I need handwritten otherwise I'll dislike your answer should match option A steel ship deck plate is 25 mmthick and 10 m wide. It is loaded witha nominal uniaxial tensile load thatfluctuates between 0 and 8000 kN.The plate has a fracture toughnessKịç equal to 28 MPa-m0.5. Determinethe number of loading cycles thatcan be endured if the initial surfacecrack has a length of 1.5 mm. Thevalues of the coefficient A and theexponent n are A = 5x1012 mm/cycleand n = 3. Assume B = 1.Select one:a. N = 8.43E+10b. N = 3.96E+10c. N = 2.89E+10d. N = 5.22E+10

Answered: Image /qna-images/answer/f749c3c0-2848-4ec9-8527-583b2df48114.jpg

A steel ship deck plate is 25 mm thick and 10 m wide. It is loaded with a nominal uniaxial tensile load that fluctuates between 0 and 8000 kN. The plate has a fracture toughness Kịc equal to 28 MPa-m0.5. Determine the number of loading cycles that can be endured if the initial surface crack has a length of 1.5 mm. The values of the coefficient A and the exponent n are A = 5×10-12 mm/cycle %3D and n = 3. Assume B = 1. Select one: a. N = 8.43E+10 b. N = 3.96E+10 c. N = 2.89E+10 d. N = 5.22E+10

A steel ship deck plate is 25 mm thick and 10 m wide. It is loaded with a nominal uniaxial tensile load that fluctuates between 0 and 8000 kN. The plate has a fracture toughness Kịc equal to 28 MPa-m0.5. Determine the number of loading cycles that can be endured if the initial surface crack has a length of 1.5 mm. The values of the coefficient A and the exponent n are A = 5×10-12 mm/cycle %3D and n = 3. Assume B = 1. Select one: a. N = 8.43E+10 b. N = 3.96E+10 c. N = 2.89E+10 d. N = 5.22E+10

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: I need answers for problems 1, 2, and 3 pertaining to the print provided.

A: As we are entitled to answer only a single question. We’ll answer question no. 1 for you. Please…

Q: What is a microcontroller? 1. General purpose device that can be programmed to carry out a finite…

A: Given question is related to electromechanical devices and controllers.

Q: Statics of Rigid Bodies Content Covered: - Method of Sections Direction: Create 1 problem based…

A: A simple truss is acted upon by two vertical forces acting at B and D, as shown. Compute to the…

Q: Determine the equivalent state of stress on an element at the same point oriented 60° clockwise with…

Q: Find the mass of the trash can. Assume IPS, set before you begin to sketch the part. The material is…

A: Given Data A=34.84 Material: PE High Density Find Find the mass of the trash.

Q: I need parts 3 and 4 answered pertaining to the print provided. I asked this question previously on…

A: (3) In the empty space of revision A9 a general note 3.6 is added stated that the revised geometric…

Q: ENTIRE ANSWER IS WRONG

A: Initial velocityFinal velocityInitial angleFinal angleWeight of the basketball

Q: I need answers for problems 1, 2, and 3 pertaining to the print.

A: 1. Yes. It is a part drawing of "BONNET SLEEVE".

Q: I need these 3 parts answered TRUE or FALSE.

A: During the life of any product, parts used for many years are replaced to improve the efficiency or…

Q: I need the answer for number 10.

A: Five Holes, each hole has diameter of 0.500 inches and the holes are equally spaced such that center…

Concept explainers

Engineering Drawing

Technical drawing has been around since ancient times. As in the ancient Renaissance, complicated drawings were created, including Leonardo da Vinci's drawing. Modern engineering drawing, including its specific orthographic projection with scale conventions, began in Europe (France) during the early stages of Industrialization. L.T. C. Rolt also made some of Marc's drawings for its block-making machinery (in 1799) that also may have contributed significantly to British engineering technology. Since he learned the art of presenting three-dimensional(3D) items in a two-dimensional(2D) plane, as we now term mechanical drawing. 

Question

I need handwritten otherwise I'll dislike your answer should match option

A steel ship deck plate is 25 mm
thick and 10 m wide. It is loaded with
a nominal uniaxial tensile load that
fluctuates between 0 and 8000 kN.
The plate has a fracture toughness
Kịç equal to 28 MPa-m0.5. Determine
the number of loading cycles that
can be endured if the initial surface
crack has a length of 1.5 mm. The
values of the coefficient A and the
exponent n are A = 5x1012 mm/cycle
and n = 3. Assume B = 1.
Select one:
a. N = 8.43E+10
b. N = 3.96E+10
c. N = 2.89E+10
d. N = 5.22E+10

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 4 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

A tensile specimen havign a diameter of 6 mm and a gauge length of 50 mm was tested to fracture and the stress-strain diagram is show. Poisson's ratio of material, v = 0.3 Determine the load P that the sample is subjected to when a stress of 300 MPa is applied. What is the instantaneous diameter of the sample given a longitudinal strain of 0.002?
Pls help ASAP
diagram and determine approximately the modulus of elasticity, the yield stress, the ultimate stress, and the fracture 2.00 in. The data is listed in the table. Plot the stress-strain 8-1. A tension test was performed on a steel specimen n original diameter of 0.503 in. and gage length of PROBLEMS *84. origi the f having an for t and stress. Use a scale of 1 in. Dodraw the elastic region, using the same stress scale but a 20 ksi and 1 in. = 0.05 in./in. strain scale of 1 in.= 0.001 in./in. Load (kip) Elongation (in.) 0. 0. 0.0005 0.0015 1.50 4.60 8.00 11.00 0.0025 0.0035 0.0050 11.80 11.80 0.0080 0.0200 12.00 16.60 0.0400 0.1000 0.2800 20.00 21.50 19.50 18.50 0.4000 0.4600 Prob. 8-1
Quick ans need in 1hr please
Determine the strength of the bedrock granite. Assume you sampled the granite where it was exposed at the surface and ran a series of 4 triaxial compression tests (results given below). Determine the Coloumb coefficient (or friction angle) and the cohesion of the rock given these test results. Either use graph paper to draw Mohr’s circles and a failure envelope to help you determine these values or use the computer to make a plot. Show all your work for credit! Test Confining pressure Axial load at failure 1 4.5 MPa 35.5 MPa 2 9 MPa 50 MPa 3 17 MPa 73 MPa…
A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the proportional limit. Stress (ksi) 40 30- 20 10- 0- 0.0 0.0 Upper scale 0.020 0.002 22 ksi O 15 ksi E 19 ksi O 10 ksi 13 ksi Lower scale- 0.040 0.060 0.080 0.100 0.004 0.006 0.008 0.010 Strain (in./in.) 0.120 0.012
The total load for a canopy overhang is 105,340# and the load is equally distributed to five steel rod ties. The sample steel rod tested has tensile strength of 20,000psi. A selection of steel rods (same material as the tested sample) is available in different sizes shown below. Select the rod size that best fits this application? (SA = Surface Area) (f= P/A) (LO4) O 1" (SA= 0.79 sq in) 3/4" (SA=0.44 sq in) O½" (SA= 0.20 sq in) O 1¼" (SA= 1.22 sq in) O 1½ (SA= 1.76 sq in)
A tensile test was conducted on a mild steel& the following data was obtained as follows. Diameter of the steel bar = 3 cm,Gauge length of the bar = 20 cm. Load at elastic limit = 250 kN . Extension at a load of 150kN = 0.21 mm . Maximum load = 380 kN . Total extension = 60 mm . Diameter of the rod at failure = 2. 25 cm Determine: (a) Young’s modulus (b) stress at elastic limit (c)the percentage of elongation (d) Percentage decrease in area.
A column made from cast iron has a cross section of A = 8272mm². On the column, a load of F = 667.4kN is acting. The compression strength of the material is σ = 355 N mm². Calculate the acting compressive stress for this case: (±0.5) N mm² What is the safety factor against fracture, if an actual compressive N stress of 198.08. is acting: mm² (±0.1)
A cylindrical pressure vessel of 2 m radius and 0.05 m wall thickness is manufactured from a steel with of 700 MPa and fracture toughness of 90 MPa m1/2. The internal pressure of the vessel during operation is expected to reach 0.75 MPa. Before the component is installed, a non-destructive testing (NDT) contractor reveals a flaw of depth 17 mm. Assess if the component is safe to be used. Use the ‘Plate in tension - through-thickness edge crack’ geometry in the K-calculator. You will need to calculate the hoop stress in the wall of the pressure vessel, assuming it to be a thin-walled cylinder. (6 marks) A safety-conscious engineer orders the flaw to be repaired. After repairing, NDT reveals that welding has introduced a new flaw, 6 mm in depth. It is assumed that as a result of welding, the residual stress in the region of the flaw is close to the yield strength of the steel. Will the vessel be safe to use in this situation? Explain how you come to your conclusion.
1. We can visualize the factor of safety for an arbitrary stress using a surface in principal stress space. For a ductile material that yields according to a von Mises criterion with a yield stress σy, sketch the von Mises surface in σ₁ - 02 space and sketch the stress surface that corresponds to a factor of safety FoS = 2. For a brittle material that yields according to a max normal (Rankine) criterion with a tensile strength Gyt and a compressive strength σvc = 20yt, sketch the yield surface and the surface that corresponds to a factor of safety FoS = 2.
show the FBD and complete solution