Problem No. 2The above load-elongation data were obtained for a specimen with Lo = 0.1 m andro 7 mm. Plot the stress-strain data and determine the E, G, and ofLoad(KN)0.012.836.743.547.050.161.471.674.271.667.6Elongation(mm)00.02010.06900.11730.18980.28641.16843.50527.302510.223513.7287

Given:Original length of the specimen, Lo=0.1 m=100 mmOriginal radius of the specimen, ro=7…

Answered: The above load-elongation data were…

The above load-elongation data were obtained for a specimen with Lo = 0.1 m and To 7 mm. Plot the stress-strain data and determine the E, G, and of

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The principal plane stresses and associated strains in a 35 ksi, 02 = 15 ksi, plane at a point are 01 1 €1 = 1.02(10-3), 2 = 0.180(10-³). ▼ Determine the modulus of elasticity. Express your answer using three significant figures and include the appropriate units. E= Submit Part B V= μA Value Request Answer Submit Determine the Poisson's ratio. Express your answer using three significant figures. ΠΑΠΙ ΑΣΦ | Η VE Units Request Answer ? vec POSSIA space ?
Sketch two more stress-strain diagrams, again one for a ductile material and one for a brittle material. Draw the stress-strain diagrams so that the modulus of toughness for the brittle material is greater than the modulus of toughness for the ductile material.
Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…
1 J A cylindrical specimen of steel having a diameter of 14.36 mm and length of 209 mm is deformed elastically in tension with a force of 58.9 kN. Suppose that the Poisson's ratio (v) is 0.3, determine The change in diameter of the specimen? (E of steel = 207 GPa)
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 35.5 mm - Final Diameter after fracture = 3.6 mm & - Ultimate stress = 396 MPa SOLUTION: iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
The yield stress for mild steel is 207MP.. A specimen with diameter of 0.01lm and length of 0.1m is subjected to a load of weight of 10kg, and the resulting elongation is 6.077 microns. Determine whether the stress is above or below the yield stress, and if it is below, compute the Young's modulus of the material.
Use the engineering stress strain diagram provided below to answer parts (A) to (H) below (the stress-strain diagram bas already been drawn for you): stress strain diagram 400 350 0 300 0 250 0 200 0 150.0 100.0 50.0 O 05 0 1 0.15 strain A. Determine the tensile strength of this alloy. B. show the elastic, plastic and total strain on the diagram stress (Mpa)
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
100 mm must elongate only 5 mm when a tensle load of 100,000 N is applied. Under these A cylindrical specimen of a brass alloy having a circumstances what must be the radius of the specimen? Consider this brass alloy to have the stress-strain behavior shown in Figure below. Tensile strengh 450 MPa (65,000 p A00 10 pu 300 200- 30 Yield strength 250 MPa (36,000 psi 2아 100 1아 100 0.005 0.20 0.30 0.40
A cylindrical specimen of a metal alloy 8 mm in diameter is stressed elastically in tension. A force of 15700 N produces a reduction in specimen diameter of 5*10^-3 mm. Compute Poisson ratio for this material if its elastic modulus is 140 GPa.
True stress-strain Engineering stress-strain strain Calculate the engineering ultimate tensile strength of a material whose strength coefficient is 535 MPa and of a tensile-test specimen that necks at a true strain of 0.55. 200 MPa O 267 MPa O 244 MPa O 222 MPa stress
A solid bar of length L = 4 m and diameter 200 mm is heated from 20 to 320 degrees celsius and restrained between two solid immovable walls. Young's modulus of the material is 90 GPa and the coefficient of thermal expansion is 22 x 10-6/°C. →Calculate the thermal strain, e, in micro-strain correct to two decimal places. micro-strain. Calculate the thermal stress, o, in megapascals (MPa) correct to two decimal places. E: σ: MPa. Hence calculate the force exerted by the bar in meganewtons (MN) correct to two decimal places: F MN. L