Barium titanate, a ceramic used in electronics, was analyzed by the following procedure: Into a Pt crucible was placed 1.2 g of Na₂CO3 and 0.8 g of Na₂B4O, plus 0.3124 g of unknown. After fusion at 1000°C in a furnace for 30 min, the cooled solid was extracted with 50 mL of 6 M HCl, transferred to a 100-mL volumetric flask, and diluted to the mark. A 25.00-mL aliquot was treated with 5 mL of 15% tartaric acid (which complexes Ti4+ and keeps it in aqueous solution) and 25 mL of ammonia buffer, pH 9.5. The solution was treated with organic reagents that complex Ba²+, and the Ba complex was extracted into CCl4. After acidification (to release the Ba²+ from its organic complex), the Ba²+ was back-extracted into 0.1 M HCl. The final aqueous sample was treated with ammonia buffer and methylthymol blue (a metal ion indicator) and titrated with 32.42 mL of 0.01376 M EDTA. Find the weight percent of Ba in the ceramic. weight percent of Ba: wt%

Barium titanate, a ceramic used in electronics, was analyzed by the following procedure: Into a Pt crucible was placed 1.2 g of Na₂CO3 and 0.8 g of Na₂B4O, plus 0.3124 g of unknown. After fusion at 1000°C in a furnace for 30 min, the cooled solid was extracted with 50 mL of 6 M HCl, transferred to a 100-mL volumetric flask, and diluted to the mark. A 25.00-mL aliquot was treated with 5 mL of 15% tartaric acid (which complexes Ti4+ and keeps it in aqueous solution) and 25 mL of ammonia buffer, pH 9.5. The solution was treated with organic reagents that complex Ba²+, and the Ba complex was extracted into CCl4. After acidification (to release the Ba²+ from its organic complex), the Ba²+ was back-extracted into 0.1 M HCl. The final aqueous sample was treated with ammonia buffer and methylthymol blue (a metal ion indicator) and titrated with 32.42 mL of 0.01376 M EDTA. Find the weight percent of Ba in the ceramic. weight percent of Ba: wt%

Chemistry

10th Edition

ISBN:9781305957404

Author:Steven S. Zumdahl, Susan A. Zumdahl, Donald J. DeCoste

Publisher:Steven S. Zumdahl, Susan A. Zumdahl, Donald J. DeCoste

Chapter1: Chemical Foundations

Section: Chapter Questions

Problem 1RQ: Define and explain the differences between the following terms. a. law and theory b. theory and...

See similar textbooks

Similar questions

Molecular Weights: -Cu 63.546g/mol A rock was analyzed for its copper content. Since copper goes through redox reactions, an iodometric totration was utilized. An unknown 1.5098 g sample was acidified using 3M sulfuric acid to dissolve the Cu compounds and diluted w/ 30mL distilled water. Kl was then added resulting in 12 and Cul precipitate from Cu²+ (first reaction). I₂ then reacted with excess Ki resulting in 13 (second reaction) w/c was titrated with Na2S203 (third reaction). 17.600mL of the titrant was required in the solution to reach the starch end point. Before the the sample was titrated, the titrant was standardized by taking 50mL of 6.786e-3 standard KIO3 sol'n, acidifying and adding KI crystals. 9.8mL was required for the titration of this solution to reach starch endpoint. a. Give the concentration (M) of S₂O3² titrant. b. Give the copper content of the rock (%w/w). wwwwwww....
A STOCK SOLUTION containing 0.1581 g/L K2CrO4 was prepared.In order to make the CALIBRATION STANDARD, 5 ml of the STOCK was transferredinto a 50ml volumetric flask and then diluted with an appropriate solvent.Calculate:(a) The ppm of K2CrO4 in the CALIBRATION STANDARD.(b) The molarity of K2CrO4 in the CALIBRATION STANDARD. (c) Calculate the molar absorptivity of K2CrO4 (at 371.0 nm). Assume that Beer's Law isobeyed over this concentration range.At 371.0 nm, this CALIBRATION STANDARD in a cell of path length 1.00 cm gave a %T of 59.752.
A 20.0 mL sample of commercial bleach was diluted with water to a 250.0 mL volumetric flask. A 50.0 mL aliquot of the diluted sample was treated with excess KI and starch. The liberated iodine was titrated with 0.399 M Na2S2O3, requiring 13.9 mL to reach the end point. (a) Identify the type of redox titration method used. (b) Identify the indicator and endpoint color. (c) Calculate the % w/v NaOCl in the sample.
A sílicate ore contains 12.00% Na,0 and weighs 0.5000 gram. On analysis by the J.L. Smith method, the sample yielded 0.1500 g of a mixture of NaCl + KA. What weight of K2PtCl, was obtained from the mixture of chlorides?
Consider an alloy of 57 wt% FeO and 43 wt% MgO. a. Calculate the composition of the alloy in atomic percent b. Calculate the amount of solid and liquid if the mass of the alloy is 350 kg
Perform the balance in basic medium: H₂0₂ (ac) + MnO4 → 0₂₁6 + MnO₂ (s) (ac) Calculate the normality of mannese oxide (IV) if 1.32 g are weighed and 25 ml are measured.
In a beaker 20mL of 0.5M Ca(OH)2 and 80mL of 0.5M CH3COOH are mixed and then this mixture is added on 2g of active coal. After waiting for about 20 minutes the solution is filtered and the filter is titrated by 1M NaOH solution in the presence of an indicator. 10mL of the NaOH solution has been used. Calculate the amount of acetic acid adsorbed per gram of the coal in moles. Explain all the steps and reactions of the experimental process by your own comments.
What is the full equation (not the net ionic equation) for the chemical reaction of 0.001 M Fe(NO3)3 plus 0.0002 M NaSCN diluted up to 10 mL with 0.1M HNO3? Please include the acid that is the diluent.
Enter a net ionic equation for the reaction of acetic acid, CH3COOHCH3COOH, with zinc. Express your answer as a balanced net ionic equation. Identify all of the phases in your answer.
Fine particles of metallic iron can be injected underground to remediate pollution of underground aquifers by the industrial solvent trichloroethane. In one experiment, 2400L of an aqueous emulsion containing ~480 kg of Fe(0) consumed 17.0 kg of trichloroethane in 5 months. Write a balanced reaction using H2O and H+ to complete the balancing. What percentage of injected iron was used by this reaction in 5 months? Fe + C2HCl3 ---> Fe2+ + C2H4 + Cl-
In an experiment to determine the concentration of H2SO4 in a brand of toilet cleanser, 10.0 cm3 of the cleanser was first diluted to 250.0 cm3 with distilled water. 25.0 cm3 of the diluted cleanser were titrated with 0.320 mol dm–3 NaOH solution, using methyl orange as indicator.If 29.2 cm3 of NaOH solution is used, what is the concentration of H2SO4 in the undiluted toilet cleanser?a. 2.30 mol dm–3b. 4.60 mol dm–3 c. 9.20 mol dm–3 d. 11.50 mol dm–3
In 'Synthesis of an Iron Complex Salt', hydrogen peroxide (H202) is added to the solution and heat is applied until boiling. A side reaction is the formation of rust brown precipitate, which consists of potassium permanganate (KMN04) ferrous ammonium sulfate, Fe(NH4)2(SO4)2-6H20] iron (III) hydroxide, Fe(OH)3 Iron (II) oxalate (FeC204)