Q.2 ( Calculate the equilibrium number of vacancies per cubic meter for copper at 160 and 927 C. The energy for vacancy formation is 0.9 eV/atom; the atomic weight and density for copper are 63.5 g/mol and 8.4 g/cm³, respectively. anification 300X. What is the

Elements Of Electromagnetics
7th Edition
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Sadiku, Matthew N. O.
ChapterMA: Math Assessment
Section: Chapter Questions
Problem 1.1MA
icon
Related questions
Question
Q 2 please
Q.2(
Calculate the equilibrium number of vacancies per cubic meter for copper at 160 and 927 C. The energy for
vacancy formation is 0.9 eV/atom; the atomic weight and density for copper are 63.5 g/mol and 8.4 g/cm³,
respectively.
Q.3 (
Suppose we count 18 grains per square inch in a photomicrograph taken at magnification 300x. What is the
ASTM grain size number (n)?
Q.4(
A sheet of BCC iron (Fe purity is 99.988 wt% ) 1 mm thick was exposed to a carburizing gas atmosphere on
one side and a decarburizing atmosphere on the other side at 725°C. After having reached steady state, the
iron was quickly cooled to room temperature. The carbon concentrations at the two surfaces of the sheet
were determined to be 0.015 and 0.0065 wt%.
Transcribed Image Text:Q.2( Calculate the equilibrium number of vacancies per cubic meter for copper at 160 and 927 C. The energy for vacancy formation is 0.9 eV/atom; the atomic weight and density for copper are 63.5 g/mol and 8.4 g/cm³, respectively. Q.3 ( Suppose we count 18 grains per square inch in a photomicrograph taken at magnification 300x. What is the ASTM grain size number (n)? Q.4( A sheet of BCC iron (Fe purity is 99.988 wt% ) 1 mm thick was exposed to a carburizing gas atmosphere on one side and a decarburizing atmosphere on the other side at 725°C. After having reached steady state, the iron was quickly cooled to room temperature. The carbon concentrations at the two surfaces of the sheet were determined to be 0.015 and 0.0065 wt%.
Expert Solution
steps

Step by step

Solved in 4 steps

Blurred answer
Knowledge Booster
Ceramics
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.
Similar questions
  • SEE MORE QUESTIONS
Recommended textbooks for you
Elements Of Electromagnetics
Elements Of Electromagnetics
Mechanical Engineering
ISBN:
9780190698614
Author:
Sadiku, Matthew N. O.
Publisher:
Oxford University Press
Mechanics of Materials (10th Edition)
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:
9780134319650
Author:
Russell C. Hibbeler
Publisher:
PEARSON
Thermodynamics: An Engineering Approach
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:
9781259822674
Author:
Yunus A. Cengel Dr., Michael A. Boles
Publisher:
McGraw-Hill Education
Control Systems Engineering
Control Systems Engineering
Mechanical Engineering
ISBN:
9781118170519
Author:
Norman S. Nise
Publisher:
WILEY
Mechanics of Materials (MindTap Course List)
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:
9781337093347
Author:
Barry J. Goodno, James M. Gere
Publisher:
Cengage Learning
Engineering Mechanics: Statics
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:
9781118807330
Author:
James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:
WILEY