Answered: estion 3: Indicate which of the…

estion 3: Indicate which of the following microstructures corresponds to Pearlite Bainite Spheroidite_ Martensite What is the reason(s) behind your selection? and Tempered Martensite

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: (a) Discuss the following iron based alloys with their applications in engineering: i. Low Carbon…

A: 1.Low Carbon steels Low carbon steels are principally composed of ferrite, a solid solution phase of…

Q: omenclature 2 composition, 3 crystal structure 4 Phase Diagrams,

A: Spheroidal graphite iron, also referred to as ductile cast iron, nodular cast iron, SG iron, and…

Q: 2. Please complete the table below. Please fill the name of the phases after the indicated heat…

A: Below is the table which indicates the phases after heat treatment

Q: 700 L 600 500- (A1)+ (A1)+ O 400 (A1) emperature,

A: steps :- (1) solutioning (2) quenching (3) aging Maximum hardness will be obtained at an optimum…

Q: Compute the mass fractions of a ferrite and cementite in pearlite. Assume T 726 C°. W₁ = WFe3 C i =

A: Given: T = 726 C To find the mass fraction of α ferrite and cementite in Pearlite

Q: Copper-Nickel alloy is widely applied in industry. (a) List at least three applications where Cu-Ni…

A: Given: The wt% of mixture = 40 Wt% CO and 60 Wt% Ni The temperature, T = 1320oC

Q: Compact Graphite cast iron was obtained from fast cooling rates. O F Strength and ductility of…

A: The above question we have to given solutions

Q: a)Draw the microstructure at each of the points A, B, C, D in the phase diagram given on the left.…

A: a) Iron carbon phase diagram from figure From the figure, it shows that at point A only the liquid…

Q: Fine pearlite of steel containing 0.45% C can be obtained after Hardening process Full annealing…

A: Introduction: The 0.45 C medium carbon steel is one of the most commonly used structural materials…

Q: Question 5 (12 marks) Referring to the Fe-C phase diagram given below, suppose an austenite having a…

A: The iron-carbon diagram shows the changes in phases of Fe-C at different temperatures as the weight…

Q: Which of the following statements about recrystallisation of metals are true? Select one or more:…

A: Solution: Given Data: Which of the following statements about recrystallisation of metals are true?…

Q: Draw a diagram of the gray and nodular gray cast iron's substructure. 2. Comment on the gray…

A: Given data:- gray and nodular gray cast iron gray wrought iron's To be explained:- Draw a diagram…

Q: Is it true that Martensite is tempered because it is too strong? Why or Why not

A: Initially, martensite is harder and brittle phase when steel is sudden cool down. When the hardness…

Q: Consider 1.0 kg of a 99.4 wt% Fe-0.6 wt% C alloy that is cooled to a temperature just below the…

Q: Plot the Iron-Iron Carbide phase diagram label all phase 400 answer the following: a-Show the…

A: Phase Diagram- it is a graphical reprsentation of the effect of temperature and composition upon…

Q: Draw Fe-C binary phase diagram and discuss martensitic transformation for 0.1C% and 0.5C% plain…

A: The iron- carbon phase diagram is given below -

Q: answer the following: 3) Plot the Iron-Iron Carbide phase diagram label all phases and temperatures,…

A: Phase Diagram-it is a graphical reprsentation of the effect of temperature and composition upon…

Q: Draw the iron-Fe3C phase diagram. Consider high carbon steel alloy.(min carbon content 0.9C%) a) It…

Q: 3- The limited solid solubility Binary phase diagram has many types of reactions like 4- the Crystal…

A: Given questions are related to material science. 3. The limited solid solubility Binary phase…

Q: What distinguishing features do eutectoid and martensitic transformations in steel have? Compare and…

A: To explain: What distinguishing features do eutectoid and martensitic transformations in steel have?

Q: 10 Cite the phases that are present and the phase- Ocompositions for the following alloy (g) 21.7…

Q: Suppose you wanted to have two samples of NiTi wire: one that is in the high-temperature austenite…

A: The high-temperature phase at 0 °C of the NiTi alloy is termed as Austenite. It tends to transform…

Q: Draw Iron - Iron Carbide Phase diagram and show the following: 4- Types of ferrous alloys on…

A: given; iron-iron carbide phase diagram;

Q: Based on the IT diagram for an iron-carbon alloy of eutectoid composition, specify the final…

A: Given: There are time temperature graph that signifies the changes in the microstructures according…

Q: If the Fe-C alloy consists of 62.29 % pearlite and 37.71 % proeutectoid cementite phase, what is the…

Q: Consider an AISI 1045 ferrite and pearlite microstructure. The sample is initially heated to 845 deg…

A: In the tempering of steels, the primary goal is to reduce the brittleness that is often associated…

Q: As pure iron is heated up through 910°C will it: 1600 C 1400 C liquid 910°C y + cementite Fe,C…

A: Solving the first question out of two. Pls, repost the question in order to get solved the other…

Q: Why does fracture toughness increase with yttria content. Use the phase diagram to explain

A: The crack strength improvement of yttria-balanced out tetragonal zirconia polycrystalline ceramics…

Q: 1- The Binary phase diagram of 2 metals completely in soluble in each othe in solid state. labeling…

A: Solution is given below

Q: What heat treatment do you apply? Using this graph, how is it possible to increase the strength and…

A: Solution:

Q: What is the crystal structure of martensite? Why can you not find a martensite phase region in the…

A: The crystal structure of the martensite is Body-Centered Tetragonal (BCT). It is a Body-Centered…

Q: Consider 4.7 kg of austenite containing 0.26 wt% C, cooled to below 727°C (1341'F). (a) What is the…

A: Givenmass of austenite =4.7gcarbon =0.26%Ccooled to below 727oC 1341oF

Q: a.) What type of binary phase diagram is Pb-Sn an example of?

A: Pb-Sn binary phase diagram is an example of "Eutectic system". A eutectic system has two components,…

Q: (a) What is the proeutectoid phase? (b) How many kilograms each of total ferrite and cementite form?…

Q: 1) To obtain a ferritic-spherical carbide (cementite) internal structure in super-eutectoid steels…

A: Annealing is a heat treatment process in which metal or alloy is heated to a certain temperature and…

Q: Use the Lead-Tin (Pb-Sn) phase diagram below to answer the following questions: Place the following…

A: Given:

Q: 1. What is wrought iron in gray? 2. Why does gray cast iron lack tensile strength? 3. What can…

A: Wrought iron is the purest iron which contains 99.5% iron but may contain upto 99.9% iron.Wrought…

Q: Use the copper silver phase diagram below. 100g of a 40 wt% Cu 60 wt% Ag alloy is made and cooled…

A: To solve this problem, we will use the copper silver phase diagram, which shows the phases of copper…

Q: Calculate the amounts of solid phases of ferrite and cementite present in pearlite. + Fe;C a + Fe;C…

A: Pearlite forms at 0.76% carbon so we need to draw line and solve the question

Q: ! 14. In gray cast iron, the graphite exists in the form of nodule flakes cementite * 5. Eutectoid…

Q: What process will result in Ferrite plus Pearlite microstructure? List the reasons why this…

A: The microstructure of ferrite and pearlite will results in hypoeutectoid steel. This is having the…

Q: 2. For a 10-90 Cu-Zn alloy, what would the percent of each phase be at 500°C, 400°C and 300°C?

Q: Using the TTT diagram, explain how you can get the following: (explain by mentioning detailed heat…

Q: What is the crystal phases just above eutectoid temperature for a carbon steel with carbon…

Q: HOME WORK Calculate the amounts of solid phases of ferrite and cementite present in pearlite. y+…

A: Given dataTo determine the solid phases of ferrite and cementite present in pearlite

Question

100%

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1: Given

VIEW

Step 2: Solution

VIEW

Solution

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 3 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Using the isothermal transformation diagram given in Figure 2 for a specific material composition to answer the following (this is NOT an Fe-C steel!). NOTE: Assume that you begin with a single-phase sample of α at 790 C.a. What temperature on the diagram corresponds to the α-to-γ phase transformation temperature that would be found on an equilibrium phase diagram? Explain your answer. b. What temperature would provide the most rapid, isothermal phase transformation of α to γ? What would be the minimum time from onset of the phase transformation to its completion? c. On Figure 2, draw and label a cooling schedule (from 790 C) that will produce a single-phase α material at 100 C. How does the thickness of the piece of material influence your ability to create a single-phase α structure? d. Why does the time to initiate phase transformation become smaller as the temperature is reduced within the temperature range above the “nose” of the TTT diagram? Be specific, what process is…
1. Given the Iron –Iron carbide phase diagram below answer the following questions:
Need neat and clean handwritten solution explaining both parts
Material science Assuming this system forms a laminar type eutectic, determine the volume proportion of phases for an equilibrium solidified 50% Pb alloy. Sketch the expected microstructure.
Metal Working: What process will result in a Martensite microstructure? List the reasons why this structure will have high strength.
please answer correctly and completly
Consider 2.0 kg of austenite containing 0.5 wt% C and cooled to just below 727°C (1341°F). (a) What is the proeutectoid phase? (b) How many kilograms each of pearlite, the proeutectoid phase, and cementite form?
1) Draw the iron-Fe;C phase diagram. Consider 0.25 and 1.1 wt% C steel alloy. It is cooled slowly from atemperature within austenite phase to room temperature. Show a) microstructure at 1000 °C b) microstructure at 730°C c) microstructure at 715°C and d) microstructure at room temperature e) What do you say about mechanical properties of these alloys, depending on their microstructure at room temperature?
Hello, I hope you are fine. I need to do this homework in Metal Engineering. I hope to get your help because I have an important homework.
2- (9 kg/s) of steam, initially at (40 bar, 300 C°), expands adiabatically in a turbine to (4 bar). Determine the power produced if the isentropic efficiency of the turbine is (78.5%).