Table Q2Steel(LowLow CarbonMedium CarbonHigh CarbonAlloys)(<0.25 wt% C)(0.25 – 0.6 wt% C)(0.6 – 1.4 wt% C)ТуреWithWithWithPlainPlainPlainPropertyAdditiveAdditiveAdditiveHardnessLowMediumMediumHighHighVery highDuctilityHighMediumMediumLowLowVery lowA mechanical properties table with different type of steels is shown in Table Q2.a) Based on Table Q2, describe the relationship of hardness and ductility.b) Suggest two methods to improve the hardness of steels by referring to Table Q2.c) Elaborate the reasons the two methods in Q2(b) can be used to improve the hardness of steels.

for solution refer below images.

a) Based on Table Q2, describe the relationship of hardness and ductility. b) Suggest two methods to improve the hardness of steels by referring to Table Q2. c) Elaborate the reasons the two methods in Q2(b) can be used to improve the hardness of steels.

a) Based on Table Q2, describe the relationship of hardness and ductility. b) Suggest two methods to improve the hardness of steels by referring to Table Q2. c) Elaborate the reasons the two methods in Q2(b) can be used to improve the hardness of steels.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Question 4 A segment of the Fe/C alloy phase diagram is shown below: Composition (at% C) 15 Temperature (°C) 0 1600 1400 1200 1000 800 600 400 1538°C 0 (Fe) 8 Y 912°C -1493 C 1394-C Y. Austenite 0.76 0.022 a, Ferrite 1 y+L 2 2.14 10 1147 C at Fe₂C L 4.30 Y+Fe3C 4 3 Composition (wt% C) 727°C 20 Cementite (Fe-C) 5 6 25 2500 2000 1500 1000 6.70 Temperature (°F) a) What are the equilibrium phases, compositions and relative fractions of the Fe-C alloy at an average composition Ccarbon of 2% and a temperature of 730 °C? b) What are the equilibrium phases, compositions and relative fractions of the Fe-C alloy at an average composition Ccarbon of 2% and a temperature of 725 °C? 7 c) Sketch the microstructure of the alloy obtained by quick cooling of the alloy from the conditions in part a) to the conditions in part b). Be sure to identify the phases in your sketch.
2. Calculate the stress in MPa retained in a metal due to shot peening, using the value of the slope indicated on the d vs. sin'y plot shown below. (1+v)/E=5.77x10-6 MPa¹; d₂-2.87179 Å Slope -0.010196 Å sin'y
Question 5: Following is tabulated data that were gathered from a series of Charpy impact tests on a tempered 4140 steel alloy. Temperature (°C) 100 75 50 25 0 -25 -50 -65 -75 -85 -100 -125 -150 -175 Impact Energy (J) 89.3 88.6 87.6 85.4 82.9 78.9 73.1 66.0 59.3 47.9 34.3 29.3 27.1 25.0 (a) Plot the data as impact energy versus temperature. (you can use Excel or other software). (b) Determine a ductile-to-brittle transition temperature as that temperature corresponding to the average of the maximum and minimum impact energies. (c) Determine a ductile-to-brittle transition temperature as that temperature at which the impact energy is 70 J.
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Question 1 1.1. Given the data in the table below for Au and Ag, which material is more likely to form vacancies at any given temperature and why? Show all calculations. Ag 3.5 x 1024 3.6 x1023³ Au Nv (m-³) T (°C) A (g/mol) 196.3 p (g/cm³) 18.63 900 800 107.9 9.5
The properties of some very ductile metals, such as certain low- carbon steels, change at low temperatures at their particular transition zone. How can this information help an engineer design machinery that will be operating in subzero temperatures?
6.8 Suppose that a cast Al-1 wt% Si alloy, contains equilibrium Si particles 1 µm in diameter. This alloy is to be heat treated by first putting all of the Si particles back into solution. (a) Draw a set of schematic curves indicating what will happen during this process. Temperature °C (b) Indicate the initial conditions, the final conditions (once a new equilibrium is reached) and the boundary conditions during dis- solution. (c) Estimate how long the alloy should be held at 550°C so as to ensure that all of the Si is dissolved. Al-Si 1500 1300 1100 900 700 500 300 660.452°C 0 -(A1) 10 AI 12.6 10 20 20 30 30 Atomic Percent Silicon 40 50 Thom L 60 Them 577+1°C 40 50 60 Weight Percent Silicon 70 70 80 80 90 90 100 1414°C (Si)- 100 Si
What is the basis of all calorimeter calculations for specific heats of materials? Can someone please answer? I don't know how the question is worded.
Composition lat% N 40 60 100 1600 2800 1500 1453 C 2600 Liquid 1400 Solidus line Liquidua line 2400 1300 1200 2200 1100 1085 C 2000 1000 20 40 100 Composition (wt N (NO What is the amount for each phase in 1kg of a 50% Ni-50% Cu alloy at temperatures of 1400, 1300, or 1200 degrees C for point A and point B? Temperature ('C) Temperature ("F)
Consider the graph below for 3 metals which have been cold-worked. From the graphs, which of the following statements are true? Stress o Select one or more: □ c. Strain & A e. B a. B and C have similar hardness; C has greater brittleness b. B is softer than C and has nearly similar ductility A is harder than C and is more ductile C d. B is harder than C but has nearly similar ductility A is harder than C and is less ductile f. A and B have similar hardness; A has greater brittleness
2. The dameter of a bar abricaled from an allay wlth properties showa in figure below redaced fromm an inltial 1.2 in to a 1.0 In diameler, to a final 1.8 in. diameter. For parts a, b. and when using the graph, you can ignore the marked paints A. B. C, and O 0) Determine the % CW nfter the first step of the process b) Determine the yield stress (in ksi) after the first step of the process t) Determine the % CW after the second step of the proces 22 Tensile srengin (ks 20 18 Yicld strength s) 16 14 10 Elongatie () Percent cold ssok
1) Draw the iron-Fe;C phase diagram. Consider 0.25 and 1.1 wt% C steel alloy. It is cooled slowly from atemperature within austenite phase to room temperature. Show a) microstructure at 1000 °C b) microstructure at 730°C c) microstructure at 715°C and d) microstructure at room temperature e) What do you say about mechanical properties of these alloys, depending on their microstructure at room temperature?