Question

The fraction of lattice points occupied by vacancies in solid aluminium at 660℃ is 10^-3 .What is the energy required to create vacancies in aluminium?

Expert Solution

Trending now

This is a popular solution!

Step by step

Solved in 3 steps

SEE SOLUTION Check out a sample Q&A here

Blurred answer

Similar questions

If the atomic radius of a metal that has the face-centered cubic crystal structure is 0.2718 nm, calculate the volume of its unit cell in nm³.
At 23° K, the crystal structure transforms from BCC to HCP keeping density same. The 0 cubic face in BCC is a = 3.42 A and in HCP is == 1.53. The lattice constant in HCP a structure is, 0 (a) 2.64 A 0 (b) 3.16 A 0 (c) 2.16 A 0 (d) 2.42 A
Grüneisen parameter for silicon The silicon crystal (diamond structure) has the following properties at 500 K. The lattice parameter (a) = 0.5440 nm, thermal expansion coefficient (a) = 3.6x106 K-', and the bulk modulus is about the same as that at room temperature (K = 99 GPa). The Debye temperature of Si is 625 K. At room temperature (300 K) its density is 2.33 g cm³, and its lattice constant is 0.5430 nm. Calculate the Grüneisen parameter at 500 K and compare with its value at room temperature in Table 1. Is 3 constant?
A sample of copper has a mass of 10.68 g when measured in air. It has a mass of 9.47 g when measured in water. Answer these four questions: What is the density of the sample? How many atoms are in the sample? What is the simple volume of the space including and surrounding each atom? Assume the atoms are evenly distributed throughout the sample. That is no FCC, BCC, or HCP crystal structure. What is the diameter of each atom?