(B) Sample of Zinc have dimensions 10mm x 20mm x 2mm is at one sides of the sample are exposed to a corrosive environment. Calculate corrosion rate in mm/y? M=65g/ mole, density-7.14g/cm³, I am-1.12 10 A/cm², 3.1536 x10 sec/year, n=2

(B) Sample of Zinc have dimensions 10mm x 20mm x 2mm is at one sides of the sample are exposed to a corrosive environment. Calculate corrosion rate in mm/y? M=65g/ mole, density-7.14g/cm³, I am-1.12 10 A/cm², 3.1536 x10 sec/year, n=2

World of Chemistry, 3rd edition

3rd Edition

ISBN:9781133109655

Author:Steven S. Zumdahl, Susan L. Zumdahl, Donald J. DeCoste

Publisher:Steven S. Zumdahl, Susan L. Zumdahl, Donald J. DeCoste

Chapter18: Oxidation–reduction Reactions And Electrochemistry

Section: Chapter Questions

Problem 35A

See similar textbooks

Similar questions

An aqueous solution of an unknown salt of gold is electrolyzed by a current of 2.75 amps for 3.39 hours. The electroplating is carried out with an efficiency of 93.0%, resulting in a deposit of 21.221 g of gold. a How many faradays are required to deposit the gold? b What is the charge on the gold ions (based on your calculations)?
An electrode is prepared from liquid mercury in contact with a saturated solution of mercury(I) chloride, Hg2Cl, containing 1.00 M Cl . The cell potential of the voltaic cell constructed by connecting this electrode as the cathode to the standard hydrogen half-cell as the anode is 0.268 V. What is the solubility product of mercury(I) chloride?
Chlorine, Cl2, is produced commercially by the electrolysis of aqueous sodium chloride. The anode reaction is 2Cl(aq)Cl2(g)+2e How long will it take to produce 2.00 kg of chlorine if the current is 5.00 102 A?
The following two half-reactions arc involved in a voltaic cell. At standard conditions, what species is produced at each electrode? Ag++eAgE=0.80VNi2++2eNiE=0.25V
An electrolysis experiment is performed to determine the value of the Faraday constant (number of coulombs per mole of electrons). In this experiment, 28.8 g of gold is plated out from a AuCN solution by running an electrolytic cell for two hours with a current of 2.00 A. What is the experimental value obtained for the Faraday Constant?
The mass of three different metal electrodes, each from a different galvanic cell, were determined before and after the current generated by the oxidation-reduction reaction in each cell was allowed to flow for a few minutes. The first metal electrode, given the label A, was found to have increased in mass; the second metal electrode, given the label B, did not change in mass; and the third metal electrode, given the label C, was found to have lost mass. Make an educated guess as to which electrodes were active and which were inert electrodes, and which were anode(s) and which were the cathode(s).
A potassium chloride solution is electrolyzed by passing a current through the solution using inert electrodes. A gas evolves at each electrode, and there is a large increase in pH of the solution. Write the half-reactions that occur at the anode and at the cathode.
A lead storage battery delivers a current of 6.00 A for one hour and 22 minutes at a voltage of 12.0 V. (a) How many grams of lead are converted to PbSO4? (b) How much electrical energy is produced in kilowatt hours?
An electrode is prepared by dipping a silver strip into a solution saturated with silver thiocyanate, AgSCN, and containing 0.10 M SCN . The cell potential of the voltaic cell constructed by connecting this electrode as the cathode to the standard hydrogen half-cell as the anode is 0.45 V. What is the solubility product of silver thiocyanate?
A metallurgist wants to gold-plate an object with a surface area of 17.21 in2. The gold plating must be 0.00200 in. thick (assume uniform thickness). (a) How many grams of gold (d=10.5g/cm3) are required? (b) How many minutes will it take to plate the object from a solution of AuCN using a current of 7.00 A? Assume 100% efficiency.
A solution contains the ions H+, Ag+, Pb2+, and Ba2+, each at a concentration of 1.0 M. (a) Which of these ions would be reduced first at the cathode during an electrolysis? (b) After the first ion has been completely removed by electrolysis, which is the second ion to be reduced? (c) Which, if any, of these ions cannot be reduced by the electrolysis of the aqueous solution?
In some old European churches, the stained-glass windowshave so darkened from corrosion and age that hardly anylight comes through. Microprobe analysis showed that tinycracks anddefects on the glass surface were enriched ininsoluble Mn(III) and Mn(IV) compounds. From AppendixE, suggest a reducing agent and conditions that might successfullyconvert thesecompounds to soluble Mn(II) withoutsimultaneously reducing Fe(III) (which gives the glassits colors) to Fe(II). Take MnO2 as representative of theinsoluble Mn(III) and Mn(IV) compounds.