A sample of metal having a rectangular cross-section; a width of 10.00 in. and a thickness of 0.25 in. is cold worked to a final width of 9.50 and a thickness of 0.20 in. If the plastic behavior of this sample is given by o= 100,000€0.5 psi, determine the new yield strength of the sample after cold working. -

A sample of metal having a rectangular cross-section; a width of 10.00 in. and a thickness of 0.25 in. is cold worked to a final width of 9.50 and a thickness of 0.20 in. If the plastic behavior of this sample is given by o= 100,000€0.5 psi, determine the new yield strength of the sample after cold working. -

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Similar questions

A copper specimen subjected to the Brinell Hardness Test using hardened steel ball indenter of diameter 13 mm and the indentation diameter 3.78 mm is measured using an optical magnifying lens with a ruler. Draw the Brinell Hardness Test setup neatly and determine the force applied on the specimen. Take Brinell Hardness Number for copper as 1037. Surface Area of Indentation (in mm2) = Applied Force (in N) =
A 5-mm-thick rectangular alloy bar is subjected to ajtensile load P by pins at A and B, as shown in the figure. The width of the bar is w = 33 mm. Strain gages bonded to the specimen measure the following strains in the longitudinal (x) and transverse (y) directions: €, =710 με and ε,--255 με (a) Determine Poisson's ratio for this specimen. (b) If the measured strains were produced by an axial load of P = 24 kN, what is the modulus of elasticity for this specimen? Answers: (a) v= (b) E= GPa
For a material when tested within the elastic limit, the value of Poisson's ratio is 0.35. When the same material is tested in plastic stage, its Poisson's ratio in the plastic stage will be (a) 0.42 (b) 0.37 (c) 0.40 (d) 0.53
Please answer letters a, b, c and d. Thank you!
please send me a solution in detail. Thanks in advance
A ceramic sample with a rectangular section can support a load of up to 290 N under a common strength test for ceramics. Its flexural strength is then 78.3 MPa and the distance between support points is 45 mm. What would be the dimensions of this sample if its width were twice its height?
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 c) Calculate the fracture work and the maximum elastic energy the metal rod can store. d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12 tons of load with 2 times the safety of yield strength. How long does the rod extend under this load?
I In a compression test and for a very ductile material similar to copper , the diameter and the length of the specimen before the test were 60mm and 80mm respectively . Find the length , in inches , after the test if the diameter became 120mm . Assume that the density remained unchanged
On the basis of extensive tests, the yield point of a particular type of mild steel-reinforcing bar is known to be normally distributed with o = 100. The composition of the bar has been slightly modified, but the modification is not believed to have affected either the normality or the value of o. (a) Assuming this to be the case, if a sample of 81 modified bars resulted in a sample average yield point of 8417 lb, compute a 90% CI for the true average yield point of the modified bar. (Round your answers to one decimal place.) Ib (b) How would you modify the interval in part (a) to obtain a confidence level of 92%? (Round your answer to two decimal places.) |---Select-- v should be changed to
A Brinell hardness tester with a diameter of 10 mm and a load of 500 kg gives an impression with a diameter of 1.62 mm in a steel alloy. Calculate the Brinell hardness (HB) in the steel alloy
A ceramic specimen having a circular cross section of radius 2.7mm is subjected to a load of 900N. The distance between the support point is 43mm. Another test is to be performed on a specimen of this same material, but one that has a square cross section of 10mm on each edge. At what load (in N) would you expect the specimen to fracture if the support point separation is 38mm?
answer shortly