Consider 2.5 kg of austenite containing 0.65 wt% C, cooled to 726 ° C a)Is the steel hypereutectoid or hypoeutectoid b)What is the primary microconstituent (proeutectoid)phase? c)How many kilograms of total ferrite and cementite form? d)How many kilograms each of pearlite and the proeutectoid phase form? Weight percent carbon

Consider 2.5 kg of austenite containing 0.65 wt% C, cooled to 726 ° C a)Is the steel hypereutectoid or hypoeutectoid b)What is the primary microconstituent (proeutectoid)phase? c)How many kilograms of total ferrite and cementite form? d)How many kilograms each of pearlite and the proeutectoid phase form? Weight percent carbon

Understanding Business

12th Edition

ISBN:9781259929434

Author:William Nickels

Publisher:William Nickels

Chapter1: Taking Risks And Making Profits Within The Dynamic Business Environment

Section: Chapter Questions

Problem 1CE

See similar textbooks

Similar questions

9. Two machines are currently in use in a process at the Dennis Kira Mfg. Co. The standards for this process are LSL = .470" and USL = .476". Machine One is currently producing with mean = .474" and standard deviation .0003". Machine Two is currently producing with mean .4745" and standard deviation .0002". Which machine has the higher capability index? Machine One has an index of (round your response to two decimal places). (round your response to two decimal places). Machine Two has an index of Machine (1) (1) Two One has the higher capability index.
A process has a sigma=rating of 3.35-o. Fraction defective for the process is P(Z Z (UTL)). What is the value of Z (LTL)?
7
What is a capable process? Is a capable process a perfect process? In other words, does a capable process produce output that meets specifications?
Twelve samples, each containing five parts, were taken from a process that produces steel rods at Emmanual Kodzi's factory. The length of each rod in the samples was determined. The results were tabulated and sample means and ranges were computed. The results were: Sample Sample Mean (in.) Range (in.) Sample Sample Mean (in.) Range (in.) 1 9.602 0.033 7 9.603 0.041 2 9.602 0.041 8 9.605 0.034 3 9.593 0.034 9 9.597 0.027 4 9.606 0.051 10 9.601 0.029 5 9.599 0.031 11 9.603 0.039 6 9.599 0.036 12 9.606 0.047 Part 2 For the given data, the x double overbarx = 9.6013 inches (round your response to four decimal places). Part 3 Based on the sampling done, the control limits for 3-sigma x overbarx chart are: Upper Control Limit (UCL Subscript x…
A machine cuts circular filters from large rolls of material. The diameters of the filters are normally distributed with a mean of 2.00 cm and a standard deviation of 0.02 cm. Specifications call for the filters to have diameters between 1.95 cm and 2.03 cm. What percent of production does not meet specifications
J 1
Linda Boardman, Inc., an equipment manufacturer in Boston, has submitted a sample cutoff valve to improve your manufacturing process. Your process engineering department has conducted experiments and found that the valve has a mean of 8.00 and a standard deviation of .04. Your desired performance is = 8.0 ± 30, where o = 0.047. Is the following statement true or false? Can Boardman produce the valve within the specified tolerance? (TRUE=yes, it can; FALSE=no, it cannot) O True O False
A process screens a certain type of potash granule, resulting in a mean diameter of 0.067 cm and a standard deviation of 0.004 cm. The allowable variation in granule diameter is from 0.048cm to 0.087cm. Is the process capable? a. Cannnot be determined because sample size is not available b. Cannot be determined because USL and LSL information is not available c. Process is NOT capable d. Process is capable
Consider a process with lower process control limit as 1.338 and upper process control limit as 1.342 . The lower specification limit is 1.335 and the upper specification limit is 1.345. Utilizing the information provided, is the process is capable of meeting design specifications?
Refer to Table 56.1-Factors for Computing Control Chart Limits.(3.sigma) for this problem. Auto pistons at Wemming Chung's plant in Shanghai are produced in a forging process, and the diameter is a critical factor that must be controlled. From sample sizes of 10 pistons produced each day, the mean and the range of this diameter have been as follows: a) What is the value of x? mm (round your response to two decimal places). b) What is the value of R? R=mm (round your response to two decimal places). c) What are the UCL, and LCL; using 3-sigma? Day 1 2 3 4 5 Upper Control Limit (UCL;)mm (round your response to two decimal places) Lower Control Limit (LCL;)mm (round your response to two decimal places). d) What are the UCL and LCL using 3-sigma? Upper Control Limit (UCLR)-mm (round your response to two decimal places). Lower Control Limit (LCL)-mm (round your response to two decimal places) Mean x (mm) 154.9 151.2 155.6 155.5 154.6 Range R (mm) 4.4 4.8 4.3 5.0 4.7 Next
A weighing process has an upper specification of 1.751 grams and a lower specification of 1.632 grams. A sample of parts had a mean of 1.7 grams with a standard deviaiton of 0.023 grams. Round your answer to four decimal places. What is the process capability index for this system?