1.6-2 A round bar of 10 mm diameter is made of alu- minum alloy 7075-T6 (see figure). When the bar is stretched by axial forces P, its diameter decreases by 0.016 mm. Find the magnitude of the load P. (Obtain the mate- rial properties from Appendix H.)

1.6-2 A round bar of 10 mm diameter is made of alu- minum alloy 7075-T6 (see figure). When the bar is stretched by axial forces P, its diameter decreases by 0.016 mm. Find the magnitude of the load P. (Obtain the mate- rial properties from Appendix H.)

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: An aluminum alloy [E = 73 GPa; v = 0.33; a= 23.0 x 10-6/°C] plate is subjected to a tensile load P.…

Q: 2. The tensile link shown is flat, is 5 mm. thick, and carries an axial loac a. Compute the maximum…

A: GIVEN- Axial load (P)=1350 N Thicknesss (t)= 5 mm

Q: A Sandwich block is comprised of brass in the centre with two aluminium plates attached to either…

Q: For the two element rod shown, element (1) is steel with: E₁ = 210 GPa, A₁ = 1000 mm², L₁= 2 m, and…

A: Given A two element rod having temperature increase of 100 °c Required Stress in both rod…

Q: 25 mm PROBLEM 2.49 Brass core The aluminum shell is fully bonded to the brass core and the assembly…

Q: A round aluminum alloy rod has a diameter of 12.5 mm and 1 m length. Its ultimate strength is 155…

A: Given:- Diameter of the round aluminum alloy rod = 12.5 mm Length of the aluminum rod = 1 m…

Q: Calculate Poisson's Ratio for a steel that has a modulus of elasticity E of 30,000,000 psi and a…

A: The given data is: Modulus of elasticity, E=30000000 psi Modulus of rigidity, G=11500000 psi

Q: Beam CX is subjected to a loading condition as shown in the figure. What will be the (a) the maximum…

Q: Question 1: The rubber band given below is subjected to the following tensile loading. Calculate the…

A: Allowable tensile strength of rubber, Allowable shear strength of steel, Tensile force, Width of…

Q: The temperature of the cylindrical rod is heated to 45°C which is fixed in between A and C rigid…

Q: 8 ksi, øy = -4 ks The normal stresses at a point in a steel member are ox 10 ksi. Using E = 29 × 10³…

A: Given data in question Stresses Elasticity modulus Poissons ratio To find out Normal strains

Q: An aluminum alloy [E = 72 GPa; v = 0.33; a= 23.0 x 10-6/°C] plate is subjected to a tensile load P.…

Q: When the normal stresses are at their maximum or minimum values, the shear stresses are zero. We can…

A: 1- Yes when normal stresses are maximum or minimum, then at that element shear stress is zero. 2-…

Q: 1. Copper bar shown calculate the stresses when the temperature drop from 85 °C to 50 °C. a =…

A: *Multiple questions* As per our guidelines we are supposed to answer?️ only one question. Kindly…

Q: An aluminium wire (E=10,600 ksi) having a diameter d%-1/8 inch. and length L=14 ft is subjected to a…

Q: The aluminum shell is fully bonded to the brass core, and the assembly is unstressed at a…

A: Given Data:Temperature of 78°FChange in Temperature = 210°FBrass…

Question

100%

1.6-2 A round bar of 10 mm diameter is made of alu-
minum alloy 7075-T6 (see figure). When the bar is stretched
by axial forces P, its diameter decreases by 0.016 mm.
Find the magnitude of the load P. (Obtain the mate-
rial properties from Appendix H.)
P
PROB. 1.6-2
7075-T6
d = 10 mm
P

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step 3

VIEW

Step by step

Solved in 3 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

A steel component is subjected to alternate cyclical loading. The steel follows Basquin's law for high cycle fatigue, o, x N = C, (where the stress amplitude is in MPa). Ignore the geometric detail and assume that Marin's modifying factors are all equal to 1. You are given the minimum stress ain = -213 MPa, the maximum stress omax = 213 MPa. The material data are Tensile strength oUTS = 539 MPa, Basquin's constant c, = 875 MPa, Basquin's exponent a = 0.085. a) Calculate the stress ratio R, the stress amplitude o, in MPa and the mean stress am in MPa. The answers are acceptable with a tolerance of 0.01 for R and of 1 MPa the stresses. R: MPa MPа b) Calculate the corresponding life, in 10° cycles, (tolerance of 0.1 106 cycles) N :
Problem 1 An axial force of P is applied to the center of the rigid end plate shown below. If the portion of the load carried by the aluminum plates is half the portion of the load carried by the brass core, (a) determine the value of h, (b) the total load if the stress in the brass is 50 MPa. Brass core (E = 105 GPa) Aluminum plates (E = 70 GPa) Rigid end plate 300 mm 60 mim 40 mm
Two steel plates are connected by a pair of splice plates with eight bolts as shown. The ultimate strength of the bolts is bolts is 270 MPa. An axial tension load of P = 480 kN is transmitted by the steel plates. If a factor of safety of 1.6 with respect to failure by fracture is specified, determine the minimum acceptable diameter "d" for the bolts. %3D P. splice plate steel steel plate plate (2) (1)
The solid rod has a diameter of 20mm. Find the following: Angle of twist at C with respect to A (in radians) Angle of twist at B with respect to A (in radians) Maximum shear stress at A (in MPa) (Shear stress at support, at a point 7mm from center. (in MPa) A-36 steel with the following properties: Modulus of Elasticity, E = 29x10^3 ksi or 200 GPa Shear Modulus/Modulus of Rigidity, G = 11.5x10^3 ksi or 79.3 GPa Poisson's Ratio, nu = 0.260 Temperature Coefficient for thermal expansion, a = 6.6x10^-6/°F or 11.7x10^-6/°C
(b) (ii) A 20 mm diameter rod made from 0.4% C steel is used to produce a steering rack. If the yield stress of the steel used is 350 MPa and a factor of safety of 2.5 is applied, what is the maximum working load that the rod can be subjected to? 2