1. A cylindrical specimen of a metal object with a radius of 3.8E-2 m and a gaugelength of 20.31 mm is pulled in tension. Use the load-elongation characteristicstabulated below to answer the following questions;Load Length(N)(mm)20.3120.381220.451820.512420.553020.613620.6442.820.6848.920.7255.220.766020.7965.820.8470.720.8777.320.9383.1 20.9888.622.1591.5823.2491.68 25.4106ChangeinlengthLength (x10-2 m) (m)Computed strain Computed stress (N/m²)(a) Compute the cross-sectional area of brass.(3

Answered: Image /qna-images/answer/5ba2fbd8-73fd-427f-a42e-72a17c9a9e59.jpg

1. A cylindrical specimen of a metal object with a radius of 3.8E-2 m and a gauge length of 20.31 mm is pulled in tension. Use the load-elongation characteristics tabulated below to answer the following questions; Load Length (N) (mm) 0 20.31 6 20.38 12 20.45 18 20.51 24 20.55 30 20.61 36 20.64 42.8 20.68 48.9 20.72 55.2 20.76 60 20.79 65.8 20.84 70.7 20.87 77.3 20.93 83.1 20.98 88.6 22.15 91.58 23.24 91.68 25.41 Change in length Length (x10-2 m) (m) Computed strain Computed stress (N/m²) (a) Compute the cross-sectional area of brass.

1. A cylindrical specimen of a metal object with a radius of 3.8E-2 m and a gauge length of 20.31 mm is pulled in tension. Use the load-elongation characteristics tabulated below to answer the following questions; Load Length (N) (mm) 0 20.31 6 20.38 12 20.45 18 20.51 24 20.55 30 20.61 36 20.64 42.8 20.68 48.9 20.72 55.2 20.76 60 20.79 65.8 20.84 70.7 20.87 77.3 20.93 83.1 20.98 88.6 22.15 91.58 23.24 91.68 25.41 Change in length Length (x10-2 m) (m) Computed strain Computed stress (N/m²) (a) Compute the cross-sectional area of brass.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A specimen of magnesium having a rectan- gular cross section of dimensions 3.2 mm × 19.1 mm (in. × in.) is deformed in ten- sion. Using the load-elongation data tabulated as follows, complete parts (a) through (f). lbf 0 310 625 1265 1670 1830 2220 2890 3170 3225 3110 2810 Load N 0 1380 2780 5630 7430 8140 9870 12,850 14,100 14,340 13,830 12,500 in. 2.500 2.501 2.502 2.505 2.508 2.510 2.525 2.575 2.625 2.675 2.725 2.775 Fracture Length mm 63.50 63.53 63.56 63.62 63.70 63.75 64.14 65.41 66.68 67.95 69.22 70.49 (a) Plot the data as engineering stress versus engineering strain. (b) Compute the modulus of elasticity. (c) Determine the yield strength at a strain offset of 0.002. (d) Determine the tensile strength of this alloy. (e) Compute the modulus of resilience. (f) What is the ductility, in percent elongation?
Semiconductor strain gauges find their primary application in the construction of transducers, such as load cells and pressure transducers. Why do measuring instruments manufacturers usually use semiconductor strain gauges even though they are significantly more expensive than metallic strain gauges? Name two pros and two cons of these strain gauges compared to metallic strain gauges. Paragraph B A Lato (Recom... 19px... v T + v
This steel alloy specimen had an original diameter of 12.8 mm and a gauge length of 50.80 mm: i) If it were subjected to a load of 120 kN and then released, what would have been its permanent elongation? Be thorough. ii) If it were subjected to a load of 230 kN and then released, what would have been its permanent elongation? Be thorough.
In a tensile test for an aluminum alloy, the sample used is 2 inches long and 0.5 inches in diameter. The proportional portion of the tension stress-strain diagram for an aluminum alloy is shown below. _x106 lb/in² Pay attention to units and calculate your answer to 1 decimal place for the unit specified above. σ (ksi) 70 t 0.00614 Determine the modulus of elasticity for this material: € (in./in.)
A tension test was performed on a specimen having an original diameter of 13.7 mm and a gauge length of 50 mm. The data are listed in the table. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Redraw the linear-elastic region, using the same stress scale but a strain scale of 20 mm = 0.001 mm/mm. From the diagram, determine approximately the modulus of elasticity. Express your answer to three significant figures and include the appropriate units. E = Submit Part B συ = Submit Part C ☐☐ μÅ of = Value Determine the ultimate stress. Express your answer to three significant figures and include the appropriate units. Request Answer μĂ Value Request Answer Units μĂ - Value Units Determine the fracture stress. Express your answer to three significant figures and include the appropriate units. ? Units ? ?
The stress-strain diagram for a steel alloy having an original diameter of 0.3 in. and a gage length of 5 in. is shown in the figure below. (Figure 1) Figure σ (ksi) 80 70 60 50 40 30 20 10 0 0 0.04 0.08 0.12 0.16 0.20 0.24 0.28 0 0.0005 0.001 0.0015 0.002 0.0025 0.0030.0035 e (in./in.) < 1 of 1 ▼ Part A Determine the modulus of resilience. Express your answer to three significant figures. (ur)approx= Submit Part B (14)approx= Determine the modulus of toughness. Express your answer to three significant figures. Submit ■ AΣ¢ † vec Provide Feedback Request Answer |VL]ΑΣΦΠ = Ivec Request Answer [C] ? MIC ? in-lb in³ in-kip in³