Consider a single crystal of some hypothetical metal that has the FCC crystal structure and is oriented such that a tensile stress is applied along a [102] direction. If slip occurs on a (111) plane and in a [101] direction, compute the stress at which the crystal yields if its critical resolved shear stress is 3.2 MPa.

Consider a single crystal of some hypothetical metal that has the FCC crystal structure and is oriented such that a tensile stress is applied along a [102] direction. If slip occurs on a (111) plane and in a [101] direction, compute the stress at which the crystal yields if its critical resolved shear stress is 3.2 MPa.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

an alloy with an avg grain diameter of 0.053 mm is l16 MPa. When the grain diameter is 0.008Amm, the yeild strength goesupto 231 MPa.lf the yeild strength is 207MPA, what would the grain diameter be?
Consider a single crystal of a hypothetical metal that has the BCC crystal structure. A stress of 50 MPa is applied in the [101] direction of the BCC unit cell.a. Determine the most favourable slip direction for the (011) slip plane of the BCC unit cell. ⟨111⟩ is the family of directions with the highest linear density in the BCC unit cell.b. If τcrss = 27.5 MPa, determine if the single crystal yields. If not, what stress level is required?c. What is the minimum stress at which the BCC single crystal yields?
6.31 The flow stress for an alloy is 100 MPa when its dislocation density is 106 cm-2, and 150 MPa when its dislocation density is 108 cm-². When the flow stress is 190 MPa, what is the dislocation density?
1. Dislocations: What Are They? What makes them significant in metals and alloys? By drawing a 2D ball and stick model, you can highlight the key characteristics of an edge dislocation, including the extra-half plane, dislocation center, slip plane, sense vector, and Burgers vector. 2.What are the Burgers and sensation (dislocation line) vectors used for? Please answer all with full detail
If ß-Sn, a tetragonal crystal (point group 4/mmm, a = 0.583 nm, and c = 0.318 nm) is subject to a tensile stress of 63 MPa along [100] and to a shear stress of 18 MPa on the (100) plane in the [010] direction. Determine: a) the tensile stress normal to (110), and b) the shear stress on the (110) plane in the [1-10] direction.
The following figure displays both an Edge Dislocation and a Screw Dislocation. Answer the following questions regarding the characteristics of each Dislocation Edge dislocation Screw dislocation