Need help understanding this one? 8.21 - Consider an alloy containing 70 wt % Ni and 30 wt % CU.1) At 1350°C, make a phase analysis assuming equilibrium conditions. In the phase analysis,include the following:a) What phases are present?b) What is the chemical composition of each phase?c) What amount of each phase is present?2) Make a similar phase analysis at 1500°C.3) Sketch the microstructure of the alloy at each of these temperatures by using circularmicroscopic fields.

1.At 1350 oC(a)The phases present are the liquid and solid (L + α). b) From the above phase diagram…

Answered: 8.21 - Consider an alloy containing 70…

Chemistry: The Molecular Science

5th Edition

ISBN:9781285199047

Author:John W. Moore, Conrad L. Stanitski

Publisher:John W. Moore, Conrad L. Stanitski

Chapter20: Chemistry Of Selected Transition Elements And Coordination Compounds

Section20.2: Iron And Steel: Pyrometallurgy

Problem 20.3E

See similar textbooks

Similar questions

A copper-nickel alloy of composition 45 wt% Ni - 55 wt% Cu is slowly heated from 1200 °C. What percentage of Ni is in the first liquid to form? Use the Cu-Ni equilibrium phase diagram shown below. 1500 Temperature (°C) 1455° 1400 Liquidus L 1300 1280° α + L Solidus 1200 1100 1085° 1240° α 1000 Cu 20 40 60 80 Ni Weight percent nickel
The assumptions about the virtual process state diagrams of metals A and B similar to the lead-tin system in Figure 9.8 are as follows. (1)The α phase and β phase exist at both ends of A and B. (2) The process composition is 36 wt% A to 64 wt% B. (3) The composition of β phase at the process temperature is 88 wt% A to 12 wt% B. Find the composition of an alloy in which the weight fraction of invitation β and total β is 0.367 and 0.768, respectively.
A copper-nickel alloy of composition 70 wt% Ni - 30 wt% Cu is slowly heated from 1250 °C. What is percentage of copper in the first liquid phase that forms? Use the Cu-Ni equilibrium phase diagram shown below. 1500 Temperature (°C) 1455° 1400 Liquidus L 1300 1280° α + L Solidus 1200 1100 1085° 1240° α 1000 Cu 20 40 60 80 Ni Weight percent nickel
The maximum solid solubility of carbon in ferrite occurs at 0.022 wt% C and 727 ° C, the eutectoid composition is 0.76 wt% C, the maximum solid solubility of carbon in austenite occurs at 2.14 wt% C and 1147 ° C, and the cementite composition is 6.7 wt% C. For 2122 g of a 3.2134 wt% C steel at 726 ° C, what will be the mass of carbon present as part of a compound?(a) 67.9 g(b) 74.2 g(c) 58.7 g(d) 83.5 g
Refer to the phase diagram below. A copper-nickel alloy of composition 70 wt% Ni-30 wt% Cu is slowly heated from a temperature of 1300°C. (a) At what temperature does the first liquid phase form? (b) What is the composition of this liquid phase? (c) At what temperature does complete melting of the alloy occur? (d) What is the composition of the last solid remaining prior to complete melting?
Av 24.
1. Which the alloying elements are stabilize austenite phase form Fe- Fe.C system.
In a system ABC, a ternary alloy with composition of 30 wt. % B and 30 wt. % C consists at a particular temperature of three phases of equilibrium compositions as follows: Liquid phase: 50 % A, 40 % B, 10 % C asolid solution: 85 % A, 10 % B, 5 % C B solid solution: 10 % A, 20 % B, 70 % C a. Plot the composition of the alloy. b. Calculate the proportion by weight of liquid, a and B present in this alloy. c. For the same temperature, find the composition of the alloy which will consist of equal proportion of a and ß phases of the compositions stated above, but with no liquid phase.
Topic: Equilibrium Phase Diagram QUESTION 1 A 50 wt% Pb-50 wt% Mg alloy is slowly cooled from 700C to 400C. (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? (c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase? Composition (at% Pb) 10 30 40 70 100 700 1200 600 a +L Ma Pb M 1000 500 800 400 Mg Pb 600 300 400 200 a + MgPb 100 MgPb 200 MgPb 20 40 60 100 (Mg) Composition (wt% Pb) (Pb) 1 (5) aungeedue
In a system ABC, a ternary alloy with composition of 30 wt. % B and 30 wt. % C consists at a particular temperature of three phases of equilibrium compositions as follows:Liquid phase: 50 % A, 40 % B, 10 % Calfa solid solution: 85 % A, 10 % B, 5 % Cbeta solid solution: 10 % A, 20 % B, 70 % Ca. Plot the composition of the alloy.b. Calculate the proportion by weight of liquid,  and  present in this alloy.c. For the same temperature, find the composition of the alloy which will consist of equal proportion of  and  phases of the compositions stated above, but with no liquid phase.
Consider the platinum-silver equilibrium phase diagram. Make phase analyses at the following points:a) The point at 42.4% Ag and 1400°C.b) The point at 42.4% Ag and 1186°C + ΔTIn the phase analyses, include:(i) The phases present(ii) The chemical compositions of the phases(iii) The amounts of each phase
Below are three different crystallographic planes for a unit cell of a hypothetical metal. The circles represent atoms: k0.4 nm>| k0.4 nm> (001) (100) (110) 1. Reconstruct a 3D units cell from the planes given indicating dimensions and atom/plane positions 2. To what prystał system does the unit cell belong? 3. What would the resulting Erystal structure be called? 4. What would the atomic packing factor be as a function of R kuu t'0> 0.55 nm 0.55 nm-

SEE MORE QUESTIONS

Recommended textbooks for you

Chemistry: The Molecular Science

Chemistry

ISBN:

9781285199047

Author:

John W. Moore, Conrad L. Stanitski

Publisher:

Cengage Learning

Principles of Modern Chemistry

Chemistry

ISBN:

9781305079113

Author:

David W. Oxtoby, H. Pat Gillis, Laurie J. Butler

Publisher:

Cengage Learning

Chemistry: The Molecular Science

Chemistry

ISBN:

9781285199047

Author:

John W. Moore, Conrad L. Stanitski

Publisher:

Cengage Learning

Principles of Modern Chemistry

Chemistry

ISBN:

9781305079113

Author:

David W. Oxtoby, H. Pat Gillis, Laurie J. Butler

Publisher:

Cengage Learning

SEE MORE TEXTBOOKS