Consider a 40 % V¢ SiC whisker-reinforced aluminum composite. Ef = 400GPa, Em= 70 GPa, and (l/d) = 20. Compute the longitudinal elastic mod-%3Dulus of this composite if all the whiskers are aligned in the longitudinaldirection. Use Halpin-Tsai-Kardos equations. Take = 2(1ld).

Solution: Given Data: Ef=400 GPaEm=70 GPal/d=20vf=0.40

Consider a 40 % Vf SiC whisker-reinforced aluminum composite. Ef = 40 ЭРа, Еm ulus of this composite if all the whiskers are aligned in the longitudina direction. Use Halpin-Tsai-Kardos equations. Take č = 2(1lld). 70 GPa, and (I/ld) = 20. Compute the longitudinal elastic moc

Consider a 40 % Vf SiC whisker-reinforced aluminum composite. Ef = 40 ЭРа, Еm ulus of this composite if all the whiskers are aligned in the longitudina direction. Use Halpin-Tsai-Kardos equations. Take č = 2(1lld). 70 GPa, and (I/ld) = 20. Compute the longitudinal elastic moc

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A composite bar BCD has a uniform external radius R. = 10 cm. Segment BC is solid steel, while segment CD is composed of a copper core of radius R,= 1cm bonded inside a steel sleeve. The lengths of the two segments are Lsc= 2 m and Lco= 1 m. The material moduli are Esteel= 200 GPa and Ecopper= 100 GPa. The bar is fixed at B and tensile loads are applied at section D (Fo= 1000 kN) and at section C (Fc= 400 kN). Compute the following: %3D Determine Axial stress of copper in segment CD in MPa. 2m 1m 400 KN 1000 KN
1. Use the method of composite areas to calculate the centroid of the plane region. a. the x coordinate is b. the y coordinate is 15 Dheminm
For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 and 3.66 GPa (2.8x10 and 5.3x 105 psi), respectively. If the volume fraction of fibers is 0.42, determine the moduli of elasticity of fiber and matrix phases. Em- E₁= i GPa GPa
A composite bar BCD has a uniform external radius Ro = 5 cm. Segment BC is solid steel, while segment CD is composed of a copper core of radius Ri = 1cm bonded inside a steel sleeve. The lengths of the two segments are LBC = 2 m and LCD = 1 m. The material moduli are Esteel = 200 GPa and Ecopper = 100 GPa. The bar is fixed at B and tensile loads are applied at section D (FD = 1000 kN) and at section C (FC = 400 kN). Compute the following: Axial stress of steel in segment BC in MPa. Axial stress of steel in segment CD in MPa. Axial stress of copper in segment CD in MPa. Total elongation of the assembly in mm.
just need help with part B. Thank you.
Q3: Analysis the composite structure shown in figure. The beam CD has El=40000 kN.m², the member AB has EA=800KN. T- A 30kN 3m -3m-
a) Find the centroid C (x,y) of the composite area b) Place a new coordinate system X-Y at the centroid C. Determine the area moment of inertia for the composite shape, Ix about the centroidal x-axis
A=9 Y=82 SHOW COMPLETE SOL
The tensile curves on the right correspond to an A356 alloy1 (unreinforced) and to the same alloy reinforced with Al3Ti particles. Please, provide the following information for the reinforced composite: Young’s modulus in GPa. UTS (MPa) The approximate proof stress 0.2 (MPa) Ductility  (%) Toughness (MJ/m3) True stress (MPa) at the fracture point.
A composite bar BCD has a uniform extemal radius R, = (x+2) cm. Segment BC is solid steel, while segment CD is composed of a copper core of radius R;= 1cm bonded inside a steel sleeve. The lengths of the two segments are Lgc = 2 m and LCD= 1 m. The material moduli are Esel = 200 GPa and Ecoper = 100 GPa. The bar is fixed at B and tensile loads are applied at section D (FD = 1000 kN) and at section C (Fc = 400 kN). Compute the following: 1. Axial stress of steel in segment BC in MPa. 2. Axial stress of steel in segment CD in MPa. 3. Axial stress of copper in segment CD in MPa. 4. Total elongation of the assembly in mm. 2m в 1m 400 KN 1000 KN