A ceramic rod tensile test is applied to the cylinders and the strain value during tensile is measured as 0.2%. Again, the change in diameter was measured as 0.04%. If the tension value measured at the time of break is (1000/5) MPa; a) Calculate the Elasticity module (E) of the ceramic? b) Calculate the poison ratio (v) of the ceramic? c) Calculate the shear modulus (G) of the ceramic.
A ceramic rod tensile test is applied to the cylinders and the strain value during tensile is measured as 0.2%. Again, the change in diameter was measured as 0.04%. If the tension value measured at the time of break is (1000/5) MPa; a) Calculate the Elasticity module (E) of the ceramic? b) Calculate the poison ratio (v) of the ceramic? c) Calculate the shear modulus (G) of the ceramic.
Related questions
Question
A ceramic rod tensile test is applied to the cylinders and the strain value during tensile is measured as 0.2%. Again, the change in diameter was measured as 0.04%. If the tension value measured at the time of break is (1000/5) MPa; a) Calculate the Elasticity module (E) of the ceramic? b) Calculate the poison ratio (v) of the ceramic? c) Calculate the shear modulus (G) of the ceramic.
Expert Solution
This question has been solved!
Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.
Step by step
Solved in 2 steps