3. Consider a test specimen with the shape of cylindrical rod, 120 mm long to be deformed by tensile load of 28000 N without experiencing plastic deformation or diameter reduction more than 8.5x10-3 mm. Which among the aluminium alloy, brass alloy, steel alloy and titanium alloy are possible candidates with yield strengths 200 MPa, 300 MPa, 400 MPa and 650 MPa, respectively.

3. Consider a test specimen with the shape of cylindrical rod, 120 mm long to be deformed by tensile load of 28000 N without experiencing plastic deformation or diameter reduction more than 8.5x10-3 mm. Which among the aluminium alloy, brass alloy, steel alloy and titanium alloy are possible candidates with yield strengths 200 MPa, 300 MPa, 400 MPa and 650 MPa, respectively.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In designing a ceramic part for a jet engine, to ensure that the part does not fail, we plan to ensure that the maximum applied stress is only one-third of the yield strength. The yield strength of this CMC part for a jet engine is 520 MPa, and its plane strain fracture toughness is 5.5 MPa√?. We utilize a nondestructive test to find any internal faults that are longer than 1.27 mm. Does our non-destructive test have the requisite sensitivity if Y = 1.4? Explain.
Attempt only if you are sure Urgent.
A high-strength steel has yield strength of 1165 MPa and fracture toughness of 95 MPavm. Calculate the size of an internal crack that will lead to catastrophic failure at an applied stress of 80% yield strength. (Y = 1.00 for internal crack, and Y=1.12 for surface crack)
Is the maximum normal stress theory useful to predict the accurate failure of brittle material?
could you answer the question please ?
I need the answer as soon as possible
(b) A 12.8 mm diameter rod and gauge length of 40 mm of aluminum alloy is pulled to failure in a tensile test. If final diameter of the rod fracture surface is 10.8 mm and fracture gauge is 64 mm, answer the following: (i) Calculate the ductility in percent reduction in area of the sample. (ii) Explain how ductility is related to the toughness of the material.
The mechanical properties of a material can be determined by a simple strees strain test. Explain THREE (3) types of test that mostly conducted for metals at room temperature. Support your answer with the diagrams of material after deformation.
Case Study Calculate the Tensile Toughness Tensile toughness measures the total energy absorbed prior to fracture and is different from fracture toughness and impact toughness. Fracture toughness measures the resistance to fracture when a flaw (i.e. crack) is present in the material. Since it is nearly impossible and costly to manufacture materials with zero or near zero defects, fracture toughness is a major consideration for all structural materials. Impact toughness measures a materials ability to withstand an impact blow (i.e. high strain rates) and is particularly important in assessing the ductile-to-brittle transition behavior (more details later). Impact toughness is also commonly referred to as notch toughness. The tensile toughness can be estimated using the stress-strain curve by measuring the area under the curve (both the elastic and plastic regions). Tensile Toughness = f Stress, σ Ty- Ey Efracture ETS Ur Ey Efracture o de = U₁ + SETS o de + Sefracture o de Ey Ey o de =…
An annealed-steel specimen has a 0.750 in. diameter and a 12.000 in. gage length. Maximum load is reached at 60,000 lbs and fracture occurs at 30,000 Ibs. For this steel, E= 360 x 10° psi. (a) Draw a sketch of stress-strain diagram for a typical steel in tension? (b) What is the ultimate tensile strength (UTS)? (c) Why does fracture occur at a lower load than the maximum load? (d) What is the elongation when a tensile stress of 30,000 psi is applied? A 400-mm-long rod with a diameter of 4.5 mm is loaded with a 5000-N weight. If the diameter decreases to 3.5 mm, compute the final length of the rod. 3. 4. A steel rod 1.5 m long and 75 mm x 75 mm in cross-section is subjected to a tensile force of 160 kN. Determine the elongation of the rod, if modulus of elasticity for the rod material is 900 GPa. 5. A hollow cylinder 4.5 m long has an outside diameter of 80 mm and inside diameter of 60 mm. If the cylinder is carrying a load of 75 kN, find the stress in the cylinder. Also find the…
A steel rod specimen with a diameter of 200mm was subjected to a force 5000 N in the stress-strain experiment, if the area of the rod at fracture was 25434 mm^2, determine the percentage of the sample ductility (RA).
Draw the stress strain diagram for a ductile and brittle material and what is the difference in it? What do you understand by strain hardening? What do you mean by percentage reduction in area? Explain the steps in ductile fracture. Explain the modes of failure in tension test.