01: Consider a unidirectionally reinforced glass fiber/epoxy composite. The fibers are continuous and 60% by volume. The tensile strength of glass fibers is 1 GPa and the Young's modulus is 70 GPa. The tensile strength of the epoxy matrix is 60 MPa and its Young's modulus is 3 GP i. Compute the Young's modulus of the composite in the longitudinal and transverse directions. ii. Compute the tensile strength of the composite in the longitudinal direction. iii. Plot the longitudinal Young's modulus and the transverse Young's modulus diagram of the composite.

01: Consider a unidirectionally reinforced glass fiber/epoxy composite. The fibers are continuous and 60% by volume. The tensile strength of glass fibers is 1 GPa and the Young's modulus is 70 GPa. The tensile strength of the epoxy matrix is 60 MPa and its Young's modulus is 3 GP i. Compute the Young's modulus of the composite in the longitudinal and transverse directions. ii. Compute the tensile strength of the composite in the longitudinal direction. iii. Plot the longitudinal Young's modulus and the transverse Young's modulus diagram of the composite.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Original question: The nominal engineering constants of a unidirectional graphite epoxy ply are given in Table below for a fiber volume fraction of 60 percent. The fiber volume is reduced to 55 percent. Estimate the engineering constants for this reduced fiber volume fraction. New question needing to be answered: Repeat with a reduced fiber volume fraction of 40 percent representative of lower fiber volume fraction materials. Table:
I need handwritten Or else dislike and all parts lease I'll rate then
Compute the ultimate strength for a composite which uses Aramid fibers and Polyester matrix. The volume fraction of fibers is 45 % and matrix is 55 %.
Explain the relationship between STRUCTURE/ PROPERTIES/ PROCESSING/ PERFORMANCE of a polymer which is a drawn fiber thermoplastic. You should have at least a sentence for each of these.
An epoxy (E=2.7GPA) is reinforced with carbon fiber with module of elasticity equal to 260 GPa. Design a composite with a longitudinal elastic modulus of 160 GPa. Select one: a. Vm = 70 vol%, Vf = 30 vol% b. Vm = 40 vol%, Vf = 50 vol% C. Vm = 39 vol%, Vf = 61 vol% d. Vm = 62 vol%, Vf = 38 vol%
A composite with a minimum elastic modulus of 50 GPa is to be created by mixing uniaxial epoxy with metal fibre. Calculate the minimum Elastic modulus of the metal fibre given the following data for the epoxy matrix: Elastic modulus of the epoxy matrix is 5 GPa • Volume fraction of the epoxy matrix is 0.6 A- в I U S x2 x
Question 2 = 219,48 M//a = 247,3785 Pa 2.1 Consider a polymer reinforced with Spectra 1000 fibers, with a fiber volume ratio of x = 15 %. For a cross sectional area of 130 mm² and a load of 250 kg, calculate the stress in the fibers and in the matrix if the matrix material is polycarbonate. 2.2 Why are fibres capable of supporting a large portion of the tensile load in composite materials?
Q5 (a) Figure 6 shows two types of polymeric products fabricated using different processing techniques. Suggest with justification for the type of processes used to produce the products: i. Product A ii. Product B A B Figure 6. Two types of polymeric products (a) plastic bottles and (b) plastic car boot tray (b) The molecular weight data of a Polymer X are given in Table 3. Once undergone a melting process, it achieves degree of polymerization, DP of 498 upon solidification. i. Calculate the number-average molecular weight (Mn) for the polymer. ii. Calculate the molecular weight for monomers of the Polymer X. iii. Prove that the Polymer X is a polytetrafluoroethylene (PTFE) with chemical formula of (C2F4)n- Given the atomic weights for carbon, C is 12.011 g/mol and fluorine, F is 18.998 g/mol.
There are 4 classifications of structural molecular characteristics of polymers - Linear, Network, Crosslinked. What is the final type? Answer:
Need correctly.
Steel wires are used to reinforce the matrix in the thermoplastic polymers. Select one: True False