6.70 (Fe) Composition (wt% C) Compute the composition of an iron-carbon alloy for which the mass fractions of total ferrite and total cementite are 0.87and 0.13, respectively. a. Co What is the proeutectoid phase for the alloy in problem 1? a. No proeutectoid phase b. Ferrite c. Cementite

6.70 (Fe) Composition (wt% C) Compute the composition of an iron-carbon alloy for which the mass fractions of total ferrite and total cementite are 0.87and 0.13, respectively. a. Co What is the proeutectoid phase for the alloy in problem 1? a. No proeutectoid phase b. Ferrite c. Cementite

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Describe experimental procedure to obtain a binary isomorphic phase diagram for metals A and B by stating the equipment and materials you need? Show typical micrographs at 3 different phase regions for the alloy 50% A and 50% B on the phase diagram you obtained
cover the manufacturing and loading of an NiCu bar. The bar has a 0.01 m x 0.01m cross-section and is 1m long. The alloy is 60% (at%) Ni and 40% (at%) Cu.
HOME WORK Calculate the amounts of solid phases of ferrite and cementite present in pearlite. y+ FegC a + Fe;C 6.70 0.022 0.76 Composition (wt % C) Temperature
Determine the fraction of eutectoid cementite with 0.84 wt.% C in the iron-carbon alloy.
1. Figure 1 shows copper-nickel piping on a marine chemical tanker. As an inspection engineer, one day you were called to inspect a corrosion problem that occur on surface of the pipe. From microstructural investigation, you find out that the corrosion problem is caused by composition variation across the grain as shown in 2. Using phase diagram given, rationalise this microstructure. Your explanation should include why there are two shades of grey colour in the microstructure and what are their compositions? You are free to choose which ever copper-nickel system (example 80% Cu – 20% Ni) you like from the phase diagram. Figure 1 0% Ni 25% Ni 50% NI 75% Ni 100% N 1500 Liquid °C 1400 1330°C 1300 Liquidus jihe 1290°C 1200 LAS Soligus line 1100 400um Solid 1000L 100% Cu 75% Cu 25% Cu 50% Cu 0% Cu Figure 2 2. you have been introduced to one type of annealing heat-treatment, which is process-annealing also known as subcritical annealing. But there are a lot of other type annealing process…
Consider a Fe-0.5% C alloy. What is the amount of pro eutectoid phase (in percentage ) just above the eutectoid temperature
Help please
T or F -In the hypereutectoid steel alloy, the primary phase is Cementite ( iron carbide ) -In the Pb-Sn hypoeutectic alloy, the primary phase is the α-phase -The eutectic composition of the solder alloy is 98%wt Sn -In the steel alloys, the weight percent of the alloying elements affects the eutectoid temperature and Ceutectoid wt%C -Austenite phase has a BCC crystal structure The microstructure is characterized by: a.The number of phases present b.The present phases’ proportions. c.How these phases are arranged or distributed d.all of the answers
A 10 30 70 1) For an A-B alloy of composition 25 wt% B (i) Draw the microstructure at T (just above the eutectoid temperature) and calculate the fraction of each phase in the microstructure. (ii) Draw the microstructure at T (just below the eutectoid temperature) and determine the amount of each phase, i.e., fraction of proeutectoid alpha, eutectoid alpha and eutectoid beta. 2) Provide a brief summary of phase transformations which are often observed in the iron-carbon alloy system due to various heat treatment procedures carried out to tune the microstructure. Compare mechanical strength and ductility of the materials/microstructures that form as a result of such heat treatment processes.
Answer the 5 questions briefly
From the phase diagram of the Fe-0.25wt%C alloy below, determine the phase fraction and elemental composition of the resulting phase immediately after solidification across the eutectoid line (725 C). a.alpha_eutectoid = 96.6 wt% and cementite = 29.85 wt% b.alpha_eutectoid = 96.6 wt% and cementite = 3.4 wt% c.alpha_eutectoid = 1.05 wt% and cementite = 29.85 wt% d.alpha_eutectoid = 29.85 wt% and cementite = 1.05 wt%