Consider the tensile stress-strain diagram in the figure below labeled 1 and 2. These diagrams are typical of metals. Answer the following questions, and consider each part as a separate question that has no relationship to previous parts of the question. Which material has the larger work hardening exponent?(clearly mention 1 or 2) How do you know? (explain in 2-3 sentences) 1 0 2 Strain Stress

Consider the tensile stress-strain diagram in the figure below labeled 1 and 2. These diagrams are typical of metals. Answer the following questions, and consider each part as a separate question that has no relationship to previous parts of the question. Which material has the larger work hardening exponent?(clearly mention 1 or 2) How do you know? (explain in 2-3 sentences) 1 0 2 Strain Stress

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

3. What effects do the alloying additions have on the microstructure and mechanical properties of air-cooled (normalized) steel specimens? 1 4. What effects do the alloying additions have on the microstructure and mechanical properties of furnace-cooled (annealed) steel specimens?
H1.
In the Figure below, the tensile breaking strength, (sigma mark)tenstile-breaking = 140 ??? breaking strength at compression (sigma mar)kcompression-breaking = 460 ??? pouring Machine part made of iron is shown. to the piece P=25 kN forces are acting. piece for t=26 mm Calculate reliability according to Coulomb - Mohr theory ?
None
12. What are is an impact tests. Sketch the impact testing machine setup and explain the basic principle of toughness determination from it. What is DBTT? sketch the impact energy vs temperature curve for plain carbon steel and discuss why do many materials become brittle at low temperatures.
An annealed material with the properties of K = 700 MPa and n= 0.2, is initially cold worked some unknown amount. It is then subjected to 15% additional cold work and its yield strength is measured as 525 MPa. What was the unknown amount of cold work induced prior to the 15% added cold work?
A through hardened gear is to be made with steel (4340) is to be used in an application requiring a minimum tensilestrength of 1514.5 MPa and a minimum ductility of 39.5%RA. Oil quenching followed by tempering is to be used. Brieflydescribe the tempering heat treatment.Explain the use of TTT/Phase diagram and combination of phases
Some alloys use a combination of strain hardening and precipitation hardening to achieve particularly high strength levels. The usual order of strengthening is solution treatment, quenching, cold working, and finally precipitation heat treatment. Why not reverse the order of the cold working and precipitation heat treatment steps?
4/ Hot working of metals can be done at below recrystallization temperature. Select one: True False
I need answer within 20 minutes please please with my best wishes