(Q.3) For 30 wt% Cu-70 wt% Ag alloy at 650 "C, (a) what phases are present? (b) What are the compositions of the phases? (c) Calculate the relative mass fraction of each phase present. 500 400 10 30 40 50 60 70 BO 961.93 90 ART A

(Q.3) For 30 wt% Cu-70 wt% Ag alloy at 650 "C, (a) what phases are present? (b) What are the compositions of the phases? (c) Calculate the relative mass fraction of each phase present. 500 400 10 30 40 50 60 70 BO 961.93 90 ART A

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: b) Figure 2 is the tin-gold phase diagram, for which only single-phase regions are labeled. Write…

A: (1) In this given Tin-gold phase diagram, there are two eutectic points.

Q: For an alloy containing 40% p Sn - 60% p Pb at a temperature of 150°C: (a) Which phases are gifts?…

Q: (d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C. (e) A Mg-Pb alloy of mass…

A: Given Data: To Find: (d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A…

Q: (Q.3) For 30 wt% Cu-70 wt% Ag alloy at 650 "C, (a) what phases are present? (b) What are the…

Q: For the phase diagram of magnesium oxide with aluminum oxide, Calculate a) all the transformations…

A: The transformations, temperature at which they occur, and the name of reaction all are discussed in…

Q: Choose fhe correct anguer ? 7) The term allotropy is normally reserved for this behavior in pure…

A: 7. 1) elements Allotropy is the existence of two or more different physical forms of a chemical…

Q: Why is alloying done? Using a Pb-Sn or Cu-Zn phase diagram, explain how you c achieve a 30% wt of…

A: Metals (or a metal plus a nonmetallic element) are heated until they are molten to make an alloy.…

Q: b) sketch corresponding heat treatment profile with To, T1, T2 shown c) and corresponding…

Q: Figure below is a binary eutectic copper-silver phase diagram. Consider if 500 grams of an 88 wt%…

Q: 2. Shown below is the binary lead-tin phase diagram from your textbook. Answer the questions below.…

A: a. Proeutectic composition is calculated at the temperature just above eutectic line of 183°C As the…

Q: TC C) 1600 3 2 1 1400 5 1148 1200아 7 100아 10 800 727 600 11

A: To determine the compositions at the marked position in the Iron-iron carbide diagram.

Q: Can anyone help with this question

A: The mass of alloy, m = 100 gmThe composition of the alloy = 80 wt%Sn and 20 wt% PbThe temperature…

Q: If our alloy has a composition of 10% i and has a temperature of 1100C, determim Si. a) What…

Q: Draw the iron-Fe3C phase diagram. Consider 0.4 and 1.1 wt% C steel alloy. It is cooled slowly from a…

A: As per our guidelines, only the first three subparts will be answered, Kindly ask other parts in…

Q: 3. For the regions and points on the Fe-C phase diagram given bellow, write the corresponding phases…

A: The reaction and corresponding composition phases are written from diagram as,

Q: BI (a) Figure BI below shows the equilibrium phase diagram of hypothetical A - B alloy system.…

A: (i) Draw the given equilibrium phase diagram.

Q: a) Indicate hypooeutenic, hypereutenic ranges and eutenic composition in wt%Sn. Use the phase…

A: a) Micro structure of alloy is given as,

Q: At what temperature does the first liquid phase form at 90% Ni? T(°C) 1600 1500 1400 1300 1200 1100…

Q: 13) If you have an alloy with a composition of 22 wt% Ag at a temperature of 779.1° C, identify: a)…

Q: 100 (iv) Given that the average density of a phase is determined as Pa = calculate the PA PB volume…

Q: Use the Lead-Tin (Pb-Sn) phase diagram below to answer the following questions: Place the following…

A: Given:

Question

(Q.3) For 30 wt% Cu-70 wt% Ag alloy at 650 "C, (a) what phases are present? (b) What are
the compositions of the phases? (c) Calculate the relative mass fraction of each phase present.
500
400
10
20
30
40
NO
Silver,
70
po
GD
91.2
(ART
As

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Phase Diagrams and Its Applications in Metallurgy

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Hi i keep getting these wrong
According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Material science Assuming this system forms a laminar type eutectic, determine the volume proportion of phases for an equilibrium solidified 50% Pb alloy. Sketch the expected microstructure.
Consider the phase diagram below. The three points A, B, and C are at concentrations of 27, 31.9, and 33.8 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300-L (liquid) 1200 20 ABC L + a C1 30 S C2 liquidus 40 L + a solidus α (solid). O a. Walpha=0.12; WL=0.41; Walpha/WL = 9.41 O b. Walpha=0.27; WL-0.26; Walpha/WL = 11.11 O c. Walpha=0.15; WL-0.26; Walpha/WL = 11.80 Od. Walpha=0.20; WL-0.31; Walpha/WL = 7.33 50 wt% Ni