3. Calculate the number of atoms per cubicmeter for metal X at 830 C. The energy forvacancy formation is 2.9 eV/atom; the atomicweight and density for Metal X are 87.3 g/moland 10 g/cm3, respectively. Answer inScientific Notation example 1.3e+28.4. Calculate the equilibrium number ofvacancies per cubic meter for metal X at544C. The energy for vacancy formation is 0.5eV/atom; the atomic weight and density forMetal X are 46.5 g/mol and 5 g/cm3,respectively. Answer in scientific notation.Round your answer to 2 significant figures.

3. Calculate the number of atoms per cubic meter for metal X at 830 C. The energy for vacancy formation is 2.9 eV/atom; the atomic weight and density for Metal X are 87.3 g/mol and 10 g/cm3, respectively. Answer in Scientific Notation example 1.3e+28.

3. Calculate the number of atoms per cubic meter for metal X at 830 C. The energy for vacancy formation is 2.9 eV/atom; the atomic weight and density for Metal X are 87.3 g/mol and 10 g/cm3, respectively. Answer in Scientific Notation example 1.3e+28.

Principles of Modern Chemistry

8th Edition

ISBN:9781305079113

Author:David W. Oxtoby, H. Pat Gillis, Laurie J. Butler

Publisher:David W. Oxtoby, H. Pat Gillis, Laurie J. Butler

Chapter22: Inorganic Materials

Section: Chapter Questions

Problem 44AP

See similar textbooks

Similar questions

Data are given in Appendix 1 for white phosphorus, P4(s). P4(g) has the following thermodynamic values: Hf=58.9kJ/mol , S=280.0J/kmol . What is the temperature at which white phosphorus sublimes at 1 atm pressure?
Are all alloys homogeneous solutions? Explain your answer.
Calculate the energy (in eV/atom) for vacancy formation in some metal, M, given that the equilibrium number of vacancies at 343oC is 9.39 × 1023 m-3. The density and atomic weight (at 343°C) for this metal are 7.75 g/cm3 and 142.6 g/mol, respectively.
The following information is given for antimony at latm: boiling point = 1440 °C AHvap(1440 °C) = 195 kJ/mol melting point = 631 °C AHfus(631 °C) = 19.6 kJ/mol specific heat solid= 0.209 J/g°C specific heat liquid= 0.259 J/g°C What is AH in kJ for the process of freezing a 29.9 g sample of liquid antimony at its normal melting point of 631 °C. kJ
Calculate the change in the enthalpy when 52.0 g of solid chrominium at 25*C and 1 atm pressure is oxidized. (Delta Hf for Cr2O3(s) is -1135 Kj/Mol.) 4Cr(S) +3 O2(g) = 2Cr2O3 (s). A. -1135 B. -284 Kj C. -568 Kj D. 1135 Kj E. 568 Kj
5. Atomic radius, crystal structure, electronegativity, and the most common valence are given in the follo table for several elements; for those that are nonmetals, only atomic radii are indicated. Crystal Structure FCC Element Ni Atomic Radius (nm) 0.1246 Electronegativity 1.8 Valence 0.071 H 0.046 0.060 0.1445 0.1431 0.1253 0.1249 FCC 1.4 1.5 1.7 1.6 +1 Ag Al Co FCC HCP BCC +3 +2 +3 Cr Fe Pt Zn 0.1241 0.1387 ВСС FCC 1.7 1.5 +2 +2 0.1332 HCP 1.7 +2 Which of these elements would you expect to form the following with nickel: (a) A substitutional solid solution having complete solubility (b) A substitutional solid solution of incomplete solubility (c) An interstitial solid solution
2. Calculate the number of vacancies per cubic meter in iron at 850°C. The energy for vacancy formation is 1.08 eV/atom. The density and atomic weight for Fe are 7.65 g/cm and 55.85 g/mol, respectively.
The rutile and fluorite structures, shown here (anions arecolored green), are two of the most common structure typesof ionic compounds where the cation to anion ratio is 1 : 2.(a) For CaF2 and ZnF2 use ionic radii, Ca2+ (r = 1.14 A° ),Zn2+ (r = 0.88 A° ), and F- (r = 1.19 A° ), to predict whichcompound is more likely to crystallize with the fluoritestructure and which with the rutile structure. (b) What arethe coordination numbers of the cations and anions in eachof these structures?
alloys are prepared with a view to impart some desirable properties. what are these properties?
Calculate the equilibrium number of vacancies per cubic meter for copper at 1000° C. The energy for vacancy information is 0.90 eV/atom and the total number of atomic sites is 8.64x1028 atoms/m3.
Safari 7:34 AM Sun Oct 1 Patterns in Natur...ule 3 assignment 2 Home LE Calibri Bold Italic (E Patterns in Nature Module 3 Assignment 1. Why is glass not a mineral? Insert Draw Layout Review View References BI ●●● U aA 2. Describe several ways in which minerals can form. Directions: Answer each question as thoroughly as possible. Please make sure all of your answers are in your own words. 3. Name two different patterns of crystal growth. Define each one. ili 4. What is a geode? Which type of crystal growth do geodes exhibit? ㅁㅇ =✓ 5. If a mineral is very hard, which type of chemical bonds would that mineral most likely have in its atomic structure, and why? A 19% 0 :
5. The table below shows the elements in the third period of the Periodic Table, the number of electrons in their outer energy level, their oxidation state in their common compounds and their melting points. element Na Mg Al Si P. CI Ar number of outer electrons 1 2. 4 7. 8. oxidation state +1 +2 +3 +4/-4 -3 -2 -1 melting point/°C 98 650 660 1414 317 115 -101 -189 Describe why silicon have significantly high melting point 1) The no of outer electron will affect the effective nuclear charge. Explain il) ilI) Iv) how effective nuclear charge can cause the decreasing the atomic size Explain why Na, Mg and Al are good conductors of electricity. Which element exists as diatomic molecules of the type X2?