In a metal forming operation when the materialhas just started yielding, the principal stressesare o, = +180 MPa, o,= - 100 MPa, o3 = 0.%3DFollowing von Mises criterion, the yield stress is

Answered: Image /qna-images/answer/5e836212-cadc-44ce-b11f-d23130e7ae96.jpg

Answered: In a metal forming operation when the…

In a metal forming operation when the materia. has just started yielding, the principal stresses +180 MPa, o2 are o, = = -100 MPa, o3 = 0 Following von Mises criterion, the yield stress %3D %3D

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Need correctly with proper explanation. I will like surely. Thank you!!!!
Please answer for that now
Q4) A plate 52 mm wide, 52 mm long, and 7 mm thick is loaded in tension in the direction of the length. The plate contains a crack as shown in the figure below, with a crack length of 11.5 mm. The material is steel with Kic= 80 MPa (m)(1/2) and Sy = 950 MPa. Determine the maximum possible load (in kN) before the plate has uncontrollable crack growth. (Beta) 7.0 6.0 5.0 4.0 3.0 2.0 1.0 a 0.2 σ h/b=0.5 1.0 0.4 a/b ratio 0.6 O.
1. A part made of Aluminum 6061-T6 has a yield strength = 400 MPa. For each stress state below, draw all 3 Mohr's circles, find the principal stresses, and calculate the safety factor against yield using both the distortion-energy (von Mises) and maximum shear stress (Tresca) criterions. (If relevant) A clearly labeled diagram (or diagrams) clearly pertaining to your analysis with a coordinate system and relevant labels. Final answer with appropriate units and significant figures. You can use the fprintf() command in MATLAB to format numerical results A 2-3 sentence reflection on your answer. Does it make sense? Why or why not? What are some implications?
Thank you for answering this question. Please you specify each step as soon as possible. Good Luck! Thank You. Find the maximum biaxial stress,ox= -20, oy= -30, o > 0, that one can apply to a 60° lamina of glass/epoxy. Use maximum stress theory. Strength values of glass/epoxy: (01Jult = 1062 MPa, (01Jult= 610 MPa, (02")ut = 30 MPa, (02)ult = 118 MPa, (T12)ult = 72 MPa
A steel rod (initial diameter: 3.2 mm, initial length: 42 mm) is extended by auniaxial tensile load of 4800 N in 120 seconds. At this load, the length of therod is measured as 49,2 mm. Calculate the followings:(a) Stress and strain occurred on the rod at this load.(b) Initial strain rate.(c) Diameter of the rod at this load.(Yield strength : 380 MPa, Ultimate Tensile Strength: 670 MPa,Modulus of Elasticity: 210000 MPa were given for this material)
please solve it now please
I need the answer as soon as possible
elongation. 6) Chapter 3: Problem 3.7: (USCS Units) The flow curve for a certain metal has a strain-hardening exponent-0.20, and its strength coefficient=26,000 lb/in2. Determine (a) flow stress at a true strain= 0.15 and (b) true strain at a flow stress = 20,000 lb/in2. (c) What is the likely metal in this problem? %3D
Pr
The diagram below shows a microscopic metal rod with a single crystal structure whose orientation is indicated by the inset. A force of F = 14.9 N is applied to the rod. The cross-sectional area is 1.1 mm². Calculate the shear stress along the close-packed direction. Dogo ooooo a. 4.65 MPa O b. 6.08 MPa c. 5.09 MPa O d. 4.04 MPa O e. 5.53 MPa
The diagram below shows a microscopic metal rod with a single crystal structure whose orientation is indicated by the inset. A force of F = 25.8 N is applied to the rod. The cross-sectional area is 1.9 mm². Calculate the shear stress along the close-packed direction. O a. 5.10 MPa O b. 6.10 MPa c. 4.66 MPa O d. 5.54 MPa Oe. 4.05 MPa