Big and clear handwriting with all the steps please . Make sure calculations and answers are accurate please. THANK YOU 2-1 Figure P2-1 shows stress-strain curves for three failed tensile-test specimens. All areplotted on the same scale.Characterize each material as brittle or ductile.Which is the stiffest?Which has the highest ultimate strength?Which has the largest modulus of resilience?Which has the largest modulus of toughness?(d)(e) |1006007075-T6802024-T35140060406 2001100200.050.100.150.20ɛ, StrainFIGURE 2-21ơ, Stress, MPao, ksi

To study the graph and answer the following questions.

2-1 Figure P2-1 shows stress-strain curves for three failed tensile-test specimens. All are plotted on the same scale. (a) Characterize each material as brittle or ductile. (b) Which is the stiffest? Which has the highest ultimate strength? Which has the largest modulus of resilience? Which has the largest modulus of toughness?

2-1 Figure P2-1 shows stress-strain curves for three failed tensile-test specimens. All are plotted on the same scale. (a) Characterize each material as brittle or ductile. (b) Which is the stiffest? Which has the highest ultimate strength? Which has the largest modulus of resilience? Which has the largest modulus of toughness?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

I just can't find The percent elongation at fracture.
The following stress-strain curve was prepared based on a tensile test of a specimen that had a circular cross-section. The gage diameter of the specimen was 0.25 inches and the gage length was 4 inches. The stress scale of the stress-strain diagram is given with the factor a = 10 ksi. Estimate: (a) The modulus of elasticity. (b) The ultimate strength. (c) The yield strength (0.2% offset). (d) The percent elongation at fracture. 2013 Michael Swanbom STRESS VS. STRAIN BY NC SA 7a bat Sat 2at at 0.05 STRAIN 0.01 0.04 0.06 0.08 0.02 0.03 0.07 0.09 STRESS
Draw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking region
200 stress 150 (MPa) 100 50 0.1 0-2 strain From the tensile stress-strain behavior for the brass specimen the diameter is 12-8 mm Calcalate the folluwing:- %3B 1- The Yield stress. 2-Modulus of elasticity. 3 - The Tensile strength.
Sketch a representative stress-strain digrama for a ductile material showing the following on it (label the axis and provid units). 1- YIELD STRENGTH. 2- TENSILE STRENGTH. 3- FRACTURE POINT. 4- HARDENING PART. 5- SOFTENING PART. 6- A METHOD TO CALCULATE THE STIFFNESS. 7- A METHOD TO CALCULATE THE DUCTILITY.
Example: Convert the change in length data in Table 3-2 to engineering stress and strain and plot a stress-strain curve Homework- help Table 3-2 The results of a tensile test of a 0.505 in. diameter aluminum alloy test bar, initial length (1o) = 2 in. Calculated LTO Load (Ib) Change in Length (in.) Stress (psi) Strain (in./in.) 0.000 1000 0.001 0.0005 4,993 14,978 24,963 34,948 37,445 39,442 39,941 39,691 37,944 3000 0.003 0.0015 5000 0.005 0.0025 7000 0.007 0.0035 7500 0.030 0.0150 7900 0.080 0.0400 8000 (maximum load) 0.120 0.0600 7950 0.160 0.0800 7600 (fracture) 0.205 0.1025
Qustions 1,2,3
The following data (in given figure) were obtained from the tensile test of Aluminum alloy. The initial diameter of test specimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
Part A The stress-strain diagram for a steel alloy having an original diameter of 0.40 in. and a gage length of 9 in. is shown in the figure below. (Figure 1) Determine the modulus of elasticity for the material. Express your answer to three significant figures and include appropriate units. HA ? Eapprox = Value Units Submit Request Answer Figure < 1 of 1 Part B a (ksi) 80 Determine the load on the specimen that causes yielding. 70 Express your answer to three significant figures and include appropriate units. 60 50 40 HA 30 20 Py = Value Units 10 € (in./in.) 0.04 0,08 0.12 0,16 0,20 0,24 0,28 O 0.0005 0.001 0.0015 0.002 0.0025 0.0030.0035 Request Answer Submit
Consider the tensile stress-strain diagram below. If samples 1 and 2 are identical except that they were tested at different temperatures, which sample was tested at a lower temperature? Note: This question will be marked negatively so consider your answer carefully. A. Sample 1 B. Both were tested at the same temperature/ Alby is by die dieselfde temperatuur getoets C. Sample 2
In stress and strain diagram for a perfectly ductile material, the yield strength, and ultimate tensile strength are well defined Select one: O True O False
I need the answer as soon as possible