Problem 2 A cylindrical specimen of a nickel alloy hav- ing an elastic modulus of 207 GPa (30 x 106 psi) and an original diameter of 10.2 mm (0.40 in.) will experience only elastic deforma- tion when a tensile load of 8900 N (2000 lb) is applied. Compute the maximum length of the specimen before deformation if the maximum allowable elongation is 0.25 mm (0.010 in.).

Problem 2 A cylindrical specimen of a nickel alloy hav- ing an elastic modulus of 207 GPa (30 x 106 psi) and an original diameter of 10.2 mm (0.40 in.) will experience only elastic deforma- tion when a tensile load of 8900 N (2000 lb) is applied. Compute the maximum length of the specimen before deformation if the maximum allowable elongation is 0.25 mm (0.010 in.).

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter1: Tension, Compression, And Shear

Section: Chapter Questions

Problem 1.6.7P: A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The...

See similar textbooks

Similar questions

A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The wire is made of a copper alloy having a stress-strain relationship that may be described mathematically by =18,0001+30000.03(=ksi) in which is nondimensional and has units of kips per square inch (ksi). (a) Construct a stress-strain diagram for the material. (bj Determine the elongation, of the wire due to the Forces P. (c) IF the forces are removed, what is the permanent set of the bar? (d) If the forces are applied again, what is the proportional limit?
The rails of a railroad track are welded together at their ends (to form continuous rails and thus eliminate the clacking sound of the wheels) when the temperature is 60°F. What compressive stress ?? =6.5×10-6 /? is produced in the rails when they are heated by the sun to 120"F if the coefficient of thermal expansion a = the modulus of elasticity E = 30 × 106 psi?
Determine the strain energy per unit volume (units of psi) and the strain energy per unit weight (units of in ) that can be stored in each or the materials listed in the accompanying table, assuming that the material is stressed to the proportional limit. DATA FOR PROBLEM 2.7-5 Material Weight Density (lb/in3) Modulus of Elasticity (ksi) Proportional Limit (psi) Mild sleel 0.284 30,000 36,000 Tool steel 0.284 30,000 75,000 Aluminum 0.0984 10,500 60,000 Rubber (soft) 0.0405 0.300 300
200 stress 150 (MPa) 100 50 0-2 strain From the tensile stress-strain behavior for the brass specimen cP the diameter is 12-8 mm Calculate the folwing:- 1- The Yield stress, 2-Modulus of elasticity. 3- The Tensile strength .
Example: Convert the change in length data in Table 3-2 to engineering stress and strain and plot a stress-strain curve Homework- help Table 3-2 The results of a tensile test of a 0.505 in. diameter aluminum alloy test bar, initial length (1o) = 2 in. Calculated LTO Load (Ib) Change in Length (in.) Stress (psi) Strain (in./in.) 0.000 1000 0.001 0.0005 4,993 14,978 24,963 34,948 37,445 39,442 39,941 39,691 37,944 3000 0.003 0.0015 5000 0.005 0.0025 7000 0.007 0.0035 7500 0.030 0.0150 7900 0.080 0.0400 8000 (maximum load) 0.120 0.0600 7950 0.160 0.0800 7600 (fracture) 0.205 0.1025
A cylindrical specimen of a titanium alloy having an elastic modulus of 207gpa and an original diameter 3.8mm will experience only am elastic deformation when a tensile load of 2000pa is applied. Compute the maximum length of the specimen before deformation if the maximum allowable elongation is 0.47mm
A Brass specimen is subjected to a Tensile test in a laboratory. The following data obtained are: Length of Specimen = 367 mm; Diameter of Specimen = 19 mm; Yield Stress = 124 N/mm?: Ultimate Stress = 217 N/mm?: Fracture Stress = 183 N/mm?: % of Elongation = 50 % % of Reduction in area = 27 %. Determine the elongation at 103 kN, Load at yielding. Maximum load, Load at fracture, Final Length & Final diameter. Take Young's Modulus as 104 GPa.
The yield stress for mild steel is 207MP.. A specimen with diameter of 0.01lm and length of 0.1m is subjected to a load of weight of 10kg, and the resulting elongation is 6.077 microns. Determine whether the stress is above or below the yield stress, and if it is below, compute the Young's modulus of the material.
*O llAsiacell Strength of m. -> 02: A steel specimen 12mm diameter has gauge length 50mm. the steel specimen had tested via tensile test under maximum load 66KN with elongation 7.5mm, and the yield load of this specimen is 15KN with elongation 2.4mm. Calculate: 1- The engineering ultimate stress (ultimate tensile strength), and engineering strain at this point. 2- The engineering stress and strain at yield point. 3- The modulus of elasticity, and the modulus of resilience. 4- The final or fracture strain of a steel specimen, if you know that the final length of specimen after testing is 58.5mm. 5- The true stress and strain for ultimate point. Q3: The yoke-and-rod connection is subjected to a tensile force of 15 kN. Determine the average normal stress in each rod and the average shear stress in the pin A between the members. Finally, find the shear strain in pin A. Take G teef 75GPA 40 mm 15 kN, 30 mm 30 mn 15 kN 04: In figure as shown below, assume that a 35mm diameter rivet joint the…
A brass specimen of the circular cross-section is fractured at 159 kN force and the final length of the specimen at fracture is 51 mm. The fracture strength of the specimen is found to be 85 kN/mm2. The percentage of elongation of the specimen is 42 %. Determine the following 4-Stress under an elastic load of 14 kN 5-Young's Modulus if the elongation is 1.5 mm at 14 kN 6-Final diameter if the percentage of reduction in area is 27 %.
A tensile test is being conducted on a steel-rod specimen with a gauge length of L0=4.0 in and an initial diameter of d0=0.75 in. If the final length of the rod at fracture is Lt= 5.53 in, find the percent elongation of the rod at fracture
A cylindrical specimen of a titanium alloy having original diameter of 2.96 mm experiences elasticdeformation when a tensile load of 2500 N is applied. Compute the maximum length of the specimenbefore deformation if the maximum allowable elongation is 0.43 mm. Note: Etitanium = 107 GPa.