A tensile test is performed on an aluminum specimen 10 mm in diameter using a gauge length of 50 mm. When the tensile force, F, reaches a value of 20 kN, the distance between the gage marks increases by 0.122 mm. Point out whether the specimen diameter decreases or increases if the Poisson's ratio is 0.34.

A tensile test is performed on an aluminum specimen 10 mm in diameter using a gauge length of 50 mm. When the tensile force, F, reaches a value of 20 kN, the distance between the gage marks increases by 0.122 mm. Point out whether the specimen diameter decreases or increases if the Poisson's ratio is 0.34.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The diagram shows a plot from an uniaxial test of an unknown metal. The uniaxial tensile test specimen had an original cross-sectional radius of 3.0 mm, an initial gauge length of 42 mm. At failure, the cross-sectional radius was 1.2 mm. Determine the yield strength of the unknown metal and the true stress at failure.
Annealed low-carbon steel has a flow curve with strength coefficient = 80,000 lb/in2 and strain-hardening exponent = 0.25. A tensile test specimen with gage length = 2.0 in is stretched to a length = 3.5 in. Determine the flow stress and average flow stress that the metal experienced during this deformation. use correct stratgy and correct E 0.55962
Draw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking region
Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…
When the diameter of a specimen subjected to a twist test increases, the shear stress increases. Select one: O a. False O b. True
A piece of steel rebar is tested in tension to determine its mechanical properties. The length of the sample is 87.3 mm and the cross-sectional area is 52.1 mm². When stretched by 37.2 mm, the force measured is 14,884 N. At this point, the graph is non-linear, but no clear neck is visible. If the Poisson's ratio of the material is 0.281, calculate the cross-sectional area (mm²) at this point.
Load (N) Elongation (mm) In a tensile test of stainless steel, the following data were obtained: 7,200 11,250 13,500 16,200 18,900 20,200 20,700 13,200 24.90 0.0 0.505 2.03 5.08 10.16 15.24 21.80 The dimensions of the cylindrical specimen were initial length L₁= 50.8 mm and initial area A₁ = 35.8 mm² and the area at fracture was Ar = 10.0 mm². Plot the stress-strain diagram and determine the following: a) Modulus of elasticity b) The yield strength at a strain offset of 0.002 c) Ultimate strength d) Fracture strength
A tension test was performed on a specimen having an original diameter of 13.7 mm and a gauge length of 50 mm. The data are listed in the table. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Redraw the linear-elastic region, using the same stress scale but a strain scale of 20 mm = 0.001 mm/mm. From the diagram, determine approximately the modulus of elasticity. Express your answer to three significant figures and include the appropriate units. E = Submit Part B συ = Submit Part C ☐☐ μÅ of = Value Determine the ultimate stress. Express your answer to three significant figures and include the appropriate units. Request Answer μĂ Value Request Answer Units μĂ - Value Units Determine the fracture stress. Express your answer to three significant figures and include the appropriate units. ? Units ? ?
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 152 kN. - Length of the specimen is 20 mm. - The yield strength is 86 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 10 kN, iv) Young's Modulus if the elongation is 2.2 mm at 10 kN and (v) Final diameter if the percentage of reduction in area is 28 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm) Answer for part 7
a. Let the tensile stress in a tension test be σ and the shear stress in a torsion test be τ. Draw a stress Mohr circle for each test (let the specimen axis, i.e. longitudinal direction, be x-axis and the transverse direction be y-axis) and express both the maximum principal stress (σmax) and the maximum shear stress (τmax) in terms of σ (for tension test) or τ (for torsion test). Mark the x-axis on the Mohr’s circle. Also indicate the directions of σmax and τmax with respect the x-axis for each case. Refer to your CE215 textbook.