A continuous and aligned fiber-reinforced composite having a cross-sectional area of 1200 mm² is subjected to an external tensile load. If the stresses sustained by the fiber and matrix phases are 152 and 2.27 MPa, respectively, the force sustained by the fiber phase is 72300 N, and the total longitudinal strain is 0.00143, determine the following: (a) The force sustained by the matrix phase (in N). (b) The modulus of elasticity of the composite material in the longitudinal direction (in GPa). i N i (c) The modulus of elasticity for the fiber phase (in GPa). GPa i GPa (d) The modulus of elasticity for the matrix phase (in GPa). GPa

A continuous and aligned fiber-reinforced composite having a cross-sectional area of 1200 mm² is subjected to an external tensile load. If the stresses sustained by the fiber and matrix phases are 152 and 2.27 MPa, respectively, the force sustained by the fiber phase is 72300 N, and the total longitudinal strain is 0.00143, determine the following: (a) The force sustained by the matrix phase (in N). (b) The modulus of elasticity of the composite material in the longitudinal direction (in GPa). i N i (c) The modulus of elasticity for the fiber phase (in GPa). GPa i GPa (d) The modulus of elasticity for the matrix phase (in GPa). GPa

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: A 30-mm-diameter popper rod is 1 m long with a yield strength of 70 MPa. Determine the axial force…

A: Given data Diameter = 30 mm Length = 1m Yield strength = 70 Mpa

Q: P2. Design a cylindrical thin-wall composite fuselage for storing compressed natural gas at a…

Q: Using the aid of a diagram, describe the behaviour stress vs strain of a brittle polymer. Give one…

A: Polymer is known for its inherent toughness and resistance to fracture .mechanical properties of…

Q: There are a variety of models that can be used to describe viscoelastic behaviors. In which of the…

A: Viscoelasticity is the property where a material behaves like both liquid as well as solid. When a…

Q: A discontinuous fibre reinforced composite consists of 20mm long carbon fibres in a polymer matrix.…

A: Given: Fiber length: L = 20 mmVolume fraction of the composite: Vf = 0.5Interfacial shear strength:…

Q: 4. If the thickness and width of the dog bone for PP are 0.12" and 0.5", respectively, and the…

Q: For safe and reliable operation, a certain polypropylene pipe must withstand an internal pressure of…

Q: A new rigid biomaterial is developed and tested as a candidate replacement tissue for volumetric…

A: In conclusion: Given the anisotropic character of the material, the elastic moduli (E11, E22, E33)…

Q: Assume that Young's modulus for bone is 1.5x10^10 N/m2 and that a bone will fracture if more than…

Q: Please don't provide handwritten solution ....

A: Given below solution-Explanation:

Q: a) A climber relies on a safety rope swing hung from a large cliff face. The diameter of the…

A: Given: The diameter of rope. d = 8.5 mm The tensile strength of rope = 138 MPa The factor of safety,…

Q: A sample of cross-linked natural rubber (polyisoprene) is found to have a shear modulus of 100 kPa…

Q: A tensile force of 200 KN is applied on a 0.02-m diameter and.2-m long rod. After applying the load,…

Q: At an axial load of 22 kN, a 15-mm-thick x 35-mm-wide polyimide polymer bar elongates 4.6 mm while…

A: Given data: Axial load: F = 22 kN Thickness of the bar: t = 15 mm Width of the bar: w = 35 mm…

Q: Which of the following statements is incorrect regarding the mechanical characteristics of polymers?…

A: Polymers: The polymers are made of long and repeating chains of the molecules. They have different…

Q: A rod of length 24.7 cm has Young's Modulus of 1.60 ✕ 1010 N/m2. Assume that a force is applied to…

Q: A mass of 30kg is hung from a steel wire of radius 7cm and length of 40m. What should be the minimum…

A: Given, Mass = m = 30 kg Radius of wire = r = 7 cm = 0.07 m Length fo the wire = L = 40 m Elastic…

Q: A cylindrical structural element is made of steel. The element must withstand an axial load of 160…

A: Given: The value of the axial loading is, P=160 kN. Thye value of yield stress is, σy=340 MPa. The…

Concept explainers

Axial Load

When a bar of the uniform cross-section is acted by a load, such that the load acts along the longitudinal axis of the bar, such kinds of loadings are known as axial loadings. In general terms, a load is an external force acting on a component. An axial load acts perpendicular to the geometric cross-section of the component. Based on the direction of the application of the load, an axial load can be tensile or compressive. The analysis of bodies under the action of axial loads is generally studied under the branch of mechanics, known as statics.

Question

A continuous and aligned fiber-reinforced composite having a cross-sectional area of 1200 mm² is subjected to an external tensile
load. If the stresses sustained by the fiber and matrix phases are 152 and 2.27 MPa, respectively, the force sustained by the fiber phase
is 72300 N, and the total longitudinal strain is 0.00143, determine the following:
(a) The force sustained by the matrix phase (in N).
i
(b) The modulus of elasticity of the composite material in the longitudinal direction (in GPa).
i
N
i
(c) The modulus of elasticity for the fiber phase (in GPa).
GPa
i
GPa
(d) The modulus of elasticity for the matrix phase (in GPa).
GPa

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1 of 4.

Step 2 of 4.

Step 3 of 4.

Step 4 of 4.

Trending now

This is a popular solution!

Step by step

Solved in 4 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

A Cotton fiber, initially 2.2 cm long, is being stretched to its maximum known strain. What would be its final length, in cm, before rupture?
A stress of 1 kPa in a polymer deceased to 0.98 kPa after six weeks. This polymer is to hold a bundle of steel rods for up to one year. If the stress is less than 1.5 kPa, the band will not hold the rods tightly. Determine the initial stress needed to hold the rods.
At an axial load of 25 kN, a 50-mm-wide by 20-mm-thick polyimide polymer bar elongates 2.8 mm while the bar width contracts 0.29 mm. The bar is 190 mm long. At the 25-kN load, the stress in the polymer bar is less than its proportional limit. Determine (a) the modulus of elasticity. (b) Poisson's ratio. (c) the change in the bar thickness. Answers: (a) E= (b) v= (c) Athickness= i i GPa mm
How does the slenderness ratio affect the buckling behavior of columns in mechanical engineering?
Which of the statements below are accurate regarding the stress-strain behavior of polymers: (This question has more than one correct answer) а. Strain softening happens in elastomers where the deformation gradually leads to a decrease in stress under constant strain rate b. As temperature is reduced, the necking behavior of plastic tensile bars completely disappears С. The slope of the stress-strain curve for totally elastic and brittle polymers is always positive d. The stress-strain curve for vulcanized elastomers has a greater slope than unvulcanized polymers throughout
A student conducted an experiment to determine the behavior of poly (ethylene) and poly (tetrafluo-roethylene) to stress. The tables below depict the results of his experiments. Part 1.1Plot the stress-strain curves for both types of material. Calculate their respective Young’s moduli (E). Howdo they compare? Part 1.2From their respective plots, determine their approximate strain energy before plastic deformation begins.How do they compare? Part 1.3What do these calculations of young’s modulus and strain energy tell us about the properties of bothmaterials? Compare the properties of both materials using these calculations.
A panel of poly(methyl methacrylate) is bolted in the long direction only at 50°C between two other components with zero coefficients of expansion. What is the stress on the polymer at 0°C? Will the polymer break?
Q2: A fiberglass composite consists of a matrix of vinyl ester and reinforcing fibers of E-glass. The volume fraction of E-glass is 30%. The density of the vinyl estiser 0.882 g/cm³, and its modulus of elasticity is 3.6 GPa. The density of E-glass is 2.6 g/cm³, and its modulus of elasticity is 76 GPa. A section of composite 1 cm by 25 cm by 2 m is fabricated with the E-glass fibers running longitudinally in the 2000 mm direction. Determine: (a) The masses of vinyl ester and E-glass fibers. (b) The density of the composite. (c) The composite modulus of elasticity in the longitudinal and the perpendicular directions of the glass fibers. (d) If the tensile strength of the glass fibers, is 1 GPA and the tensile strength of the epoxy matrix is 60 MPa, find the tensile strength of the composite in the longitudinal direction.
A sample of silicone breast implant, polydimethylsiloxane (PDMS), is placed under unconfined compression. The magnitudes of the resulting longitudinal and transverse strains have been measured to be 2.7 and 1.341, respectively. The young's modulus of the implant is 500 kPa. Calculate the shear and bulk moduli.
A composite material consists of 60% glass fibre by volume (V₁ = 0.6). Half of the fibre is in unidirectional (0°) roving form and the other half is continuous fibre (0°, 90°) mat. The matrix is polyester. The properties of the constituent materials are shown in Table 4. Table 4 Density (Mg.m³) Tensile modulus (GPa) Tensile strength (MPa) Fibre 2.6 69 1200 i. Calculate the density of the composite material Matrix 1.1 2 35 ii. Calculate the tensile strength, oc, and the tensile modulus, Ec, of the composite in the 0° and 90° directions using the simple "rule of mixtures" approach.
C A cantilever beam is subjected to a downward force of 5 kN at its free end, as shown in Fig. 1. The beam is supported by a circular bracket (BD) attached to a wall. The bracket is made of ductile steel whose elastic limit is 300 MPa, both in tension and compression. Determine the diameter of supporting post using Von-Mises theory. (Hint: Neglected the weight of the beam, the ends B and D are welded) Fig.3 3 m B 2 m 2 m 2 m 5 kN
A new high stiffness plastic material has a length of 19.7 inches and a thickness of 3 mm and is being considered for use as a bone fixation plate. When subjected to a tensile load of 10000 N, the material stretches to a length of 19.88 inches. Please find the width of this material, which has a modulus of 4 GPa.