initial gauge diameter d, = 10 mm and gauge length, 1, = 100 mm is %3D subjected to tension test. A tensile force P= 50 kN is applied at the ends of the specimen as shown, resulting in an elongation of 1 mm in gauge length. The Poisson's ratio (µ) of the specimen is Take shear modulus of material, G = 25 GPa. Consider engineering stress-strain conditions. P