Answered: Compute the line energy of dislocation… | bartleby

Related questions

Question

Compute the line energy of dislocation in fcc, diamond. The shear modulus of
carbon is 462 GNm 2. The diameter of carbon atom in diamond is 1.54Å.
Answer: 1.46 x 10-³J/m

Expert Solution

Step by step

Solved in 3 steps with 5 images

SEE SOLUTION Check out a sample Q&A here

Blurred answer

Similar questions

The strain components εx, εy, and γxy are given for a point in a body subjected to plane strain. Determine the principal strains, the maximum in-plane shear strain, and the absolute maximum shear strain at the point. Show the angle θp, the principal strain deformations, and the maximum in-plane shear strain distortion on a sketch. εx = -750 με, εy = -345 με, and γxy = 1250 μrad. Enter the angle such that -45°≤θp≤ +45°.
In a standard tensile strain test, a 20 mm diameter aluminum rod is subjected to a tensile force of P = 30KN. If μ = 0.35 (Poisson's ratio) and E = 70 GPa (Young's modulus), determine: a) The elongation of the rod in a calibrated length of 150 mm and b) The change in the diameter of the rod
H.W A uniform glass rod having a length L is placed in the smooth hemispherical bowl having a radius r. Determine the angle of inclination 0 for equilibrium. Ans: L+VL+128r 2NCOSO No 0 = cos %3D 16r Note: By observation = 0.
if Vf=0.8 (volume fraction fiber) longitudinal modulus=? poisson's ratio=? in-plane shear stress=?
Problem 3: Suppose a 62-kg mountain climber has a 0.84 cm diameter nylon rope. Randomized Variables m = 62 kg d = 0.84 cm 1=31 m By how much does the mountain climber stretch her rope, in centimeters, when she hangs 31 m below a rock outcropping? Assume the Young's modulus of the rope is 5 x 10° N/m². AL=
A high-carbon steel with a fully pearlitic microstructure was used to form a high-strength bolt (H.-C. Lee et al., J. Mater. Proc. Tech. 211, 1044 (2011)). It was found that the bolt head had an average interlamellar spacing of 257 nm whereas the average spacing in the body of the bolt was 134 nm. Assuming that dislocation pileup is the primary mechanism responsible for the strength of this alloy, what ratio of strength (or hardness) might be expected in the head and body of the bolt?