Answered: Problem 2 A plain-carbon steel contains… | bartleby

Related questions

Question

Problem 2
A plain-carbon steel contains 93 wt % ferrite and 7 wt % Fe;C. What is its average carbon content in
weight percent?

Expert Solution

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Blurred answer

Similar questions

Which of the following statements is correct? (1 Point) d. All of these b. Patm = 14.7 psi c. Patm = 100000 bar %3D a. Patm = 101.3kPa
Determine the composition of the Liquid (wt% Sn) for a 40 wt% Sn, 60 wt% Pb alloy at 250°C.
For this question there could be one or MULTIPLE answers, Choose the best Match/Matches. For a monatomic ideal gas in thermal equilibrium near room temperature, a. U = 3/2 NkT. b. U = 5/2 NkT. c. degrees of freedom include translational and rotational motions. d. degrees of freedom include translational, rotational, and vibrational motions. e. U = 5/2 pV. f. U = 3/2 pV. Explain work please.
3. In an experiment to determine the thermal conductivity of a bar of a new alloy, one end is maintained at 0C and the other at 100C. The bar has a cross-sectional area of 1cm? and a length of 20cm. If the rate of heat conduction through the bar is 34 Watts, what is the thermal conductivity of the bar? उ 券

A hot air balloon uses the principle of buoyancy to create lift. By making the air inside the balloon less dense then the surrounding air, the balloon is able to lift objects many times its own weight. A large hot air balloon has a maximum balloon volume of 2090 m3. a. If the air temperature in the balloon is 54 °C, how much additional mass, in kilograms, can the balloon lift? Assume the molar mass of air is 28.97 g/mol, the air density is 1.20 kg/m3, and the air pressure is 1 atm.
4. The density of the most common polymorph of ice is 917 kg/m³. Use the Clausius-Clapeyron relation to explain why the slope of the phase boundary between water and ice is negative. b. How much pressure would you have to put on an ice cube to make it melt at -2° C? а.
PERUUS A metal has an initial oxide coating thickness, y, of 60 nm. After 2 hours at 700°C the oxide has grown to a thickness of 80 nm. Assuming a parabolic growth rate law applies, i.e. y² = c t + d (where, t is the time in hours and both c and d are constants) what will be the approximate thickness of the coating after a total of 36 hours at 700°C? 210 nm. 116 nm. O 232 nm. 420 nm. 126 nm. SVOJE VŠET