Example8.2: An L-shaped structural section is direct extruded from an aluminum billet in which Lo = 500 mm and Do = 100 mm. Dimensions of the cross section are given in Figure below, Die angle 90°. Determine (a) extrusion ratio, (b) shape factor, and(c) length of the extruded section if the butt remaining in the container at the end of the ram stroke is 25 mm. %3D

Example8.2: An L-shaped structural section is direct extruded from an aluminum billet in which Lo = 500 mm and Do = 100 mm. Dimensions of the cross section are given in Figure below, Die angle 90°. Determine (a) extrusion ratio, (b) shape factor, and(c) length of the extruded section if the butt remaining in the container at the end of the ram stroke is 25 mm. %3D

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

3. Estimate the force required for a 90° bending of a St 50 steel of thickness of 1.5 mm in a V die, the die opening can be taken as seven times the thickness, the length of the part is 1.5 m and TS = 500 MPa? (a) 200 KN, (b) 214 KN, (c) 224 KN, (d) 234 KN, (e) 244 KN
Estimate the maximum bending force requires for a 3 mm thick and 300 mm long Ti-6Al-4V titanium alloy sheet (Sy=925 MPa, S_UT = 1000 MPa, and E=110 GPa), annealed and quenched at 25 oC, in a wiping die with a width of 150 mm. Hint: recall that k-factor for a wiping die varies from 0.3-0.34. A)5.3 kN B)5.7 kN C)633 kN D)None of the above
None
Company XSheetMetal Ltd. is mass producing the component illustrated in Figure 1.
4)
I think the answer is 0Mpa , Looking for Explanation.
find the die shape factor in an extrusion process, if the diameter of the extruded cross-section is =15 cm and the diameter of the circle of the same area as the extruded shape is = 10 cm
Calculate the ram pressure during indirect extrusion process when a cylindrical billet is 300 mm long and 150 mm in diameter used to produce a 45 mm diameter. In this process: a=0.8, b=1.4, K=275MPA, n=0.12.
An indirect extrusion operation produces the cross-section shown in Figure 1 (Dimensions in cm) from an aluminum alloy (annealed) billet whose diameter is 300 mm and length of 500 mm. In the Johnson strain equation, a=0.8 and b=1.2 Determine the ram force in the process
Manufacturer process A compound die will be used to blank and punch a large rectangle (90x150mm blank dimensions) out of 6061ST aluminum alloy sheet stock 3.5 mm thick. The diameter of inside hole is 25 mm. The aluminum sheet metal has a tensile strength = 310 MPa. Determine the minimum tonnage press (force) to perform the blanking and punching operation (1) assume that blanking and punching occur simultaneously and (2) assume that punching occurs first, then blanking. Take: Ac=0.06
Stick-slip phenomenon results in extrusion defect.