Brass metal is subjected to a156 Kgf load, with a 2.23 mmdiameter of indenter. Theindentation of on sample isDj = 1.22 mm and D2 = 0.85%3Dmm respectively. Find theBHN value of the givensample.a. 449O b. 173O C. 149O d. 125

Answered: Image /qna-images/answer/78a00988-6b7e-4323-a3bd-ebc0f7a2ce0c.jpg

Answered: Brass metal is subjected to a 156 Kgf…

Brass metal is subjected to a 156 Kgf load, with a 2.23 mm diameter of indenter. The indentation of on sample is D = 1.22 mm and D2 = 0.85 mm respectively. Find the BHN value of the given sample.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Find the reading of the device for tensile testing of cement mortar in the unit KN if the cement…

A: Given : Tensile strength = 1.5 MPa Area = 2*2.3 cm^2

Q: Tensile test specimens are extracted from the "" and "y" directions of a rolled sheet of metal. "X"…

A: Since you have posted a question having multiple subparts we will solve first three subpart for you.…

Q: A 5 m long iron rod was stretched until its strain becomes 0.001. Find the elongation of the rod. A.…

A: Given:- Length of the rod (L) = 5 m = 5000 mm Strain developed in the rod = 0.001 To Find:-…

Q: From the tensile stress-strain behaviour for a casted iron as shown in the following curve. Please…

A: Given data: The original length of the specimen is L = 100 mm. The tensile stress is σt = 300 MPa.

Q: nm ha

Q: 10 A pulse is sent from a ship to the floor of the ocean 420 m below the ship; 0.60 s later the…

Q: From the tensile stress-strain behavior for the brass specimen , the diameter is 12-8 mm Calcalate…

Q: A tensile force of 10 kN is applied on a 0.02-m diameter and 2-m long rod. After applying the load,…

Q: A square cross-section v-notched specimen of height 75 mm has each side of 10 mm has been selected…

A: Given data height of specimen (h) = 75 mm side = 10 mm thickness of notch = 1.9 mm To determine…

Q: An aluminum specimen subjected to the Brinell hardness test, the indenter and indentation diameters…

Q: Determine the extension (m) of the whole system shown ik1-15.42 Nm, 42-27.49 Nm, 43-363 7.83 Nm, and…

Q: Stress strain behavior of a cast iron with a diameter of 15.8mm and gauge length of 60.80mm is shown…

A: Given Stress strain graph L =60.8 mm Diameter 15.8 mm to find Percentage elongation

Q: a 200mm long rod with a diameter of 50mm is loaded with a 4kN weight.the rod finale length 201.314mm…

A: Hello. Since your question has multiple sub-parts, we will solve first three sub-parts for you. If…

Q: a tensile test is conducted for a metal wire which has a diameter of 4.7 the maximum recorded force…

Q: 200 stress (MPa) 150 100 50 0.1 0-2 strain From the tensile stress-strain behavior for the brass…

Q: a 12mm thick steel tire has a width of 110mm and an internal diameter of 800mm. It is heated and…

A: Thickness, t= 12 mm Width, w= 110 mm Internal diameter of the tire, d= 800 mm Wheel diameter, D=…

Q: The brass has a shear modulus (G) of 40 GPa. In the torsion test calculated results. (G) was found…

Q: Determine the young's modulus of metal alloy having the following tensile stress - strain diagram

A: We Know that slope of stress strain diagram gives youngs modules. Here at strain=0.001…

Q: At the proportional limit, a 24 mm thick x 69 mm wide bar elongates 6.8 mm under an axial load of…

A: Given that , Elongation =6.8mmAxial load=453kN Length of bar l=1.8m Poison ratio=0.3

Q: Please answer these three questions. Thank you! A material has a Poisson’s ratio of -0.2 . Which…

A: Givenpart 1A material has a Poisson’s ratio of -0.2 . Which of the following is true?a. Strain is…

Q: In a Torsion test done, the following data were collected: the radius of the specimen was 3mm and…

Q: A copper specimen subjected to the Brinell Hardness Test using hardened steel ball indenter of…

A: Write the value of the Brinell hardness number. BHN=807 Write the diameter of the ball indenter.…

Q: The diagram below shows a microscopic metal rod with a single crystal structure whose orientation is…

Q: A tensile forceo f 100 kN is applied on a 0.02-m diameter and 2-m long rod. After applying the load,…

A: Given: The tensile force is F=100 kN. The initial diameter is do=0.02 m. The initial length of the…

Q: A square cross-section v-notched specimen of height 75 mm has each side of 11 mm has been selected…

A: Given: The height of specimen, h = 75 mm The side of specimen, s = 11 mm The notch thickness, t =…

Q: At the proportional limit, a 18 mm thick 84 mm wide bar elongates 6.9 mm under an axial load of 495…

A: The change in width of the bar is -0.1242 mm.

Q: A wire 10 m long has a cross-sectional area 1.25 x 10-4 m2. It is subjected to a load of 5 kg. If…

Q: A 2.0-inch diameter 4140 steel bar is austenized and tempered in oil without Agitation, determine…

Q: If the Young’s modulus and rigidity modulus of a material are 210GPa and 70GPa respectively,…

A: We have given the following problem If the Young’s modulus and rigidity modulus of a material are…

Q: The diagram below shows a microscopic metal rod with a single crystal structure whose orientation is…

Q: 2. Calculate the stress in MPa retained in a metal due to shot peening, using the value of the slope…

A: The graph for d vs sin²ϕ is .

Q: A mild steel rod of 12mm diameter was tested for tensile strength with the gauge length of 60mm.…

A: Given data: ● The initial diameter and gauge length of the mild steel rod: do = 12 mm , Lo = 60 mm ●…

Q: The brass has a shear modulus (G) of 40 GPa. In the torsion test calculated results, (G) was found…

Q: A tensile force of 100 kN is applied on a 0.02-m diameter and 2-m long rod. After applying the load,…

A: The tensile force is F=100 kN. The initial diameter of the rod is di=0.02 m. The initial length of…

Q: been selected to perform Charpy impact test. A v-notch of thickness 1.75 mm is made at the middle of…

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

Brass metal is subjected to a
156 Kgf load, with a 2.23 mm
diameter of indenter. The
indentation of on sample is
Dj = 1.22 mm and D2 = 0.85
%3D
mm respectively. Find the
BHN value of the given
sample.
a. 449
O b. 173
O C. 149
O d. 125

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Solve the moj and tabulation and state whether tensile or compress
A ul ? KBIS M 1:11 O photo_2021-0... -> 200 stress 150 (MPa) (00 50 0-2 strain From the tensile stress-strain behavior for the brass specimen d the diamcter is 12-8 mm Calculate the folluding:- 1- The Yield stress. 2- Modulus of elasticity. 3 - The Tensile strength . II
in a Torsion test done. the following data were collected: the radius of the specimen was 3mm and the gauge length was 76.2mm. During the elastic zone: T1=0. 01N.m. 81=14.760, 12-17.13N.m, and 02 36.910, The modulus of rigidity G will be equal to: Select one O a 44.283 GPa. O b. 26.522 GPa. O C 462.91 MPa. O d. 12.94 GPa.
please help me answer this question with complete solution and figure. i promise to give high rating, thank you very much.
I need a step by step answer please how to solve this :)
O IY:YY docs.google.com/forms O Superficial cracks. In a tensile strength test a metal bar with initial and final length of 2 in. and 2.195 in. respectively. Find the * .percentage of cold working 9.75 % 15.82 % 8.53 % 12.54 % 17.38 % O Which one of the following NDT methods can be considered as the * :most efficient Dye-penetrant. Ultrasonic. II
Correct one
Which of the following annealing process Negate effect of cold working by (recovery/ recrystallization) O a. O b. 0 с. O d. Process anneal Spheroidize Normalize Stress relief
Asiacell l. ZA0 @ 团 / photo_2021-02-18_13-04... 200 stress 150 (MPa) 100 50 0.1 0-2 0.3 strain From the tensile stress -strain behavior for the brass specimen ,cP the diameter is 12-8 mm Calculat e the follouding :- 1- The Yield stress , 2-Modulus of elasticity. - The Tensile strength .
Please l need the answer quick
A 2.0-inch diameter 4140 steel bar is austenized and tempered in oil without Agitation, determine the resulting hardness at 0.6 inches below the surface, present all the Procedure to get to the answer
Solve this early both parts