Answered: 4- A structural alloy has a rupture…

4- A structural alloy has a rupture strength of 238N/mm?. Cold deformation amount is 34% after rupture. Find the true rupture strength of this alloy.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter11: Fracture And Fatigue

Section: Chapter Questions

Problem 11.14P

See similar textbooks

Related questions

Q: a. Which of the following gives the approximate modulus elasticity of the The stress-strain diagram…

A: Solution;

Q: Which of these cast iron would allow the greatest amount of plastic deformation before fracture .…

A: Nodular cast iron has highest tensile strength of about 70ksi followed by grey cast iron with 50ksi…

Q: Two previously undeformed cylindrical specimens of an alloy are to be strain hardened by reducing…

Q: A setup for single-edge-notch-bending (SENB) tests is shown below. Support rollers provide…

A: Given Data: Thickness of the specimen is t=10 mm. Height of the specimen is W=10 mm. Modulus of…

Q: A cylindrical specimen of cold-worked steel has a Brinell hardness of 240. If the specimen remained…

Q: A. Which material is considered as ductile and which one is considered as brittle? Explain. What is…

A: Part A) Material A has a typical ultimate stress point and breaking stress point, along with a clear…

Q: A single crystal of BCC iron is subjected to tensile stress of 100 MPa along the [001] direction.…

Q: A) A specimen of alloy having the following engineering stresses produces the corresponding plastic…

A: Given :- To find :- Engineering stress corresponding to engineering strain of 0.4

Q: For a bronze alloy, the stress at which plastic deformation begins is 275 MPa (40,000 psi), and the…

Q: A laminated [0/90/0/90]s graphite/epoxy beam is 1 mm thick, is 20 mm wide, and has 0.125 mm thick…

A: Given;t = 1 mm = 10-3 mw = 20 mm = 20d' = 0.125 mm =0.125E1 = 180 GpaE2 = 10 Gpaν12 = 0.28 G12 = 7…

Q: The assembly shown consists of an aluminum shell (E, = 70 GPa, aą = 23.6 × 106PC) fully bonded to a…

A: We will use equillibrium and Axial deformation equation.

Q: Q7> Ductile-to-brittle transition temperature (DBTT) is a very important parameter in the design of…

A: a) Introduction : The ductile-to-brittle transition temperature (DBTT) is a well-known phenomena in…

Q: Given your understanding of what initiates and controls failure in materials, which of the following…

A: Designing materials, elements, or structures that can endure periodic or static load requirements is…

Q: Mechanical Properties-Metals For a bronze alloy, the stress at which plastic deformation begins is…

Q: After an inspection it is found that a structural ceramic part has no flaws greater than 100…

A: calculate the maximum service stress (in MPa)

Concept explainers

Alloys

An alloy is an admixture of two or more metals or a metal and a non-metal. Since ancient times, man has been using alloys. Alloying helps to retain the properties of the parent matter, such as hardness, strength, toughness, ductility and is corrosion-resistant. Copper alloys such as brass have antimicrobial properties that help to fight against (Coronavirus disease 2019) COVID-19 and other hospital-acquired infections. Some common alloys are brass, bronze, solder steel, etc. Most alloys have a lower melting point than their constituents. This is due to the presence of a nonmetal as one of the constituents that behaves as an impurity and restricts the raise of melting point.

Question

4- A structural alloy has a rupture strength of 238N/mm?. Cold deformation amount is 34% after
rupture. Find the true rupture strength of this alloy.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

cold working process

VIEW

true rupture strength calculation

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Given your understanding of what initiates and controls failure in materials, which of the following will increase the failure strength or lifetime of a test piece or component and why? a. Decreasing the difference between the maximum and minimum stress values, as this effects the stress concentration factor b. Decreasing the temperature below the brittle-ductile transition temperature, to make it harder C. Polishing to reduce surface defects Od. Increasing its volume, to give a larger cross sectional area Oe. Increasing the grain size so there are less grain boundaries to initiate failure
For a bronze alloy, the stress at which plastic deformation begins is 275 MPa (40,000 psi), and the modulus of elasticity is 115 GPa (16.7 x106 psi). (a) What is the maximum load that may be applied to a specimen with a cross-sectional area of 325 mm2 (0.5 in.2) without plastic de- formation? (15pts)(b) If the original specimen length is 115 mm (4.5 in.), what is the maximum length to which it may be stretched without causing plastic deformation?(15pts)
(Solid Mechanics) A setup for single-edge-notch-bending (SENB) tests is shown below. Support rollers provide frictionless contact with the specimen, while a load is applied at the middle of the top surface of specimen. The thickness of the specimen is 10 mm and the height W 10mm. The properties for this ductile alloy are E = 70 GPa, v=0.3, σᵧ = 400 MPa, Kᵢ? = 25 MPa.m¹/². (1) Ignore any crack or defects in the material, what is the maximum static force that the specimen could carry before failure? (2) A cyclic load of low amplitude 2.8 kN is applied. Because of the cyclic load a defect is nucleated on the edge and grows into a fatigue crack of 2 mm length shown in the right. If the cycling is interrupted, what is the maximum static tensile force that the specimen could carry? (3) With more cycles, the fatigue crack keeps growing. Estimate the critical crack length (a range is fine) at which the plate will fail from the low-amplitude cyclic load 2.8 kN only. (maximum two iterations are…
I need the answer as soon as possible
The assembly shown consists of an aluminum shell (E,= 70 GPa, a, = 23.6 × 10-6rC) fully bonded to a steel core (Es = 200 GPa, as = 11.7 x 10-6rC) and the assembly is unstressed at a temperature of 20°C. Considering only axial deformations, determine the stress in the aluminum when the temperature reaches 215°C. 200 mm 20 mm Aluminum shell Steel 50 mm core The stress in the aluminum is MPa.
A cylindrical specimen of cold-worked steel has a Brinell hardness of 240. If the specimen remained cylindrical during deformation and its original radius was 11.8 mm, determine its radius after deformation. For steel, the dependence of tensile strength on percent cold work is shown in Animated Figure 7.19b. i mm
Q7> Ductile-to-brittle transition temperature (DBTT) is a very important parameter in the design of metallic materials for engineering applications. It has been well known that most of BCC and HCP metals show the DBT phenomenon; however, there is no DBTT in FCC metals. (a) Explain the reason in terms of deformation and fracture. You must compare the BCC and FCC. (b) The ductile fracture surface consists of many dimples. Explain their formation mechanism from the concept of point defects. (c) There are two types in the brittle fracture. Explain and Compare them.
A laminated [0/90/0/90]s graphite/epoxy beam is 1 mm thick, is 20 mm wide, and has 0.125 mm thick plies. The lamina properties are E1 = 180 GPa, E2 = 10 GPa, ν12 = 0.28, G12 = 7 GPa Xt = 1700 MPa, Xc = 1400 MPa, Yt = 40 MPa, Yc = 230 MPa (a) Determine the flexural modulus of the beam (b) How could the flexural modulus be improved without changing the ply materials, the number of plies, or the ply orientations? (c) Using the Maximum Stress Criterion for each ply, determine the magnitude of the maximum allowable bending moment that the beam can withstand. Which ply fails first?
After an inspection it is found that a structural ceramic part has no flaws greater than 100 micrometers in size, calculate the maximum service stress (in MPa) available with SiC. Assume that Y= 1
2- What is the largest size (mm) internal through crack that a thick plate of aluminium alloy 7075-T651 can support at an applied stress of (a) three-quarters of the yield strength and (b) one-half of the yield strength? Assume Y = 1. for 7075-T651, KỊC = 24.2 MPa ym and oYS = 495 MPa.
A 7075-T651 alloy is used in a structural component in an airplane. The component must not fail when subjected to a stress of 250 MPa. Several surface flaws have been detected on the component. What is the largest (deepest) surface flaw that could be permitted with the 250 MPa maximum stress? Use data from Table 1 and assume this component geometry and loading condition result in a Y value of 1.25. Yield Strength KI Material MPa ksi MPa√m ksiVin. Metals Aluminum alloy (7075-T651) 495 72 24 22
A steel specimen is tested in tension. The specimen is 50 mm wide by 25 mm thick in the test region.The specimen yields at a load of 160 kN and fractures at 215 kN. Determine the tensile stress at fracture.